A self-ordered porous film was fabricated on aluminum alloy in a ternary boric-sulfuric-oxalic acid electrolyte system. By means of voltage–time response, the oxidation process as well as the growth efficiency was st...A self-ordered porous film was fabricated on aluminum alloy in a ternary boric-sulfuric-oxalic acid electrolyte system. By means of voltage–time response, the oxidation process as well as the growth efficiency was studied. Field emission scanning electron microscopy（FE-SEM） was adopted to reveal the morphological and microstructural features of as-fabricated oxide layers. The corrosion protection properties of the films were investigated by electrochemical impedance spectroscopy and potentiodynamic polarization measurements. The results showed that increasing the concentration of the double ionic layer located at the oxide interface could accelerate the film growth rate. The anodic oxidative layer with thickness of 8-9 μm and pore diameter of 10-14 nm maintains the pattern and topography of workpieces, compared with the overall closed film with hierarchical structure. Both samples exhibited much lower corrosion current density after boil water sealing. Meanwhile, a superior stability could be achieved through raising the ambient temperature.展开更多
The effects of Pb^2+concentration,current density,deposition time and temperature on Pb deposit structure were investigated.In lower Pb^2+concentration(~0.15 mol/L),carambola-like 3D-Pb structure was constructed,while...The effects of Pb^2+concentration,current density,deposition time and temperature on Pb deposit structure were investigated.In lower Pb^2+concentration(~0.15 mol/L),carambola-like 3D-Pb structure was constructed,while in higher Pb2+concentration(≥0.30 mol/L),Pb deposits exhibited pyramid-like structure.Furthermore,the oxide layer and anodic potential of carambola-shaped 3D-Pb(Cara-Pb)and pyramid-shaped 3D-Pb(Pyra-Pb)anodes were investigated and compared with those of fresh Pb anode.After 72 h galvanostatic electrolysis(50 mA/cm2)in 160 g/L H2SO4 solution,the oxide layer on Pyra-Pb was much thicker than that on Cara-Pb and Pb anodes,which remarkably relieved intercrystalline corrosion of the metallic substrate.Additionally,the oxide layer on Pyra-Pb anode presented a larger surface area and higher PbO2 content.Hence,Pyra-Pb anode showed a 40 m V lower anodic potential compared to Cara-Pb and Pb anodes.In sum,Pyra-Pb anode had a potential to decrease energy consumption and prolong the life span of traditional Pb anode.展开更多
Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstat...Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstate on the coating thickness, mass gain,surface morphology and corrosion resistance were studied by eddy current instrument,electronic scales,scanning electron microscope and immersion tester.With the addition of sodium tungstate,the electrolytic conductivity increases and the final voltage decreases.The sodium tungstate has a minor effect on the coating thickness,but lightens the coating color.With increasing sodium tungstate concentration,the size of micropores on the coatings is enlarged and the corrosion resistance of the anodized samples decreases.展开更多
Al specimens were covered with TiO2 film by sol-gel dip-coating and then anodized in ammonium adipate solution.The structure,composition and capacitance properties of the anodic oxide film were investigated by transmi...Al specimens were covered with TiO2 film by sol-gel dip-coating and then anodized in ammonium adipate solution.The structure,composition and capacitance properties of the anodic oxide film were investigated by transmission electron microscopy (TEM),Auger electron spectroscopy (AES),X-ray diffractometry (XRD) and electrochemical impedance spectroscopy (EIS).It was found that an anodic oxide film with a dual-layer structure formed between TiO2 coating and Al substrate.The film consisted of an inner Al2O3 layer and an outer Ti-Al composite oxide layer.The thickness of layers varied with the number of times of sol-gel dip-coating.The capacitance of anodic oxide films formed on coated specimens was at most 80% higher than that without TiO2.In film formation mechanism,it was claimed that the formation of composite oxide film was mainly affected by the structure of micro-pores network in TiO2 coating which had an influence on Al3+ and O2? ions transport during the anodizing.展开更多
文摘A self-ordered porous film was fabricated on aluminum alloy in a ternary boric-sulfuric-oxalic acid electrolyte system. By means of voltage–time response, the oxidation process as well as the growth efficiency was studied. Field emission scanning electron microscopy（FE-SEM） was adopted to reveal the morphological and microstructural features of as-fabricated oxide layers. The corrosion protection properties of the films were investigated by electrochemical impedance spectroscopy and potentiodynamic polarization measurements. The results showed that increasing the concentration of the double ionic layer located at the oxide interface could accelerate the film growth rate. The anodic oxidative layer with thickness of 8-9 μm and pore diameter of 10-14 nm maintains the pattern and topography of workpieces, compared with the overall closed film with hierarchical structure. Both samples exhibited much lower corrosion current density after boil water sealing. Meanwhile, a superior stability could be achieved through raising the ambient temperature.
