The microstructures and dielectric properties of Sb2O3-doped Ti deficient barium strontium titanate ceramics prepared by solid state method were investigated with non-stoichiometric level and Sb2O3content by SEM,XRD a...The microstructures and dielectric properties of Sb2O3-doped Ti deficient barium strontium titanate ceramics prepared by solid state method were investigated with non-stoichiometric level and Sb2O3content by SEM,XRD and LCR measure system.It is found that with the increase ofδ,(Ba0.75Sr0.25)Ti1-δO3-2δceramics transform from single phase solid solutions with typical cubic perovskite structure to multiphase compounds while(Ba0.75Sr0.25)Ti0.998O2.996ceramics remain to be single-phase with the increasing Sb2O3content.The distortion of the ABO3perovskite lattice caused by VTi″″and VO..induces the drop of Curie temperature and the rise of relative dielectric constant in(Ba0.75Sr0.25)Ti1-δO3-2δceramics with increasingδvalue.The orientation of VO??elastic dipoles results in the domain-wall pinning and thus the reduction of the dielectric loss.With increasing Sb2O3content,the relative dielectric constant,dielectric constant maximum and Curie temperature of(Ba0.75Sr0.25)Ti0.998O2.996ceramics decrease dramatically while the dielectric loss increases.展开更多
基金Project(BK20140517)supported by the Natural Science Foundation of Jiangsu Province,ChinaProject(14KJB430011)supported by Jiangsu Provincial Natural Science Foundation for Colleges and Universities,China
文摘The microstructures and dielectric properties of Sb2O3-doped Ti deficient barium strontium titanate ceramics prepared by solid state method were investigated with non-stoichiometric level and Sb2O3content by SEM,XRD and LCR measure system.It is found that with the increase ofδ,(Ba0.75Sr0.25)Ti1-δO3-2δceramics transform from single phase solid solutions with typical cubic perovskite structure to multiphase compounds while(Ba0.75Sr0.25)Ti0.998O2.996ceramics remain to be single-phase with the increasing Sb2O3content.The distortion of the ABO3perovskite lattice caused by VTi″″and VO..induces the drop of Curie temperature and the rise of relative dielectric constant in(Ba0.75Sr0.25)Ti1-δO3-2δceramics with increasingδvalue.The orientation of VO??elastic dipoles results in the domain-wall pinning and thus the reduction of the dielectric loss.With increasing Sb2O3content,the relative dielectric constant,dielectric constant maximum and Curie temperature of(Ba0.75Sr0.25)Ti0.998O2.996ceramics decrease dramatically while the dielectric loss increases.