Fe75Zr3Si13B9 magnetic amorphous powders were fabricated by mechanical alloying. Bulk amorphous and nanocrystalline alloys with 20 mm in diameter and 7 mm in height were fabricated by the spark plasma sintering techno...Fe75Zr3Si13B9 magnetic amorphous powders were fabricated by mechanical alloying. Bulk amorphous and nanocrystalline alloys with 20 mm in diameter and 7 mm in height were fabricated by the spark plasma sintering technology at different sintering temperatures. The phase composition, glass transition temperature （Tg）, onset crystallization temperature （Tx）, peak temperature （Tp） and super-cooled liquid region （ΔTx） of Fe75Zr3Si13B9 amorphous powders were analyzed by X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The phase transition, microstructure, mechanical properties and magnetic performance of the bulk alloys were discussed with X-ray diffractometer, scanning electron microscope （SEM）, Gleeble 3500 and vibration sample magnetometer （VSM）, respectively. It is found that with the increase in the sintering temperature at the pressure of 500 MPa, the density, compressive strength, micro-hardness and saturation magnetization of the sintering samples improved significantly, the amorphous phase began to crystallize gradually. Finally, the desirable amorphous and nanocrystalline magnetic materials at the sintering temperature of 863.15 K and the pressure of 500 MPa have a density of 6.9325 g/cm3, a compressive strength of 1140.28 MPa and a saturation magnetization of 1.28 T.展开更多
Clay has a significant influence on the relationship between resistivity index I and water saturation Sw （i.e, I-Sw relationship） of reservoir rocks because it complicates the current paths of these rocks. It is dif...Clay has a significant influence on the relationship between resistivity index I and water saturation Sw （i.e, I-Sw relationship） of reservoir rocks because it complicates the current paths of these rocks. It is difficult to reveal the physical mechanisms of these clay effects on the conductivities of various rocks by physical laboratory measurements because the pore structure, micro distribution and content of clay inside a rock can not be observed and controlled during the experiments. We present a digital rock approach to study these clay effects on the electrical transport properties of reservoir rocks at pore scale using lattice gas automation （LGA） method. The digital rock samples are constructed with the information of grain size distribution from SEM images of reservoir rocks. The LGA is then applied on these digital rocks fully saturated with fluids to simulate the electrical transport properties for revealing the effects of volume and distribution patterns of clay on the non-Archie behaviors of the I-Sw relationship. The very good agreement between the simulated results and the laboratory measurements clearly demonstrates the validity of the LGA in numerical research of rock physics. Based on these studies, a new model has been developed for quantitatively describing the relationship between the saturation exponent and the volume of clay （Vsh）. This development may improve the evaluation for the fluid saturations in reservoir rocks.展开更多
The epoxidation of unsaturated fatty acid methyl esters(FAMEs)by peroxyacetic acid generated in situ from hydrogen peroxide and acetic acid was studied in the presence of SO3H-functional Brnsted acidic ionic liquid (I...The epoxidation of unsaturated fatty acid methyl esters(FAMEs)by peroxyacetic acid generated in situ from hydrogen peroxide and acetic acid was studied in the presence of SO3H-functional Brnsted acidic ionic liquid (IL)[C3SO3HMIM][HSO4]as catalyst.The effects of hydrogen peroxide/ethylenic unsaturation ratio,acetic acid concentration,IL concentration,recycling of the IL catalyst,and temperature on the conversion to oxirane were studied.The kinetics and thermodynamics of unsaturated FAMEs epoxidation and the kinetics of oxirane cleavage of the epoxidized FAMEs by acetic acid were also studied.The conversion of ethylenic unsaturation group to oxirane, the reaction rate of the conversion to oxirane,and the rate of hydrolysis(oxirane cleavage)were higher by using the IL catalyst.展开更多