基金Project(51704130)supported by the National Natural Science Foundation of ChinaProject(GK-201905)supported by the Research Fund of State Key Laboratory of Rare Metals Separation and Comprehensive Utilization,ChinaProject(jxxjbs16026)supported by the Doctoral Scientific Research Foundation of Jiangxi University of Science and Technology,China
文摘The effects of Pb^2+concentration,current density,deposition time and temperature on Pb deposit structure were investigated.In lower Pb^2+concentration(~0.15 mol/L),carambola-like 3D-Pb structure was constructed,while in higher Pb2+concentration(≥0.30 mol/L),Pb deposits exhibited pyramid-like structure.Furthermore,the oxide layer and anodic potential of carambola-shaped 3D-Pb(Cara-Pb)and pyramid-shaped 3D-Pb(Pyra-Pb)anodes were investigated and compared with those of fresh Pb anode.After 72 h galvanostatic electrolysis(50 mA/cm2)in 160 g/L H2SO4 solution,the oxide layer on Pyra-Pb was much thicker than that on Cara-Pb and Pb anodes,which remarkably relieved intercrystalline corrosion of the metallic substrate.Additionally,the oxide layer on Pyra-Pb anode presented a larger surface area and higher PbO2 content.Hence,Pyra-Pb anode showed a 40 m V lower anodic potential compared to Cara-Pb and Pb anodes.In sum,Pyra-Pb anode had a potential to decrease energy consumption and prolong the life span of traditional Pb anode.
基金Projects(GJJ08363,GJJ09573)supported by the Scientific Research Fund of Jiangxi Provincial Education Department,China
文摘Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstate on the coating thickness, mass gain,surface morphology and corrosion resistance were studied by eddy current instrument,electronic scales,scanning electron microscope and immersion tester.With the addition of sodium tungstate,the electrolytic conductivity increases and the final voltage decreases.The sodium tungstate has a minor effect on the coating thickness,but lightens the coating color.With increasing sodium tungstate concentration,the size of micropores on the coatings is enlarged and the corrosion resistance of the anodized samples decreases.
文摘Al specimens were covered with TiO2 film by sol-gel dip-coating and then anodized in ammonium adipate solution.The structure,composition and capacitance properties of the anodic oxide film were investigated by transmission electron microscopy (TEM),Auger electron spectroscopy (AES),X-ray diffractometry (XRD) and electrochemical impedance spectroscopy (EIS).It was found that an anodic oxide film with a dual-layer structure formed between TiO2 coating and Al substrate.The film consisted of an inner Al2O3 layer and an outer Ti-Al composite oxide layer.The thickness of layers varied with the number of times of sol-gel dip-coating.The capacitance of anodic oxide films formed on coated specimens was at most 80% higher than that without TiO2.In film formation mechanism,it was claimed that the formation of composite oxide film was mainly affected by the structure of micro-pores network in TiO2 coating which had an influence on Al3+ and O2? ions transport during the anodizing.