The influence on fine particle aggregation and flotation behavior induced by high intensity conditioning(HIC) from saturated of the slurry with CO2 saturation was investigated.Bubble size measurements were conducted.T...The influence on fine particle aggregation and flotation behavior induced by high intensity conditioning(HIC) from saturated of the slurry with CO2 saturation was investigated.Bubble size measurements were conducted.The effect of dissolved gas,xanthate addition and agitation speed on fine sphalerite particle aggregation-and flotation-behavior were studied.The results show that during HIC in air or CO2 saturated water xanthate acts as a frother.The dissolved gas content in the pulp and HIC play a synergistic role in promoting fine particle aggregation and hence flotation;a significantly enhanced aggregation of fine sphalerite particles in a CO2 saturated slurry by HIC is observed.The aggregate size increased when the agitation speed was increased from 700 r/min to 1500 r/min.Increasing the HIC speed to 1500 r/min caused a positive impact on flotation kinetics.Further increasing the speed to 2000 r/min resulted in an adverse effect on flotation kinetics.展开更多
Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_...Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_(2)O_(3) particles are uniformly distributed in the Al matrix.Brinell hardness results indicate that different from the traditional 6061 Al matrix alloy,the aging kinetics of the composite is obviously accelerated by the reinforcement particles.The T6-treated composite exhibits excellent tensile properties at both room temperature and elevated temperature.Especially at 350℃,the T6-treated composite not only has a high yield strength of 121 MPa and ultimate tensile strength of 128 MPa,but also exhibits a large elongation of 11.6%.Different strengthening mechanisms of nano-AlN and submicron-Al_(2)O_(3) particles were also discussed in detail.展开更多
The mechanism of high pressure roll grinding on improvement of compression strength of oxidized hematite pellets was researched by considering their roasting properties. The results indicate that oxidized hematite pel...The mechanism of high pressure roll grinding on improvement of compression strength of oxidized hematite pellets was researched by considering their roasting properties. The results indicate that oxidized hematite pellets require higher preheating temperature and longer preheating time to attain required compression strength of pellets compared with the common magnetite oxidized pellets. It is found that when the hematite concentrates are pretreated by high pressure roll grinding （HPRG）, the compression strengths of preheated and roasted oxidized hematite pellets get improved even with lower preheating and roasting temperatures and shorter preheating and roasting time. The mechanism for HPRG to improve roasting properties of oxidized pellets were investigated and the cause mainly lies in the increase of micro-sized particles and the decrease of dispersion degree for hematite concentrates, which promotes the hematite concentrate particles to be compacted, the solid-phase crystallization, and finally the formation of Fe203 bonding bridges during subsequent high temperature roasting process.展开更多
基金Project 50674103 supported by the National Natural Science Foundation of China
文摘The influence on fine particle aggregation and flotation behavior induced by high intensity conditioning(HIC) from saturated of the slurry with CO2 saturation was investigated.Bubble size measurements were conducted.The effect of dissolved gas,xanthate addition and agitation speed on fine sphalerite particle aggregation-and flotation-behavior were studied.The results show that during HIC in air or CO2 saturated water xanthate acts as a frother.The dissolved gas content in the pulp and HIC play a synergistic role in promoting fine particle aggregation and hence flotation;a significantly enhanced aggregation of fine sphalerite particles in a CO2 saturated slurry by HIC is observed.The aggregate size increased when the agitation speed was increased from 700 r/min to 1500 r/min.Increasing the HIC speed to 1500 r/min caused a positive impact on flotation kinetics.Further increasing the speed to 2000 r/min resulted in an adverse effect on flotation kinetics.
基金supported by the Key Program of National Natural Science Foundation of China(No.51731007)the National Natural Science Foundation of China(No.52071179)the Fundamental Research Funds for the Central Universities(No.30920021160).
文摘Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_(2)O_(3) particles are uniformly distributed in the Al matrix.Brinell hardness results indicate that different from the traditional 6061 Al matrix alloy,the aging kinetics of the composite is obviously accelerated by the reinforcement particles.The T6-treated composite exhibits excellent tensile properties at both room temperature and elevated temperature.Especially at 350℃,the T6-treated composite not only has a high yield strength of 121 MPa and ultimate tensile strength of 128 MPa,but also exhibits a large elongation of 11.6%.Different strengthening mechanisms of nano-AlN and submicron-Al_(2)O_(3) particles were also discussed in detail.
基金Project(50725416) supported by the National Natural Science Funds for Distinguished Young Scholars of China
文摘The mechanism of high pressure roll grinding on improvement of compression strength of oxidized hematite pellets was researched by considering their roasting properties. The results indicate that oxidized hematite pellets require higher preheating temperature and longer preheating time to attain required compression strength of pellets compared with the common magnetite oxidized pellets. It is found that when the hematite concentrates are pretreated by high pressure roll grinding （HPRG）, the compression strengths of preheated and roasted oxidized hematite pellets get improved even with lower preheating and roasting temperatures and shorter preheating and roasting time. The mechanism for HPRG to improve roasting properties of oxidized pellets were investigated and the cause mainly lies in the increase of micro-sized particles and the decrease of dispersion degree for hematite concentrates, which promotes the hematite concentrate particles to be compacted, the solid-phase crystallization, and finally the formation of Fe203 bonding bridges during subsequent high temperature roasting process.