YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering m...YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering method. The structures and phaseevolution of the coatings were studied with X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersivespectrometry （EDS）. The relation between microstructures and properties of the BPs-coated samples was discussed. The results showthat the adhesion strength and gain mass of the BPs-coated samples with isothermal oxidation at 1100℃ for 100 h are 3.3 N and0.00817 mg/cm^2, respectively, while those of the non-BPs-coated sample are 2.6 N and 0.00559 mg/cm^2, respectively. The EDSmapping analysis indicates that an obvious outward diffusion of Cr from the substrate to BPs coated samples occurs after isothermaloxidation. The BPs-coated sample shows the superior adhesion and oxidation resistance compared with non-BPs-coated samples.展开更多
Thermo-plasticity of homogenized 7050 aluminum ingot was investigated by instantaneous tensile tests conducted at different temperatures. The results show that, with the increase of testing temperatures, the strength ...Thermo-plasticity of homogenized 7050 aluminum ingot was investigated by instantaneous tensile tests conducted at different temperatures. The results show that, with the increase of testing temperatures, the strength decreases, and the plasticity increases firstly and then decreases in homogenized 7050 ingot. When the studied alloy is deformed between 380℃ and 420℃, the deformation resistance is lower and plasticity is better. And the actual heating temperature for ingot before hot extrusion should be controlled between 360 ~C and 400 ~C. At low tensile temperatures, the deformation structure is mainly composed of dislocation substructure. With the increase of testing temperatures, transgranular fracture transforms into intergranular fracture progressively during deformation. At high tensile temperatures, the grain boundaries are weakened, deformation is concentrated at the grain boundaries and the re-orientation of equilibrium phases at grain boundaries appears.展开更多
基金Project(51271111)supported by the National Natural Science Foundation of ChinaProject(14KY0515)support by Graduate Research and Innovation Special Projects of Shanghai University of Engineering Science,China
文摘YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering method. The structures and phaseevolution of the coatings were studied with X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersivespectrometry （EDS）. The relation between microstructures and properties of the BPs-coated samples was discussed. The results showthat the adhesion strength and gain mass of the BPs-coated samples with isothermal oxidation at 1100℃ for 100 h are 3.3 N and0.00817 mg/cm^2, respectively, while those of the non-BPs-coated sample are 2.6 N and 0.00559 mg/cm^2, respectively. The EDSmapping analysis indicates that an obvious outward diffusion of Cr from the substrate to BPs coated samples occurs after isothermaloxidation. The BPs-coated sample shows the superior adhesion and oxidation resistance compared with non-BPs-coated samples.
基金Project(JPPT-115-2-948) supported by the National Civilian Matched Program of China
文摘Thermo-plasticity of homogenized 7050 aluminum ingot was investigated by instantaneous tensile tests conducted at different temperatures. The results show that, with the increase of testing temperatures, the strength decreases, and the plasticity increases firstly and then decreases in homogenized 7050 ingot. When the studied alloy is deformed between 380℃ and 420℃, the deformation resistance is lower and plasticity is better. And the actual heating temperature for ingot before hot extrusion should be controlled between 360 ~C and 400 ~C. At low tensile temperatures, the deformation structure is mainly composed of dislocation substructure. With the increase of testing temperatures, transgranular fracture transforms into intergranular fracture progressively during deformation. At high tensile temperatures, the grain boundaries are weakened, deformation is concentrated at the grain boundaries and the re-orientation of equilibrium phases at grain boundaries appears.