Magnetic properties and magnetocaloric effects （MCEs） of the HoPdA1 compounds with the hexagonal ZrNiAl-type and the orthorhombic TiNiSi-type structures are investigated. Both the compounds are found to be antiferro...Magnetic properties and magnetocaloric effects （MCEs） of the HoPdA1 compounds with the hexagonal ZrNiAl-type and the orthorhombic TiNiSi-type structures are investigated. Both the compounds are found to be antiferromagnet with the Nrel tem- perature TN=12 and 10 K, respectively. A field-induced metamagnetic transition from antiferromagnetic （AFM） state to ferro- magnetic （FM） state is observed below TN. For the hexagonal HoPdA1, a small magnetic field can induce an FM-like state due to a weak AFM coupling, which leads to a high saturation magnetization and gives rise to a large MCE around TN. The maxi- mal value of magnetic entropy change （ASM） is -20.6 J/kg K with a refrigerant capacity （RC） value of 386 J/kg for a field change of 0-5 T. For the orthorhombic HoPdA1, the critical field required for metamagnetic transition is estimated to be about 1.5 T, showing a strong AFM coupling. However, the maximal ASM value is still -13.7 J/kg K around TN for a field change of 0-5 T. The large reversible ASM and considerable RC suggest that HoPdA1 may be an appropriate candidate for magnetic re- frigerant in a low temperature range.展开更多
Self-assembled Fe_(3)O_(4)hierarchical microspheres(HMSs) were prepared by a one-pot synchronous reduction–self-assembling (SRSA) hydrothermal method.In this simple and inexpensive synthetic process,only glycerol,wat...Self-assembled Fe_(3)O_(4)hierarchical microspheres(HMSs) were prepared by a one-pot synchronous reduction–self-assembling (SRSA) hydrothermal method.In this simple and inexpensive synthetic process,only glycerol,water,and a single iron source (potassium ferricyanide (K3[Fe(CN)6]))were employed as reactants without additional reductants,surfactants,or additives.The iron source,K3[Fe(CN)6],and glycerol significantly affected the synthesis of Fe_(3)O_(4)HMSs.Fe_(3)O_(4)HMSs with a self-assembled spherical shape readily functioned as high-performance anode materials for lithiumion batteries with a specific capacity of>1000 mA h g^(-1)at0.5 A g^(-1)after 270 cycles.Further charging and discharging results revealed that Fe_(3)O_(4)HMSs displayed good reversible performance (>1000 mA h g^(-1)) and cycling stability (700 cycles) at 0.5 A g^(-1).Furthermore,as multifunctional materials,the as-obtained Fe_(3)O_(4)HMSs also exhibited high saturation magnetization (99.5 emu g^(-1)) at room temperature (25°C) and could be further employed as efficient and magnetically recyclable catalysts for the hydrogenation of nitro compounds.展开更多
基金Project(13961001D)supported by the Key Basic Research Project of Hebei Province,ChinaProject(2013BAE08B01)supported by the National Key Technology R&D Program of China
文摘Fe75Zr3Si13B9 magnetic amorphous powders were fabricated by mechanical alloying. Bulk amorphous and nanocrystalline alloys with 20 mm in diameter and 7 mm in height were fabricated by the spark plasma sintering technology at different sintering temperatures. The phase composition, glass transition temperature （Tg）, onset crystallization temperature （Tx）, peak temperature （Tp） and super-cooled liquid region （ΔTx） of Fe75Zr3Si13B9 amorphous powders were analyzed by X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The phase transition, microstructure, mechanical properties and magnetic performance of the bulk alloys were discussed with X-ray diffractometer, scanning electron microscope （SEM）, Gleeble 3500 and vibration sample magnetometer （VSM）, respectively. It is found that with the increase in the sintering temperature at the pressure of 500 MPa, the density, compressive strength, micro-hardness and saturation magnetization of the sintering samples improved significantly, the amorphous phase began to crystallize gradually. Finally, the desirable amorphous and nanocrystalline magnetic materials at the sintering temperature of 863.15 K and the pressure of 500 MPa have a density of 6.9325 g/cm3, a compressive strength of 1140.28 MPa and a saturation magnetization of 1.28 T.
