A new testing procedure to estimate the low-temperature stiffness of the reclaimed asphalt pavement （RAP） binder was developed. In the testing procedure, the SuperpaveTM Bending Beam Rheometer （BBR） with special m...A new testing procedure to estimate the low-temperature stiffness of the reclaimed asphalt pavement （RAP） binder was developed. In the testing procedure, the SuperpaveTM Bending Beam Rheometer （BBR） with special modifications and binder blending charts by Asphalt Institute were utilized. Modifications involved the development of a new kind of sample mold and different testing parameters were made to BBR testing procedure to capture the theological properties of bitumen mortars produced by mixing fresh binder with fine RAP materials or RAP aggregate. The stiffness relationship between binder and bitumen mortar was established based on the BBR test results. The blended binder stiffness in bitumen RAP mortar was estimated from the RAP mortar stiffness based on the binder-mortar relationship. And finally, the RAP binder stiffness was estimated from the blended binder and fresh binder stiffness based on the blending charts by Asphalt Institute. The results indicate that the new procedure can capture the rheological properties of bitumen mortar and can be used to estimate the low temperature stiffness of RAP binder without binder extraction and/or any chemical treatments.展开更多
The effect of diamond-like carbon(DLC)coating(fabricated by cathodic arc deposition)on mechanical properties,tribological behavior and corrosion performance of the Ni−Al−bronze(NAB)alloy was investigated.Nano-hardness...The effect of diamond-like carbon(DLC)coating(fabricated by cathodic arc deposition)on mechanical properties,tribological behavior and corrosion performance of the Ni−Al−bronze(NAB)alloy was investigated.Nano-hardness and pin-on-plate test showed that DLC coating had a greater hardness compared with NAB alloy.Besides,the decrease in friction coefficient from 0.2 for NAB substrate to 0.13 for the DLC-coated sample was observed.Potentiodynamic polarization and EIS results showed that the corrosion current density decreased from 2.5μA/cm2 for bare NAB alloy to 0.14μA/cm2 for DLC-coated sample in 3.5 wt.%NaCl solution.Moreover,the charge transfer resistance at the substrate−electrolyte interface increased from 3.3 kΩ·cm2 for NAB alloy to 120.8 kΩ·cm2 for DLC-coated alloy,which indicated an increase in corrosion resistance due to the DLC coating.展开更多
Asphalt mixture is a highly heterogeneous material, which is one of the reasons for high measurements uncertainty when subjected to tests. The results of such tests are often unreliable, which may lead to making bad p...Asphalt mixture is a highly heterogeneous material, which is one of the reasons for high measurements uncertainty when subjected to tests. The results of such tests are often unreliable, which may lead to making bad professional judgments. They can be avoided by carrying out reliable analyses of measurement uncertainty adequate for the research methods used and conducted before the actual research is done. This paper presents the calculation of measurements uncertainty using as an example--the determination of the stiffness modulus of the asphalt mixture, which, in turn, was accomplished using the indirect tension method. The paper also shows the employment of the basic methods of statistical analysis, such as testing two mean values and conformity tests. Essential concepts in measurements uncertainty have been compiled and the determination of the stiffness module parameters are discussed. It has been demonstrated that the biggest source of error in the stiffness modulus measuring process is the displacement measure. The aim of the research was to find the measurement uncertainty for stiffness modulus by an indirect tensile test and the presentation of examples of the used statistical methods.展开更多
基金Project(200831800044) supported by the Ministry of Communication of ChinaProject(50878054) supported by the National Natural Science Foundation of ChinaProject(06Y31) supported by the Department of Communication of Zhejiang Province,China
文摘A new testing procedure to estimate the low-temperature stiffness of the reclaimed asphalt pavement （RAP） binder was developed. In the testing procedure, the SuperpaveTM Bending Beam Rheometer （BBR） with special modifications and binder blending charts by Asphalt Institute were utilized. Modifications involved the development of a new kind of sample mold and different testing parameters were made to BBR testing procedure to capture the theological properties of bitumen mortars produced by mixing fresh binder with fine RAP materials or RAP aggregate. The stiffness relationship between binder and bitumen mortar was established based on the BBR test results. The blended binder stiffness in bitumen RAP mortar was estimated from the RAP mortar stiffness based on the binder-mortar relationship. And finally, the RAP binder stiffness was estimated from the blended binder and fresh binder stiffness based on the blending charts by Asphalt Institute. The results indicate that the new procedure can capture the rheological properties of bitumen mortar and can be used to estimate the low temperature stiffness of RAP binder without binder extraction and/or any chemical treatments.
文摘The effect of diamond-like carbon(DLC)coating(fabricated by cathodic arc deposition)on mechanical properties,tribological behavior and corrosion performance of the Ni−Al−bronze(NAB)alloy was investigated.Nano-hardness and pin-on-plate test showed that DLC coating had a greater hardness compared with NAB alloy.Besides,the decrease in friction coefficient from 0.2 for NAB substrate to 0.13 for the DLC-coated sample was observed.Potentiodynamic polarization and EIS results showed that the corrosion current density decreased from 2.5μA/cm2 for bare NAB alloy to 0.14μA/cm2 for DLC-coated sample in 3.5 wt.%NaCl solution.Moreover,the charge transfer resistance at the substrate−electrolyte interface increased from 3.3 kΩ·cm2 for NAB alloy to 120.8 kΩ·cm2 for DLC-coated alloy,which indicated an increase in corrosion resistance due to the DLC coating.
文摘Asphalt mixture is a highly heterogeneous material, which is one of the reasons for high measurements uncertainty when subjected to tests. The results of such tests are often unreliable, which may lead to making bad professional judgments. They can be avoided by carrying out reliable analyses of measurement uncertainty adequate for the research methods used and conducted before the actual research is done. This paper presents the calculation of measurements uncertainty using as an example--the determination of the stiffness modulus of the asphalt mixture, which, in turn, was accomplished using the indirect tension method. The paper also shows the employment of the basic methods of statistical analysis, such as testing two mean values and conformity tests. Essential concepts in measurements uncertainty have been compiled and the determination of the stiffness module parameters are discussed. It has been demonstrated that the biggest source of error in the stiffness modulus measuring process is the displacement measure. The aim of the research was to find the measurement uncertainty for stiffness modulus by an indirect tensile test and the presentation of examples of the used statistical methods.