TiB2/C cathode composites with various contents of TiB2 were prepared and their characterizations were observed and compared. The expansion of samples due to sodium and bath penetration was tested with a modified labo...TiB2/C cathode composites with various contents of TiB2 were prepared and their characterizations were observed and compared. The expansion of samples due to sodium and bath penetration was tested with a modified laboratory Rapoport apparatus and the appearances of the cut sections of specimens after electrolysis were studied. The results show that the mass of TiB2/C cathode composites with mass fraction of TiB2 less than 70% appreciably increases, but that of the composites with mass fraction of TiB2 more than 70% decreases slightly after being baked. The resistance to sodium and bath penetration of TiB2/C cathode composites increases with the increase of TiB2 content, especially in the composites with high TiB2 content. TiB2/C cathode composites have high resistance to the penetration of sodium and bath as well as good wettability by molten aluminum, and keep integrality and have little change of appearance after electrolysis, which indicates that TiB2/C cathode composites can be used as inert wettable cathode for aluminum electrolysis.展开更多
The current study focuses on the electrolyte penetration of the graphite cathode in a NaF−KF−LiF−AlF_(3) aluminum-electrolysis system with a cryolite ratio of 1.3.It involves a comprehensive investigation of the elect...The current study focuses on the electrolyte penetration of the graphite cathode in a NaF−KF−LiF−AlF_(3) aluminum-electrolysis system with a cryolite ratio of 1.3.It involves a comprehensive investigation of the electrolyte in the cathode before and after electrolysis by X-ray diffraction and analysis of the results by semi-quantitative calculation in MAUD.The results show that KF can promote electrolyte penetration,with higher KF contents resulting in greater penetration.During electrolyte penetration,K_(2)NaAlF_(6) and solid solutions containing KF play important roles in KF-containing systems.LiF effectively prevents the electrolyte penetration,while the Na_(3)Li_(3)Al_(2)F_(12) phase plays an essential role in systems with high LiF contents.展开更多
文摘TiB2/C cathode composites with various contents of TiB2 were prepared and their characterizations were observed and compared. The expansion of samples due to sodium and bath penetration was tested with a modified laboratory Rapoport apparatus and the appearances of the cut sections of specimens after electrolysis were studied. The results show that the mass of TiB2/C cathode composites with mass fraction of TiB2 less than 70% appreciably increases, but that of the composites with mass fraction of TiB2 more than 70% decreases slightly after being baked. The resistance to sodium and bath penetration of TiB2/C cathode composites increases with the increase of TiB2 content, especially in the composites with high TiB2 content. TiB2/C cathode composites have high resistance to the penetration of sodium and bath as well as good wettability by molten aluminum, and keep integrality and have little change of appearance after electrolysis, which indicates that TiB2/C cathode composites can be used as inert wettable cathode for aluminum electrolysis.
基金financial supports from the National Natural Science Foundation of China (Nos.51774080,22078056)the National Key R&D Program of China (No.2018YFC1901905)。
文摘The current study focuses on the electrolyte penetration of the graphite cathode in a NaF−KF−LiF−AlF_(3) aluminum-electrolysis system with a cryolite ratio of 1.3.It involves a comprehensive investigation of the electrolyte in the cathode before and after electrolysis by X-ray diffraction and analysis of the results by semi-quantitative calculation in MAUD.The results show that KF can promote electrolyte penetration,with higher KF contents resulting in greater penetration.During electrolyte penetration,K_(2)NaAlF_(6) and solid solutions containing KF play important roles in KF-containing systems.LiF effectively prevents the electrolyte penetration,while the Na_(3)Li_(3)Al_(2)F_(12) phase plays an essential role in systems with high LiF contents.