Square piles of reinforced concrete(RC)in marine environments are susceptible to chloride-inducedcorrosion.A novel reverse-seepage technique(RST)is applied to square piles to block the intrusion of chlorides.Thisresea...Square piles of reinforced concrete(RC)in marine environments are susceptible to chloride-inducedcorrosion.A novel reverse-seepage technique(RST)is applied to square piles to block the intrusion of chlorides.Thisresearch introduces a computational model designed to predict the lifespan of corrosion initiation in reinforced concretesquare piles when applied reverse-seepage pressure.The model considers the impacts of chloride binding and the tripletime-dependence property among the permeability,the corrected surface chloride concentration,and the diffusioncoefficient.The proposed numerical model is solved using the alternating direction implicit(ADI)approach,and itsaccuracy and reliability are evaluated by contrasting the computational outcomes with the analytical solution andexperimental results.Furthermore,the primary factors contributing to the corrosion of reinforced concrete square pilesare analyzed.The results indicate that applying RST can decrease the chloride penetration depth and prolong the lifespanof corrosion initiation in square piles.The water-cement ratio and reverse seepage pressure are the most influentialfactors.A water pressure of 0.4 MPa can double the life of concrete,and the durable life of concrete with a water-cementratio of 0.3 can reach 100 years.展开更多
The electrochemical behavior of X70 pipeline steel in (0.5mol·L-1 Na2CO3+1 mol·L-1 NaHCO3) solution was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). X-ray photoel...The electrochemical behavior of X70 pipeline steel in (0.5mol·L-1 Na2CO3+1 mol·L-1 NaHCO3) solution was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) were used to analyze the composition and microstructure of the surface film. The results showed that there were two anodic peaks at -600 mV and -350 mV. The surface film formed at -600 mV mainly consisted of ferrous carbonates and ferrous hydroxycarbonates. It had a small reaction resistance. It was metastable and possessed poor protective property. Numerous pits and microcracks existed on the film, which could be the active paths for the initiation of stress corrosion cracking. The surface film formed at -350 mV, mainly consisted of ferric oxides. It has high reaction resistance and offered good protection for the substrate.展开更多
The effects of pulse parameters on the cobalt content, surface morphologies and grain size of Zn-Co alloy deposits were studied using a pulse plating technique with a square-wave current containing reverse pulse. Aver...The effects of pulse parameters on the cobalt content, surface morphologies and grain size of Zn-Co alloy deposits were studied using a pulse plating technique with a square-wave current containing reverse pulse. Average current density and reverse anodic current density amongst the variables investigated have very strong effects on the cobalt content in the Zn-Co alloy deposits. Grain size, surface appearance and internal stress in the deposit were improved significantly by introducing the reverse current. Varieties of Zn-Co alloy compositionally modulated multilayer (CMM) coatings with large differences in cobalt contents for different sublayers were electrodeposited by designing corresponding waveforms using a computer-aided pulse plater and characterized in terms of surface morphologies. Cross-sectional morphologies of the Zn-Co alloy CMM coatings, examined using field emission gun scanning electron microscopy (FEGSEM), confirmed the layered structure.展开更多
基金Projects(52178371,52108355,52178321)supported by the National Natural Science Foundation of ChinaProject(202305)supported by the Research Project of Engineering Research Centre of Rock-Soil Drilling&Excavation and Protection,Ministry of Education,China。
文摘Square piles of reinforced concrete(RC)in marine environments are susceptible to chloride-inducedcorrosion.A novel reverse-seepage technique(RST)is applied to square piles to block the intrusion of chlorides.Thisresearch introduces a computational model designed to predict the lifespan of corrosion initiation in reinforced concretesquare piles when applied reverse-seepage pressure.The model considers the impacts of chloride binding and the tripletime-dependence property among the permeability,the corrected surface chloride concentration,and the diffusioncoefficient.The proposed numerical model is solved using the alternating direction implicit(ADI)approach,and itsaccuracy and reliability are evaluated by contrasting the computational outcomes with the analytical solution andexperimental results.Furthermore,the primary factors contributing to the corrosion of reinforced concrete square pilesare analyzed.The results indicate that applying RST can decrease the chloride penetration depth and prolong the lifespanof corrosion initiation in square piles.The water-cement ratio and reverse seepage pressure are the most influentialfactors.A water pressure of 0.4 MPa can double the life of concrete,and the durable life of concrete with a water-cementratio of 0.3 can reach 100 years.
基金Supported by State Key Basic Research Plan (G19990650).
文摘The electrochemical behavior of X70 pipeline steel in (0.5mol·L-1 Na2CO3+1 mol·L-1 NaHCO3) solution was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) were used to analyze the composition and microstructure of the surface film. The results showed that there were two anodic peaks at -600 mV and -350 mV. The surface film formed at -600 mV mainly consisted of ferrous carbonates and ferrous hydroxycarbonates. It had a small reaction resistance. It was metastable and possessed poor protective property. Numerous pits and microcracks existed on the film, which could be the active paths for the initiation of stress corrosion cracking. The surface film formed at -350 mV, mainly consisted of ferric oxides. It has high reaction resistance and offered good protection for the substrate.
文摘The effects of pulse parameters on the cobalt content, surface morphologies and grain size of Zn-Co alloy deposits were studied using a pulse plating technique with a square-wave current containing reverse pulse. Average current density and reverse anodic current density amongst the variables investigated have very strong effects on the cobalt content in the Zn-Co alloy deposits. Grain size, surface appearance and internal stress in the deposit were improved significantly by introducing the reverse current. Varieties of Zn-Co alloy compositionally modulated multilayer (CMM) coatings with large differences in cobalt contents for different sublayers were electrodeposited by designing corresponding waveforms using a computer-aided pulse plater and characterized in terms of surface morphologies. Cross-sectional morphologies of the Zn-Co alloy CMM coatings, examined using field emission gun scanning electron microscopy (FEGSEM), confirmed the layered structure.