Effects of Cr3C2,VC and La2O3 additions on the WC grain morphology,hardness and toughness of WC-10Co alloys were investigated.To intensify the grain growth driving force,nano W and nano C,instead of the conventionally...Effects of Cr3C2,VC and La2O3 additions on the WC grain morphology,hardness and toughness of WC-10Co alloys were investigated.To intensify the grain growth driving force,nano W and nano C,instead of the conventionally used WC,were used as the starting materials.To obtain a three-dimensional WC grain morphology,the natural sinter skins of the alloys were observed directly by scanning electron microscopy.It is shown that the additions have a strong ability in regulating the WC grain morphological and grain size distribution characteristics and the combinations of hardness and toughness.Due to the formation of regular and homogeneous triangular platelet WC grains,WC-10Co-0.6Cr3C2-0.06La2O3 alloy shows an excellent combination of hardness and toughness.The morphological regulation mechanism,the relationship between the WC grain morphology and the properties were discussed.展开更多
The microstructure and mechanical properties of alloy 617 B in the process of 5000 h aging at 750 °C were systematically investigated by means of SEM, TEM and mechanical analysis. M23C6 particles were dispersed i...The microstructure and mechanical properties of alloy 617 B in the process of 5000 h aging at 750 °C were systematically investigated by means of SEM, TEM and mechanical analysis. M23C6 particles were dispersed inside grains and distributed discontinuously along grain boundaries and γ′ phases were situated at intragranular sites in the process of aging. The size of precipitates increased with increasing aging time. Inter- and intra-granular carbide and γ′ phase particles inside grains resulted in the precipitation strengthening of this aged alloy, enhancing the strength and hardness. The aged alloy possessed good stabilities of hardness and strength during aging. An obvious decrease of the toughness of this aged alloy was due to γ′ phase particles limiting plastic deformation to the area nearby grain boundaries, resulting in the occurrence of crack along grain boundaries. Additionally, the intergranular cracks apparently led to a decrease in the toughness for this aged alloy due to carbide particles at grain boundaries. The toughness of this aged alloy was fairly stable possibly due to the unchanged distribution of the precipitates during aging.展开更多
Cr/CrN multilayer coatings with bilayer periods in the range from 1351 to 260 nm were prepared on 304 stainless steel substrates by arc ion plating to study the microstructure and properties of multilayer coatings and...Cr/CrN multilayer coatings with bilayer periods in the range from 1351 to 260 nm were prepared on 304 stainless steel substrates by arc ion plating to study the microstructure and properties of multilayer coatings and stimulate their application.SEM results confirm the clear periodicity of the Cr/CrN multilayer coatings and the clear interface between individual layers.XRD patterns reveal that these multilayer coatings contain Cr,CrN and Cr_2N phases.Because Cr layer is softer than its nitride layer,the hardness decreases with the shortening of the bilayer period(or increasing volume fraction of Cr layer).The Cr/CrN multilayer coating with 862 nm period possesses the highest indentation toughness due to a proper individual Cr and nitride layer thickness.However,for the Cr/CrN multilayer with the bilayer period of 1351 nm,it possesses the lowest toughness due to more nitride phase.The indentation toughness of Cr/CrN multilayer coatings is related with their bilayer period.A coating with a proper individual Cr and nitride layer thickness possesses the highest indentation toughness.展开更多
A retrogression process was applied to AA7075alloy at180,240and320°C for1,30,50,70,90and120min.After the retrogression,aging treatment was reapplied with T6conditions(120°C,24h).The mechanical properties of ...A retrogression process was applied to AA7075alloy at180,240and320°C for1,30,50,70,90and120min.After the retrogression,aging treatment was reapplied with T6conditions(120°C,24h).The mechanical properties of aged samples were determined by V-Charpy and hardness tests and also,physical properties of samples were determined by electrical conductivity tests.Moreover,microstructural properties were characterized by light microscope and transmission electron microscope.The results show that the effects of the temperature and the duration of the retrogression and reagent on the impact toughness and hardness are related to the precipitates at the grain boundary.展开更多
The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were...The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were analyzed by the laser optical modulator, the scanning electron microscopy, the energy dispersive spectrometer, the hardness and impact tests. The experimental results show that the dual phases of bainite and residual austenite can be obtained by the severity isothermal quenching, the fractographies of specimens change from quasi-cleavage to dimple at 310℃ for 60min, the impact toughness for specimens at the room temperature isothermally (achieves) 130J/cm^2, meantime and its hardness is more than 45(HRC).展开更多
