The recovery stress characteristics of a TiNi shape memory alloy wire under different constraint conditions were studied. The results show that the recovery stress rate (dσ/dT) in the second heating cycle increases s...The recovery stress characteristics of a TiNi shape memory alloy wire under different constraint conditions were studied. The results show that the recovery stress rate (dσ/dT) in the second heating cycle increases significantly with the increasing constraining-spring coefficient in the first heating cycle. As a result, a distinct discontinuity appears on the recovery stress curves of the TiNi alloy wires in the second heating process. Also, the results of differential scanning calorimeter(DSC) measurements show that after the thermomechanical process, the heating curve of the TiNi alloy wire consists of two independent endothermic peaks.展开更多
The microstructures of the brazed joints for commercially pure Ti and stainless steel were investigated by the applications of various filler alloys including Ag-, Ti-, Zr- and Ni-based alloys. Generally, the dissimil...The microstructures of the brazed joints for commercially pure Ti and stainless steel were investigated by the applications of various filler alloys including Ag-, Ti-, Zr- and Ni-based alloys. Generally, the dissimilar joints between Ti and stainless steel were dominated by the Ti-based intermetallic compounds （IMCs）, e.g. （Ti, Zr）2（Fe, Ni）, TiFe, TiCu, and Ti2（Fe, Ni）, due to a significant dissolution of Ti from the base metal. The （Fe-Cr） cr phase was also observed near the stainless steel due to a segregation of Cr into the interface region. This research demonstrates empirically that the brittleness of the Ti and stainless steel joint can not be avoided only by applying single braze alloy or single insert metal, and thus an introduction of additional suitable interlayer between the filler alloy and the base metal is necessary to prevent the brittleness of the joint.展开更多
Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni ...Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni powders were blown into the melting pool by a six-hole coaxial nozzle powder injection system. Exothermic reactions between Ti and Ni took place in the melting pool, and a cladding layer of titanium nickel intermetallic compounds was produced. Laser nitriding in a nitrogen-rich atmosphere followed the production of the cladding layer, and formed a golden yellow TiN layer over it. An optical and a scanning electron microscope were used to investigate the microstructures and measure the thicknesses of the cladding layer and the TiN layer. Phase identification was carried out by XRD. For the nitriding sample, the microhardness profile of the clad layer was tested. The optimal process parameters of the in situ synthesis of titanium nickel intermetallic compounds were obtained.展开更多
基金Project(50071037) supported by the National Natural Science Foundation of China Project supported by the ScientificResearch Foundation for the Returned Overseas Chinese Scholars Education Ministry of China
文摘The recovery stress characteristics of a TiNi shape memory alloy wire under different constraint conditions were studied. The results show that the recovery stress rate (dσ/dT) in the second heating cycle increases significantly with the increasing constraining-spring coefficient in the first heating cycle. As a result, a distinct discontinuity appears on the recovery stress curves of the TiNi alloy wires in the second heating process. Also, the results of differential scanning calorimeter(DSC) measurements show that after the thermomechanical process, the heating curve of the TiNi alloy wire consists of two independent endothermic peaks.
基金supported by the Korea Atomic Energy Research Institute (KAERI) R&D Program
文摘The microstructures of the brazed joints for commercially pure Ti and stainless steel were investigated by the applications of various filler alloys including Ag-, Ti-, Zr- and Ni-based alloys. Generally, the dissimilar joints between Ti and stainless steel were dominated by the Ti-based intermetallic compounds （IMCs）, e.g. （Ti, Zr）2（Fe, Ni）, TiFe, TiCu, and Ti2（Fe, Ni）, due to a significant dissolution of Ti from the base metal. The （Fe-Cr） cr phase was also observed near the stainless steel due to a segregation of Cr into the interface region. This research demonstrates empirically that the brittleness of the Ti and stainless steel joint can not be avoided only by applying single braze alloy or single insert metal, and thus an introduction of additional suitable interlayer between the filler alloy and the base metal is necessary to prevent the brittleness of the joint.
文摘Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni powders were blown into the melting pool by a six-hole coaxial nozzle powder injection system. Exothermic reactions between Ti and Ni took place in the melting pool, and a cladding layer of titanium nickel intermetallic compounds was produced. Laser nitriding in a nitrogen-rich atmosphere followed the production of the cladding layer, and formed a golden yellow TiN layer over it. An optical and a scanning electron microscope were used to investigate the microstructures and measure the thicknesses of the cladding layer and the TiN layer. Phase identification was carried out by XRD. For the nitriding sample, the microhardness profile of the clad layer was tested. The optimal process parameters of the in situ synthesis of titanium nickel intermetallic compounds were obtained.