Ni54Mn25Ga21 alloy was prepared to investigate the microstructure, martensitic transformation and high-temperature shape-memory effect. Ni54Mn25Ga21 alloy exhibits single phase of non-modulated martensite with tetrago...Ni54Mn25Ga21 alloy was prepared to investigate the microstructure, martensitic transformation and high-temperature shape-memory effect. Ni54Mn25Ga21 alloy exhibits single phase of non-modulated martensite with tetragonal structure at room temperature. Its martensitic start temperature Ms, martensitic finish temperature Mf on cooling, and austenitic start temperature As, austenitic finish temperature Af on heating are 260.2, 237.8, 262.5 and 287.8 ℃, respectively. The compressive strength and strain of Ni54Mn25Ga21 single crystal were measured to be 845 MPa and 20.5%, respectively, with compressive axis along the growth direction of the rods. An excellent shape-memory strain of 6.1%, which is the best performance among high-temperature shape-memory alloys up to the present, is obtained when prestrained to 8%.展开更多
基金Project(50771086)supported by the National Natural Science Foundation of ChinaProject(NCET-09-0676)supported by Program for New Century Excellent Talents in University(NCET),China+1 种基金Project supported by Program for New Century Excellent Talents in Fujian Provincial University(NCETFJ),ChinaProject(2009H0039)supported by Fujian Provincial Department of Science and Technology,China
基金Project(50371005) supported by the National Natural Science Foundation of China
文摘Ni54Mn25Ga21 alloy was prepared to investigate the microstructure, martensitic transformation and high-temperature shape-memory effect. Ni54Mn25Ga21 alloy exhibits single phase of non-modulated martensite with tetragonal structure at room temperature. Its martensitic start temperature Ms, martensitic finish temperature Mf on cooling, and austenitic start temperature As, austenitic finish temperature Af on heating are 260.2, 237.8, 262.5 and 287.8 ℃, respectively. The compressive strength and strain of Ni54Mn25Ga21 single crystal were measured to be 845 MPa and 20.5%, respectively, with compressive axis along the growth direction of the rods. An excellent shape-memory strain of 6.1%, which is the best performance among high-temperature shape-memory alloys up to the present, is obtained when prestrained to 8%.