Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing tempera...Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.展开更多
In this work the statistical mechanical equation of state was developed for volumetric properties of crystalline and amorphous polymer blends.The Ihm-Song-Mason equations of state(ISMEOS) based on temperature and dens...In this work the statistical mechanical equation of state was developed for volumetric properties of crystalline and amorphous polymer blends.The Ihm-Song-Mason equations of state(ISMEOS) based on temperature and density at melting point(T_m and ρ_m) as scaling constants were developed for crystalline polymers such as poly(propylene glycol) + poly(ethylene glycol)-200(PPG + PEG-200),poly(ethylene glycol) methyl ether-300(PEGME-350) + PEG-200 and PEGME-350 + PEG-600.Furthermore,for amorphous polymer blends containing poly(2,6-dimethyl-1,4-phenylene oxide)(PPO) + polystyrene(PS) and PS + poly(vinylmethylether)(PVME),the density and surface tension at glass transition(ρ_g and γ_g) were used for estimation of second Virial coefficient.The calculation of second Virial coefficients(B_2),effective van der Waals co-volume(b) and correction factor(α) was required for judgment about applicability of this model.The obtained results by ISMEOS for crystalline and amorphous polymer blends were in good agreement with the experimental data with absolute average deviations of 0.84%and 1.04%,respectively.展开更多
This paper reports on the preparation of Fe82.7-85.7Si2-4.9B9.2-11.2P1.5.2.7C0,8 soft magnetic amorphous alloys with a distinctly high Fe content of 93.5-95.5 wt.% by component design and composition adjustment. All a...This paper reports on the preparation of Fe82.7-85.7Si2-4.9B9.2-11.2P1.5.2.7C0,8 soft magnetic amorphous alloys with a distinctly high Fe content of 93.5-95.5 wt.% by component design and composition adjustment. All alloys can be readily fabricated into completely amorphous ribbon samples with good surface quality by the single copper roller melt-spinning method. These alloys show good bending ductility and excellent magnetic properties after annealing, i.e., low coercivity （He） of 3.3-5.9 A/m, high permeability （μe） of 5000-10000 and high flux saturation density （Bs） of 1.63-1.66 T. The mechanism of the good glass forming ability （GFA）and soft-magnetic properties are explored. The amorphous alloys with the high Fe content comparable to that of the desired high Si alloy can be promising candidates for the potential application in electric devices.展开更多
文摘Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.
文摘In this work the statistical mechanical equation of state was developed for volumetric properties of crystalline and amorphous polymer blends.The Ihm-Song-Mason equations of state(ISMEOS) based on temperature and density at melting point(T_m and ρ_m) as scaling constants were developed for crystalline polymers such as poly(propylene glycol) + poly(ethylene glycol)-200(PPG + PEG-200),poly(ethylene glycol) methyl ether-300(PEGME-350) + PEG-200 and PEGME-350 + PEG-600.Furthermore,for amorphous polymer blends containing poly(2,6-dimethyl-1,4-phenylene oxide)(PPO) + polystyrene(PS) and PS + poly(vinylmethylether)(PVME),the density and surface tension at glass transition(ρ_g and γ_g) were used for estimation of second Virial coefficient.The calculation of second Virial coefficients(B_2),effective van der Waals co-volume(b) and correction factor(α) was required for judgment about applicability of this model.The obtained results by ISMEOS for crystalline and amorphous polymer blends were in good agreement with the experimental data with absolute average deviations of 0.84%and 1.04%,respectively.
基金the National Natural Science Foundation of China(Grant No.51541106)Ningbo International Cooperation Projects(Grant No.2015D10022)+2 种基金Ningbo Major Project for Science and Technology(Grant No.201401B1003003)Ningbo Natural Science Foundations(Grant No.2015A610007)General Research Fund of Hong Kong(Grant No.CityU 102013)
文摘This paper reports on the preparation of Fe82.7-85.7Si2-4.9B9.2-11.2P1.5.2.7C0,8 soft magnetic amorphous alloys with a distinctly high Fe content of 93.5-95.5 wt.% by component design and composition adjustment. All alloys can be readily fabricated into completely amorphous ribbon samples with good surface quality by the single copper roller melt-spinning method. These alloys show good bending ductility and excellent magnetic properties after annealing, i.e., low coercivity （He） of 3.3-5.9 A/m, high permeability （μe） of 5000-10000 and high flux saturation density （Bs） of 1.63-1.66 T. The mechanism of the good glass forming ability （GFA）and soft-magnetic properties are explored. The amorphous alloys with the high Fe content comparable to that of the desired high Si alloy can be promising candidates for the potential application in electric devices.