Reliability and wear resistance of cutting picks play a significant role in coal mine exploitation with coal shearers.Tool bit separation,blade breaking,severe erosion of the cutting body and fatigue fractures are the...Reliability and wear resistance of cutting picks play a significant role in coal mine exploitation with coal shearers.Tool bit separation,blade breaking,severe erosion of the cutting body and fatigue fractures are the main reasons for failure of cutting picks.We carried out carburization on a 30CrMnMo alloy to synthesize a new cutting pick material with improved mechanical properties and high wear resistance.The results indicated that carburization can effectively strengthen the surface of the 30CrMnMo alloy by forming a thick carburized layer and thus significantly improve the surface hardness and wear resistance.In addition,the excellent toughness of 30CrMnMo alloy as a substrate of cutting picks can prevent brittle ruptures and fatigue fractures under high impact stress conditions.The significant decrease in both frictional coefficient and rate of erosion of this carburized 30CrMnMo alloy suggests that this alloy is a potential material for cutting picks of coal shearers after rational carburization.展开更多
Gas-boriding in N2-H2-BCl3 atmosphere resulted in the formation of a thick layer on Inconel 600 alloy.The microstructure of layer produced at 920℃for 2 h consisted of a mixture of chromium borides and nickel borides....Gas-boriding in N2-H2-BCl3 atmosphere resulted in the formation of a thick layer on Inconel 600 alloy.The microstructure of layer produced at 920℃for 2 h consisted of a mixture of chromium borides and nickel borides.The objective of investigations was to determine the influence of the chemical and phase compositions of borided layer on its mechanical properties.The nanoindentation was carried out using Berkovich diamond tip under a load of 50 m N.The gas-borided layer was characterized by high indentation hardness HIT from 1542.6 HV to 2228.7 HV and high elastic modulus EIT from 226.9 to 296.4 GPa.It was found that the mixture with higher percentage of chromium borides was the reason for the increase in HIT and EIT values.The fracture toughness(KC)was measured using Vickers microindentation technique under a load of 0.98 N.The presence of high compressive stresses in normal direction to the top surface caused the strong anisotropy of the borided layer,in respect of fracture toughness.The high difference between the lowest(0.5763 MPa·m^1/2)and the highest(4.5794 MPa·m^1/2)fracture toughness was obtained.This situation was caused by the differences in chemical and phase compositions of tested areas,presence of porosity and residual stresses.Generally,the higher KC values were obtained in areas with lower chromium content.展开更多
基金Project (51074189) supported by the National Natural Science Foundation of ChinaProject (20100162110001) supported by Research Fund for the Doctoral Program of Higher Education of ChinaProject (2011BAE09B02) supported by the National Science & Technology Special Foundation of China
文摘Effects of Cr3C2,VC and La2O3 additions on the WC grain morphology,hardness and toughness of WC-10Co alloys were investigated.To intensify the grain growth driving force,nano W and nano C,instead of the conventionally used WC,were used as the starting materials.To obtain a three-dimensional WC grain morphology,the natural sinter skins of the alloys were observed directly by scanning electron microscopy.It is shown that the additions have a strong ability in regulating the WC grain morphological and grain size distribution characteristics and the combinations of hardness and toughness.Due to the formation of regular and homogeneous triangular platelet WC grains,WC-10Co-0.6Cr3C2-0.06La2O3 alloy shows an excellent combination of hardness and toughness.The morphological regulation mechanism,the relationship between the WC grain morphology and the properties were discussed.
基金Project(2012AA050501)supported by the National High-tech Research and Development Program of ChinaProject(NY20110102)supported by the National Energy Applied Technology and Engineering Demonstration Program,China+1 种基金Project(2012CB724401)supported by the National Basic Research Program of ChinaProject(003)supported by CSEE Youth Science & Technology Innovation,China
文摘The microstructure and mechanical properties of alloy 617 B in the process of 5000 h aging at 750 °C were systematically investigated by means of SEM, TEM and mechanical analysis. M23C6 particles were dispersed inside grains and distributed discontinuously along grain boundaries and γ′ phases were situated at intragranular sites in the process of aging. The size of precipitates increased with increasing aging time. Inter- and intra-granular carbide and γ′ phase particles inside grains resulted in the precipitation strengthening of this aged alloy, enhancing the strength and hardness. The aged alloy possessed good stabilities of hardness and strength during aging. An obvious decrease of the toughness of this aged alloy was due to γ′ phase particles limiting plastic deformation to the area nearby grain boundaries, resulting in the occurrence of crack along grain boundaries. Additionally, the intergranular cracks apparently led to a decrease in the toughness for this aged alloy due to carbide particles at grain boundaries. The toughness of this aged alloy was fairly stable possibly due to the unchanged distribution of the precipitates during aging.
