Pseudo-spin-valve (PSV) sandwiches using amorphous CoNbZr alloy as soft magnetic layer were fabricated by magnetron sputtering. The giant magnetoresistance (GMR) and its dependence on the thickness of magnetic layer w...Pseudo-spin-valve (PSV) sandwiches using amorphous CoNbZr alloy as soft magnetic layer were fabricated by magnetron sputtering. The giant magnetoresistance (GMR) and its dependence on the thickness of magnetic layer were investigated. Anti-parallel magnetization alignments were observed in the samples with very thin CoNbZr thickness (2-4 nm) and a maximum GMR ratio of 6.5% was obtained. The Camley-Barnas semiclassical model was extended for amorphous layer based magnetic sandwiches by considering that the mixed layers exist between the ferromagnetic and nonmagnetic layer. The calculated results agree with the experimental results very well, indicating that the new model gives a more realistic picture of the physical processes that take place in the magnetic sandwiches. Moreover, the calculated results for amorphous sandwiches also clarify that the occurrence of maximum GMR at very small thickness of amorphous layer is ascribed to the short mean-free-path in amorphous materials.展开更多
Glass-forming ability is a long-standing concern in the field of metallic glasses(MGs),which greatly limits their maximum casting size and extensive applications.In this work,we report an ultrasonic-assisted rapid col...Glass-forming ability is a long-standing concern in the field of metallic glasses(MGs),which greatly limits their maximum casting size and extensive applications.In this work,we report an ultrasonic-assisted rapid cold welding of bulk MGs without using any additives.MGs with various compositions are welded together under a 20,000-Hz highfrequency ultrasonic vibration without losing their amorphous nature.The ultrasonic technology offers the advantages of rapid bonding(<1 s)at low temperature(near room temperature)and low stress(<1 MPa).According to the phenomenon observed in the experiment,the activated fresh atoms diffuse through the broken channel port under continuous rupture of the oxide layer,and the ultrasonic vibration accelerates the atomic-diffusion process.Finally,stable bonding of the MG interface is realized.This universal ultrasonic-assisted welding process can realize the composition design of dissimilar MGs as well as tuning of new materials with new performance.展开更多
基金Project (90306015) supported by NSFC Project supported by Youth Foundation of Science and Technology of UESTC
文摘Pseudo-spin-valve (PSV) sandwiches using amorphous CoNbZr alloy as soft magnetic layer were fabricated by magnetron sputtering. The giant magnetoresistance (GMR) and its dependence on the thickness of magnetic layer were investigated. Anti-parallel magnetization alignments were observed in the samples with very thin CoNbZr thickness (2-4 nm) and a maximum GMR ratio of 6.5% was obtained. The Camley-Barnas semiclassical model was extended for amorphous layer based magnetic sandwiches by considering that the mixed layers exist between the ferromagnetic and nonmagnetic layer. The calculated results agree with the experimental results very well, indicating that the new model gives a more realistic picture of the physical processes that take place in the magnetic sandwiches. Moreover, the calculated results for amorphous sandwiches also clarify that the occurrence of maximum GMR at very small thickness of amorphous layer is ascribed to the short mean-free-path in amorphous materials.
基金supported by the Key Basic and Applied Research Program of Guangdong Province,China(2019B030302010)the National Natural Science Foundation of China(51871157,51971150 and 51775351)+2 种基金the Science and Technology Innovation Commission Shenzhen(JCYJ20170412111216258)the National Key Research and Development Program of China(2018YFA0703605)Shenzhen Basic Research Project(JCYJ20190808152409578).
文摘Glass-forming ability is a long-standing concern in the field of metallic glasses(MGs),which greatly limits their maximum casting size and extensive applications.In this work,we report an ultrasonic-assisted rapid cold welding of bulk MGs without using any additives.MGs with various compositions are welded together under a 20,000-Hz highfrequency ultrasonic vibration without losing their amorphous nature.The ultrasonic technology offers the advantages of rapid bonding(<1 s)at low temperature(near room temperature)and low stress(<1 MPa).According to the phenomenon observed in the experiment,the activated fresh atoms diffuse through the broken channel port under continuous rupture of the oxide layer,and the ultrasonic vibration accelerates the atomic-diffusion process.Finally,stable bonding of the MG interface is realized.This universal ultrasonic-assisted welding process can realize the composition design of dissimilar MGs as well as tuning of new materials with new performance.