Mg-25 wt% Mg2Ni composite was prepared by sintered method, hydrided at 613 K and then ball-milled with 1.5 wt% PdC12 additive for 51 h. The effects of PdCl2 on the hydriding and dehydriding behavior of Mg-25 wt% Mg2Ni...Mg-25 wt% Mg2Ni composite was prepared by sintered method, hydrided at 613 K and then ball-milled with 1.5 wt% PdC12 additive for 51 h. The effects of PdCl2 on the hydriding and dehydriding behavior of Mg-25 wt% Mg2Ni composite were investigated. The absorption and desorption rate of the composite with PdCl2 is fast and the hydrogen storage capacity is more than that of the composite without PdCl2. The maximum hydrogen storage capacity reached 3.48 wt% at 373 K, and 5.05 wt% H at 453 K, respectively. The improvement of sorption and desorption kinetics is attributed to the catalytic effect of PdCl2, and the grain refining and lattice strain introduced by ball milling.展开更多
Mg2Ni0.8Cr0.2-x wt.% CoO/Al2O3 (x=0.5, 1, 2 and 3) composites were prepared by mechanically milling sintered Mg2Ni0.8Cr0.2 alloy and CoO/Al2O3 compound for 45 h. The addition of CoO/Al2O3 compound resulted in the good...Mg2Ni0.8Cr0.2-x wt.% CoO/Al2O3 (x=0.5, 1, 2 and 3) composites were prepared by mechanically milling sintered Mg2Ni0.8Cr0.2 alloy and CoO/Al2O3 compound for 45 h. The addition of CoO/Al2O3 compound resulted in the good kinetics properties of hydriding/dehydriding reaction of the composites. The composite with 1.0 wt.% CoO/Al2O3 catalyst could reach the maximum hydrogen absorption capacity (2.9 wt.%) within 5 min at 393 K under H2 pressure of 4 MPa, and can desorb rapidly at 493 K. The decomposition and synthesis of hydrogen molecule on Mg2Ni0.8Cr0.2 alloy surface was promoted by addition of CoO/Al2O3 catalyst. In addition, the formation of metallic Ni particles, strain and defects during the ball milling process also resulted in the improved hydrogenation performance of Mg2Ni-based alloys.展开更多
The Ga-Hg binary system was thermodynamically assessed by the CALPHAD method, but only configuration contributions were considered to the entropy of the liquid. The Mg-Hg binary system has not been assessed yet. In th...The Ga-Hg binary system was thermodynamically assessed by the CALPHAD method, but only configuration contributions were considered to the entropy of the liquid. The Mg-Hg binary system has not been assessed yet. In the assessments of the Ga-Hg and Mg-Hg binary systems, solutions including liquid and hcp (Mg) were treated as substitution solutions, of which the excess Gibbs energies were formulated with the Relich-Kister polynomial. The intermetallic phases in the Mg-Hg binary system, Mg3Hg, Mg5Hg2, Mg2Hg, Mg5Hg3, MgHg, and MgHg2, were described as stoichiometric compounds. Based on the reported experimental data and thermodynamic properties of the phase diagram, sets of self-consistent parameters describing all phases in the Ga-Hg and the Mg-Hg binary systems were obtained.展开更多
基金Project supported by the Special Funds for Postdoctoral Research Project of China (No. 20060401035)the Hi-Tech Research and Development Program (863) of China (No. 2006AA11A159)
文摘Mg-25 wt% Mg2Ni composite was prepared by sintered method, hydrided at 613 K and then ball-milled with 1.5 wt% PdC12 additive for 51 h. The effects of PdCl2 on the hydriding and dehydriding behavior of Mg-25 wt% Mg2Ni composite were investigated. The absorption and desorption rate of the composite with PdCl2 is fast and the hydrogen storage capacity is more than that of the composite without PdCl2. The maximum hydrogen storage capacity reached 3.48 wt% at 373 K, and 5.05 wt% H at 453 K, respectively. The improvement of sorption and desorption kinetics is attributed to the catalytic effect of PdCl2, and the grain refining and lattice strain introduced by ball milling.
基金Project (No. TG20000264-06) supported by the Special Funds forMajor States Basic Research Project of MOST, China
文摘Mg2Ni0.8Cr0.2-x wt.% CoO/Al2O3 (x=0.5, 1, 2 and 3) composites were prepared by mechanically milling sintered Mg2Ni0.8Cr0.2 alloy and CoO/Al2O3 compound for 45 h. The addition of CoO/Al2O3 compound resulted in the good kinetics properties of hydriding/dehydriding reaction of the composites. The composite with 1.0 wt.% CoO/Al2O3 catalyst could reach the maximum hydrogen absorption capacity (2.9 wt.%) within 5 min at 393 K under H2 pressure of 4 MPa, and can desorb rapidly at 493 K. The decomposition and synthesis of hydrogen molecule on Mg2Ni0.8Cr0.2 alloy surface was promoted by addition of CoO/Al2O3 catalyst. In addition, the formation of metallic Ni particles, strain and defects during the ball milling process also resulted in the improved hydrogenation performance of Mg2Ni-based alloys.
文摘The Ga-Hg binary system was thermodynamically assessed by the CALPHAD method, but only configuration contributions were considered to the entropy of the liquid. The Mg-Hg binary system has not been assessed yet. In the assessments of the Ga-Hg and Mg-Hg binary systems, solutions including liquid and hcp (Mg) were treated as substitution solutions, of which the excess Gibbs energies were formulated with the Relich-Kister polynomial. The intermetallic phases in the Mg-Hg binary system, Mg3Hg, Mg5Hg2, Mg2Hg, Mg5Hg3, MgHg, and MgHg2, were described as stoichiometric compounds. Based on the reported experimental data and thermodynamic properties of the phase diagram, sets of self-consistent parameters describing all phases in the Ga-Hg and the Mg-Hg binary systems were obtained.