The effects of surface-modified porous titanium implants with different porosities and pore sizes on osseointegration were investigated in vivo.Three porous titanium implants(A30,A40 and A50 containing volume fraction...The effects of surface-modified porous titanium implants with different porosities and pore sizes on osseointegration were investigated in vivo.Three porous titanium implants(A30,A40 and A50 containing volume fractions of space-holder NaCl being 30%,40%and 50%,respectively)were manufactured by metal injection moulding(MIM).The surface-modified implants were implanted into muscles and femurs of hybrid male dogs.Interface osteogenic activity and histological bone ingrowth of porous titanium implants were evaluated at 28,56 and 84 d.The results showed that when additive space-holder amount of NaCl increased from 30%to 50%(volume fraction),the general porosity and mass fraction of macropores of porous titanium rose from 42.4%to 62.0%and from 8.3%to 69.3%,respectively.Histologic sections and fluorescent labeling showed that the A50 implant demonstrated a significantly higher osteogenic capacity at 28 d than other implants.Bone ingrowth into the A30 implant was lower than that into other implants at 84 d.Therefore,the pore structure of A50 implant was suitable for new bone tissue to grow into porous implant.展开更多
A novel antibacterial biomimetic porous titanium implant with good osseointegration was prepared by freeze-casting and thermal oxidation.Bone integration properties of the porous titanium implant were evaluated by cel...A novel antibacterial biomimetic porous titanium implant with good osseointegration was prepared by freeze-casting and thermal oxidation.Bone integration properties of the porous titanium implant were evaluated by cell proliferation assay,alkaline phosphatase activity assay,X-ray examination and hard bone tissue biopsy.The in vitro cell proliferation and the level of differentiation of the group with a modified nano-porous implant surface were significantly higher than those in the group without surface modification and the dense titanium control group(P<0.05).In vivo,bone growth and osteogenesis were found in the experimental groups with modified and unmodified porous titanium implants;osteoblasts in the modified group had more mature differentiation in the pores compared to the unmodified group.Such implants can form solid,biologically compatible bone grafts with bone tissues,exhibiting good osseointegration.展开更多
基金Project(81571021) supported by the National Natural Science Foundation of ChinaProjects(2015WK3012,2018SK2017) supported by the Hunan Provincial Science and Technology Department Project,ChinaProject(20160301) supported by New Talent Project of the Third Xiangya Hospital of Central South University,China
文摘The effects of surface-modified porous titanium implants with different porosities and pore sizes on osseointegration were investigated in vivo.Three porous titanium implants(A30,A40 and A50 containing volume fractions of space-holder NaCl being 30%,40%and 50%,respectively)were manufactured by metal injection moulding(MIM).The surface-modified implants were implanted into muscles and femurs of hybrid male dogs.Interface osteogenic activity and histological bone ingrowth of porous titanium implants were evaluated at 28,56 and 84 d.The results showed that when additive space-holder amount of NaCl increased from 30%to 50%(volume fraction),the general porosity and mass fraction of macropores of porous titanium rose from 42.4%to 62.0%and from 8.3%to 69.3%,respectively.Histologic sections and fluorescent labeling showed that the A50 implant demonstrated a significantly higher osteogenic capacity at 28 d than other implants.Bone ingrowth into the A30 implant was lower than that into other implants at 84 d.Therefore,the pore structure of A50 implant was suitable for new bone tissue to grow into porous implant.
基金Projects (51290295,51305464) supported by the National Natural Science Foundation of ChinaProject (2016JJ6156) supported by the Natural Science Foundation of Hunan Province,China+1 种基金Project (2016JC2064) supported by Key Research and Development Project of Hunan Province,ChinaProject (20130162120094) supported by Specialized Research Fund for the Doctoral Program of Higher Education,China
文摘A novel antibacterial biomimetic porous titanium implant with good osseointegration was prepared by freeze-casting and thermal oxidation.Bone integration properties of the porous titanium implant were evaluated by cell proliferation assay,alkaline phosphatase activity assay,X-ray examination and hard bone tissue biopsy.The in vitro cell proliferation and the level of differentiation of the group with a modified nano-porous implant surface were significantly higher than those in the group without surface modification and the dense titanium control group(P<0.05).In vivo,bone growth and osteogenesis were found in the experimental groups with modified and unmodified porous titanium implants;osteoblasts in the modified group had more mature differentiation in the pores compared to the unmodified group.Such implants can form solid,biologically compatible bone grafts with bone tissues,exhibiting good osseointegration.