Pretreated Mg-Li alloy sheets were pre-plated in a NiCO3？2Ni（OH）2？4H2O solution to form a thin Ni-P alloy film and then plating in a NiSO4？6H2O solution was carried out to obtain a protective coating.The surface ...Pretreated Mg-Li alloy sheets were pre-plated in a NiCO3？2Ni（OH）2？4H2O solution to form a thin Ni-P alloy film and then plating in a NiSO4？6H2O solution was carried out to obtain a protective coating.The surface morphology,structure and corrosion resistance of the coating were studied.The results showed that a flat,bright and compact plating layer,which was integrated into the matrix metal,was obtained.The P content of the Ni-P coating reached 13.56%（mass fraction）.The hardness value of the Ni-P coating was about HV 549.The polarization curve showed that the corrosion potential of the Ni-P coating reached ？0.249 V（vs SCE）.A long passivation region was found on the polarization curve,and this phenomenon indicated that the coating has an excellent anti-corrosion property.展开更多
基金Projects(50974114,51174060) supported by National Natural Science Foundation of ChinaProject(2008AA03Z512) supported by High-tech Research and Development Program of ChinaProject(20070145049) supported by PhD Programs Foundation of Ministry of Education of China
文摘Pretreated Mg-Li alloy sheets were pre-plated in a NiCO3？2Ni（OH）2？4H2O solution to form a thin Ni-P alloy film and then plating in a NiSO4？6H2O solution was carried out to obtain a protective coating.The surface morphology,structure and corrosion resistance of the coating were studied.The results showed that a flat,bright and compact plating layer,which was integrated into the matrix metal,was obtained.The P content of the Ni-P coating reached 13.56%（mass fraction）.The hardness value of the Ni-P coating was about HV 549.The polarization curve showed that the corrosion potential of the Ni-P coating reached ？0.249 V（vs SCE）.A long passivation region was found on the polarization curve,and this phenomenon indicated that the coating has an excellent anti-corrosion property.