Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polyca...Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polycarboxlic series high range water reduce agent and sodium sulfate hardening accelerating agent. Two kinds of curing condition, namely steam curing condition and standard curing condition, are adopted. The result shows that HPC, added with polycarboxlic series of high performance water reducer, has high workability and strength, while sodium sulfate accelerating agent causes poor workability and low strength. Thus for vapor-cured HPC and its formulations, naphthalene series high range water reducing agent with less sodium sulfate should be given pri- ority. Therefore, the differences of curing conditions should be considered when selecting HPC admixtures.展开更多
Biaxial compression tests are performed on 100 mm × 100 mm × 100 mm cubic specimens of plain high-strength highperformance concrete （HSHPC） at seven kinds of stress ratios, σ2：σ3 =0 ： - 1, -0.20 ： - 1...Biaxial compression tests are performed on 100 mm × 100 mm × 100 mm cubic specimens of plain high-strength highperformance concrete （HSHPC） at seven kinds of stress ratios, σ2：σ3 =0 ： - 1, -0.20 ： - 1, -0.30 ： - 1, -0.40 ： - 1, -0.50 ： -1, -0. 75 ： - 1, and - 1.00 ： - 1 after exposure to normal and high temperatures of 20, 200, 300, 400, 500 and 600 ℃, using a large static-dynamic true triaxial machine. Frictionreducing pads are three layers of plastic membranes with glycerine in-between for the compressive loading plane. Failure modes of the specimens are described. The two principally static compressive strengths are measured. The influences of the temperatures and stress ratios on the biaxial strengths of HSHPC after exposure to high temperatures are also analyzed. The experimental results show that the uniaxial compressive strength of plain HSHPC after exposure to high temperatures does not decrease completely with the increase in temperature; the ratios of the biaxial to its uniaxial compressive strengths depend on the stress ratios and brittleness-stiffness of HSHPC after exposure to different high temperatures. The formula of the Kupfer-Gerstle failure criterion modified with the temperature and stress ratio parameters for plain HSHPC is proposed.展开更多
The thermophysical properties,such as thermal conductivity,thermal diffusivity,specific heat capacity and linear thermal expansion of reactive powder concrete(RPC) with different steel fiber volumetric fractions are i...The thermophysical properties,such as thermal conductivity,thermal diffusivity,specific heat capacity and linear thermal expansion of reactive powder concrete(RPC) with different steel fiber volumetric fractions are investigated by means of high temperature tests. The thermophysical characteristics of RPC with different fiber volumes under different temperatures are analyzed and compared with those of the common high-strength concrete and high-performance concrete. The empirical relationships of thermophysical properties with temperature and fiber volume are identified. By the heat transfer and solid physics methods,the microscopic physical mechanism of heat transfer process and heat conduction properties of RPC are investigated,and the theoretical formulas of specific heat capacity and thermal expansion coefficient are derived,respectively. The effects of temperature and steel fibers on the specific heat capacity and the thermal expansion coefficient are quantitatively analyzed and the discriminant conditions are provided. It is shown that the experimental results are consistent with the theoretical prediction.展开更多
基金Supported by the National Basic Research Programe of China("973"Program)(2009CB623203)the Construction Department of Zhejiang Province Foundation(1006)+1 种基金the Education Department of Zhejiang Province Foundation(Y200909029)the Doctoral Innovation Foundation of Nanjing University of Aeronautics andAstronautics(BCXJ07-04)~~
文摘Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polycarboxlic series high range water reduce agent and sodium sulfate hardening accelerating agent. Two kinds of curing condition, namely steam curing condition and standard curing condition, are adopted. The result shows that HPC, added with polycarboxlic series of high performance water reducer, has high workability and strength, while sodium sulfate accelerating agent causes poor workability and low strength. Thus for vapor-cured HPC and its formulations, naphthalene series high range water reducing agent with less sodium sulfate should be given pri- ority. Therefore, the differences of curing conditions should be considered when selecting HPC admixtures.
文摘Biaxial compression tests are performed on 100 mm × 100 mm × 100 mm cubic specimens of plain high-strength highperformance concrete （HSHPC） at seven kinds of stress ratios, σ2：σ3 =0 ： - 1, -0.20 ： - 1, -0.30 ： - 1, -0.40 ： - 1, -0.50 ： -1, -0. 75 ： - 1, and - 1.00 ： - 1 after exposure to normal and high temperatures of 20, 200, 300, 400, 500 and 600 ℃, using a large static-dynamic true triaxial machine. Frictionreducing pads are three layers of plastic membranes with glycerine in-between for the compressive loading plane. Failure modes of the specimens are described. The two principally static compressive strengths are measured. The influences of the temperatures and stress ratios on the biaxial strengths of HSHPC after exposure to high temperatures are also analyzed. The experimental results show that the uniaxial compressive strength of plain HSHPC after exposure to high temperatures does not decrease completely with the increase in temperature; the ratios of the biaxial to its uniaxial compressive strengths depend on the stress ratios and brittleness-stiffness of HSHPC after exposure to different high temperatures. The formula of the Kupfer-Gerstle failure criterion modified with the temperature and stress ratio parameters for plain HSHPC is proposed.
基金supported by the National Natural Science Foundation of China (Grant No. 50974125)the National Basic Research Program of China ("973" Project) (Grant Nos.2010CB226804,2002CB412705)the Beijing Key Laboratory Projects
文摘The thermophysical properties,such as thermal conductivity,thermal diffusivity,specific heat capacity and linear thermal expansion of reactive powder concrete(RPC) with different steel fiber volumetric fractions are investigated by means of high temperature tests. The thermophysical characteristics of RPC with different fiber volumes under different temperatures are analyzed and compared with those of the common high-strength concrete and high-performance concrete. The empirical relationships of thermophysical properties with temperature and fiber volume are identified. By the heat transfer and solid physics methods,the microscopic physical mechanism of heat transfer process and heat conduction properties of RPC are investigated,and the theoretical formulas of specific heat capacity and thermal expansion coefficient are derived,respectively. The effects of temperature and steel fibers on the specific heat capacity and the thermal expansion coefficient are quantitatively analyzed and the discriminant conditions are provided. It is shown that the experimental results are consistent with the theoretical prediction.