Magnesium alloys have good biocompatibility, but their mechanical properties and corrosion resistance may not be satisfied for using as degradable materials within bone due to its high corrosion rate in the physiologi...Magnesium alloys have good biocompatibility, but their mechanical properties and corrosion resistance may not be satisfied for using as degradable materials within bone due to its high corrosion rate in the physiological environment. Nano β-TCP particles were added into Mg-Zn-Zr alloy to improve its microstructure and the properties. As-extruded Mg-3Zn-0.8Zr alloy and Mg-3Zn-0.8Zr/xβ-TCP （x=0.5%, 1.0% and 1.5%） composites were respectively fabricated. The grains of Mg-Zn-Zr/β-TCP composites were significantly refined. The results of the tensile tests indicate that the ultimate tensile strength and the elongation of composites were improved with the addition of β-TCP. The electrochemical test result in simulation body fluid shows that the corrosion resistance of the composites was strongly enhanced comparing with that of the alloy. The corrosion potential of Mg-3Zn0.8-Zr/1.0β-TCP composite is 1.547 V and its corrosion current density is 1.20×10 6 A/cm 2 .展开更多
基金Project(51071108)supported by the National Natural Science Foundation of ChinaProject(09JCZDJC18500)supported by the Key Project of Natural Science Foundation of Tianjin,China
文摘Magnesium alloys have good biocompatibility, but their mechanical properties and corrosion resistance may not be satisfied for using as degradable materials within bone due to its high corrosion rate in the physiological environment. Nano β-TCP particles were added into Mg-Zn-Zr alloy to improve its microstructure and the properties. As-extruded Mg-3Zn-0.8Zr alloy and Mg-3Zn-0.8Zr/xβ-TCP （x=0.5%, 1.0% and 1.5%） composites were respectively fabricated. The grains of Mg-Zn-Zr/β-TCP composites were significantly refined. The results of the tensile tests indicate that the ultimate tensile strength and the elongation of composites were improved with the addition of β-TCP. The electrochemical test result in simulation body fluid shows that the corrosion resistance of the composites was strongly enhanced comparing with that of the alloy. The corrosion potential of Mg-3Zn0.8-Zr/1.0β-TCP composite is 1.547 V and its corrosion current density is 1.20×10 6 A/cm 2 .