Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid...Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid nitrogen-assisted cooling（LNSC） was carried out to get the higher cooling rate and improve the surface properties. The experimental results were compared with those of Ar gas protection at room temperature. The samples after LSM with LNSC resulted in a thinner melted layer, a highly homogeneous, refined melted microstructure and formed a lot of worm-like nanocrystals and local amorphous structures. Microhardness of the melted layer with LNAC was improved to HV 90-148 as compared to HV 65-105 of the samples with Ar gas protection. The corrosion resistance of the melted layer in a 3.5% Na Cl solution（mass fraction） was improved because of the grain refinement and redistribution of β-Mg17Al12 phases following rapid quenching associated with the process.展开更多
The ZK60 magnesium alloy plates were welded by laser beam welding (LBW) and the microstructures in the partially melted zone (PMZ) of welded joints were investigated. For the as-cast alloy, the eutectoid mixtures alon...The ZK60 magnesium alloy plates were welded by laser beam welding (LBW) and the microstructures in the partially melted zone (PMZ) of welded joints were investigated. For the as-cast alloy, the eutectoid mixtures along grain boundaries (GBs) in the PMZ are liquefied during welding, and their re-solidified materials present hypoeutectic characters, which lead to more severe segregation of the Zn element along GBs, and thus enhance the cracking tendency of the PMZ. The main reasons for liquation cracking of PMZ are described as that the absence of liquid at the terminal stage of solidification leads to the occurrence of shrinkage cavities in PMZ, from which liquation cracking initiates, and propagates along the weakened GBs under the tensile stress originating from solidification shrinkage and thermal contraction. Lower heat input can reduce the cracking tendency, and the plastic processing such as rolling also contributes to the mitigation of PMZ liquation cracking by reducing the size of eutectoid phases and changing their distribution in the base metal.展开更多
基金Project(51305292)supported by the National Natural Science Foundation of ChinaProject(2014-024)supported by Shanxi Scholarship Council of China
文摘Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid nitrogen-assisted cooling（LNSC） was carried out to get the higher cooling rate and improve the surface properties. The experimental results were compared with those of Ar gas protection at room temperature. The samples after LSM with LNSC resulted in a thinner melted layer, a highly homogeneous, refined melted microstructure and formed a lot of worm-like nanocrystals and local amorphous structures. Microhardness of the melted layer with LNAC was improved to HV 90-148 as compared to HV 65-105 of the samples with Ar gas protection. The corrosion resistance of the melted layer in a 3.5% Na Cl solution（mass fraction） was improved because of the grain refinement and redistribution of β-Mg17Al12 phases following rapid quenching associated with the process.
基金Project (2011ZX06001-003) supported by the National Science and Technology Major Project, ChinaProject (51274092) supported by the National Natural Science Foundation of China
文摘The ZK60 magnesium alloy plates were welded by laser beam welding (LBW) and the microstructures in the partially melted zone (PMZ) of welded joints were investigated. For the as-cast alloy, the eutectoid mixtures along grain boundaries (GBs) in the PMZ are liquefied during welding, and their re-solidified materials present hypoeutectic characters, which lead to more severe segregation of the Zn element along GBs, and thus enhance the cracking tendency of the PMZ. The main reasons for liquation cracking of PMZ are described as that the absence of liquid at the terminal stage of solidification leads to the occurrence of shrinkage cavities in PMZ, from which liquation cracking initiates, and propagates along the weakened GBs under the tensile stress originating from solidification shrinkage and thermal contraction. Lower heat input can reduce the cracking tendency, and the plastic processing such as rolling also contributes to the mitigation of PMZ liquation cracking by reducing the size of eutectoid phases and changing their distribution in the base metal.