基金Project(51171118)supported by the National Natural Science Foundation of ChinaProject(2012-4)supported by the Liaoning Provincial Key Laboratory of Advanced Materials,Shenyang University,China
文摘Cr/CrN multilayer coatings with bilayer periods in the range from 1351 to 260 nm were prepared on 304 stainless steel substrates by arc ion plating to study the microstructure and properties of multilayer coatings and stimulate their application.SEM results confirm the clear periodicity of the Cr/CrN multilayer coatings and the clear interface between individual layers.XRD patterns reveal that these multilayer coatings contain Cr,CrN and Cr_2N phases.Because Cr layer is softer than its nitride layer,the hardness decreases with the shortening of the bilayer period(or increasing volume fraction of Cr layer).The Cr/CrN multilayer coating with 862 nm period possesses the highest indentation toughness due to a proper individual Cr and nitride layer thickness.However,for the Cr/CrN multilayer with the bilayer period of 1351 nm,it possesses the lowest toughness due to more nitride phase.The indentation toughness of Cr/CrN multilayer coatings is related with their bilayer period.A coating with a proper individual Cr and nitride layer thickness possesses the highest indentation toughness.
基金supported by Yildiz Technical University Scientific Research Project Unit under Contract No:2016-07-02-DOP02
文摘A retrogression process was applied to AA7075alloy at180,240and320°C for1,30,50,70,90and120min.After the retrogression,aging treatment was reapplied with T6conditions(120°C,24h).The mechanical properties of aged samples were determined by V-Charpy and hardness tests and also,physical properties of samples were determined by electrical conductivity tests.Moreover,microstructural properties were characterized by light microscope and transmission electron microscope.The results show that the effects of the temperature and the duration of the retrogression and reagent on the impact toughness and hardness are related to the precipitates at the grain boundary.
基金Project(10541225) supported by the Ministry of Education of Heilongjiang Province
文摘The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were analyzed by the laser optical modulator, the scanning electron microscopy, the energy dispersive spectrometer, the hardness and impact tests. The experimental results show that the dual phases of bainite and residual austenite can be obtained by the severity isothermal quenching, the fractographies of specimens change from quasi-cleavage to dimple at 310℃ for 60min, the impact toughness for specimens at the room temperature isothermally (achieves) 130J/cm^2, meantime and its hardness is more than 45(HRC).
基金the Youth Foundation of China University of Mining & Technology (No.2009A056)the Tribology Science Fund from State Key Laboratory of Tribology at Tsinghua University (No.SKLTKF08A01)+1 种基金the National Natural Science Foundation of China (Nos.50905180 and 51005234)the National Science and Technology Pillar Program in the Eleventh Five-Year Plan Period (No.2008BAB36B02)
文摘Reliability and wear resistance of cutting picks play a significant role in coal mine exploitation with coal shearers.Tool bit separation,blade breaking,severe erosion of the cutting body and fatigue fractures are the main reasons for failure of cutting picks.We carried out carburization on a 30CrMnMo alloy to synthesize a new cutting pick material with improved mechanical properties and high wear resistance.The results indicated that carburization can effectively strengthen the surface of the 30CrMnMo alloy by forming a thick carburized layer and thus significantly improve the surface hardness and wear resistance.In addition,the excellent toughness of 30CrMnMo alloy as a substrate of cutting picks can prevent brittle ruptures and fatigue fractures under high impact stress conditions.The significant decrease in both frictional coefficient and rate of erosion of this carburized 30CrMnMo alloy suggests that this alloy is a potential material for cutting picks of coal shearers after rational carburization.
基金financially supported by Ministry of ScienceHigher Education in Poland as a part of the “02/24/DSPB” Project
文摘Gas-boriding in N2-H2-BCl3 atmosphere resulted in the formation of a thick layer on Inconel 600 alloy.The microstructure of layer produced at 920℃for 2 h consisted of a mixture of chromium borides and nickel borides.The objective of investigations was to determine the influence of the chemical and phase compositions of borided layer on its mechanical properties.The nanoindentation was carried out using Berkovich diamond tip under a load of 50 m N.The gas-borided layer was characterized by high indentation hardness HIT from 1542.6 HV to 2228.7 HV and high elastic modulus EIT from 226.9 to 296.4 GPa.It was found that the mixture with higher percentage of chromium borides was the reason for the increase in HIT and EIT values.The fracture toughness(KC)was measured using Vickers microindentation technique under a load of 0.98 N.The presence of high compressive stresses in normal direction to the top surface caused the strong anisotropy of the borided layer,in respect of fracture toughness.The high difference between the lowest(0.5763 MPa·m^1/2)and the highest(4.5794 MPa·m^1/2)fracture toughness was obtained.This situation was caused by the differences in chemical and phase compositions of tested areas,presence of porosity and residual stresses.Generally,the higher KC values were obtained in areas with lower chromium content.