基金sponsored by the National Natural Science Foundation of China（Grant No.41074103） the National Key Fundamental R＆D Project（Grant No.2007CB209601） the China National Petroleum Cooperation Fundamental Research Program（Grant No.06A30102）
文摘Clay has a significant influence on the relationship between resistivity index I and water saturation Sw （i.e, I-Sw relationship） of reservoir rocks because it complicates the current paths of these rocks. It is difficult to reveal the physical mechanisms of these clay effects on the conductivities of various rocks by physical laboratory measurements because the pore structure, micro distribution and content of clay inside a rock can not be observed and controlled during the experiments. We present a digital rock approach to study these clay effects on the electrical transport properties of reservoir rocks at pore scale using lattice gas automation （LGA） method. The digital rock samples are constructed with the information of grain size distribution from SEM images of reservoir rocks. The LGA is then applied on these digital rocks fully saturated with fluids to simulate the electrical transport properties for revealing the effects of volume and distribution patterns of clay on the non-Archie behaviors of the I-Sw relationship. The very good agreement between the simulated results and the laboratory measurements clearly demonstrates the validity of the LGA in numerical research of rock physics. Based on these studies, a new model has been developed for quantitatively describing the relationship between the saturation exponent and the volume of clay （Vsh）. This development may improve the evaluation for the fluid saturations in reservoir rocks.
文摘The epoxidation of unsaturated fatty acid methyl esters(FAMEs)by peroxyacetic acid generated in situ from hydrogen peroxide and acetic acid was studied in the presence of SO3H-functional Brnsted acidic ionic liquid (IL)[C3SO3HMIM][HSO4]as catalyst.The effects of hydrogen peroxide/ethylenic unsaturation ratio,acetic acid concentration,IL concentration,recycling of the IL catalyst,and temperature on the conversion to oxirane were studied.The kinetics and thermodynamics of unsaturated FAMEs epoxidation and the kinetics of oxirane cleavage of the epoxidized FAMEs by acetic acid were also studied.The conversion of ethylenic unsaturation group to oxirane, the reaction rate of the conversion to oxirane,and the rate of hydrolysis(oxirane cleavage)were higher by using the IL catalyst.
基金supported by the National Natural Science Foundation of China (Grant Nos. 50731007 and 51021061)the Knowledge Innovation Project of the Chinese Academy of Sciencesthe High-Technology Research and Development Program of China
文摘Magnetic properties and magnetocaloric effects （MCEs） of the HoPdA1 compounds with the hexagonal ZrNiAl-type and the orthorhombic TiNiSi-type structures are investigated. Both the compounds are found to be antiferromagnet with the Nrel tem- perature TN=12 and 10 K, respectively. A field-induced metamagnetic transition from antiferromagnetic （AFM） state to ferro- magnetic （FM） state is observed below TN. For the hexagonal HoPdA1, a small magnetic field can induce an FM-like state due to a weak AFM coupling, which leads to a high saturation magnetization and gives rise to a large MCE around TN. The maxi- mal value of magnetic entropy change （ASM） is -20.6 J/kg K with a refrigerant capacity （RC） value of 386 J/kg for a field change of 0-5 T. For the orthorhombic HoPdA1, the critical field required for metamagnetic transition is estimated to be about 1.5 T, showing a strong AFM coupling. However, the maximal ASM value is still -13.7 J/kg K around TN for a field change of 0-5 T. The large reversible ASM and considerable RC suggest that HoPdA1 may be an appropriate candidate for magnetic re- frigerant in a low temperature range.
基金the financial support from the National Natural Science Foundation of China (21501004,21771003,21901007 and 21671005)Anhui Provincial Natural Science Foundation for Distinguished Youth (1808085J27)。
文摘Self-assembled Fe_(3)O_(4)hierarchical microspheres(HMSs) were prepared by a one-pot synchronous reduction–self-assembling (SRSA) hydrothermal method.In this simple and inexpensive synthetic process,only glycerol,water,and a single iron source (potassium ferricyanide (K3[Fe(CN)6]))were employed as reactants without additional reductants,surfactants,or additives.The iron source,K3[Fe(CN)6],and glycerol significantly affected the synthesis of Fe_(3)O_(4)HMSs.Fe_(3)O_(4)HMSs with a self-assembled spherical shape readily functioned as high-performance anode materials for lithiumion batteries with a specific capacity of>1000 mA h g^(-1)at0.5 A g^(-1)after 270 cycles.Further charging and discharging results revealed that Fe_(3)O_(4)HMSs displayed good reversible performance (>1000 mA h g^(-1)) and cycling stability (700 cycles) at 0.5 A g^(-1).Furthermore,as multifunctional materials,the as-obtained Fe_(3)O_(4)HMSs also exhibited high saturation magnetization (99.5 emu g^(-1)) at room temperature (25°C) and could be further employed as efficient and magnetically recyclable catalysts for the hydrogenation of nitro compounds.