Ni coating and Ni-Co alloy coatings were produced by adjusting the composition of the plating solution using a direct current electrodepositing process. The oxidation behaviors of nickel and nickel-cobalt alloys in ai...Ni coating and Ni-Co alloy coatings were produced by adjusting the composition of the plating solution using a direct current electrodepositing process. The oxidation behaviors of nickel and nickel-cobalt alloys in air at 960 ℃ were studied by thermogravimetric （TG） analyzer and then the formed oxide scales were examined by scanning electron microscopy/energy dispersive spectroscopy （SEM/EDS）, X-ray diffractometry （XRD）, and Raman spectroscopy. The scale morphologies, composition, grain size and mechanism of oxidation were discussed in detail. The results show that oxidation rates ofNi, Ni-7%Co （mass fraction） and Ni-15%Co generally follow parabolic relationship, whereas that of Ni-30% Co alloy follows cubic relationship. The higher the Co content of the alloys is, the faster the oxidation rate is. Metal concentration profiles reveal cobalt depletion in the alloy surface beneath oxide scales, and a progressive＇enrichment in cobalt towards the outer surface of the scale.展开更多
Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the...Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.展开更多
An 8 mm-high NiCoCrAlYTa coating was epitaxially built-up on a directionally solidified (DS) Ni-based superalloy blade tip by electro-spark deposition.Epitaxial morphologies of the coating and its microstructural char...An 8 mm-high NiCoCrAlYTa coating was epitaxially built-up on a directionally solidified (DS) Ni-based superalloy blade tip by electro-spark deposition.Epitaxial morphologies of the coating and its microstructural characteristics were investigated by means of SEM,XRD and TEM etc.It is observed that the fine column-like dendrites originated from the γ'-particles or γ'-clusters of the DS substrate and are un-continuously coarsened.The β-phase particles precipitate and grow eutectically with the γ-phase.The orientation of fine column dendrites depends on electro-spark deposition processing parameters and the microstructure can be characterized with superfine γ and β phases.展开更多
基金Project (2005CB623703) supported by the National Basic Research Program of China Project (50474051) supported by the National Natural Science Foundation of China+2 种基金 Project (CX2009B032) supported by Innovation Foundation for Postgraduate of Hunan Province, China Project (ZKJ2008018) supported by the Precious Apparatus Open Share Foundation of Central South University, China Project (2009ybfz02) supported by the Outstanding Doctoral Dissertation Support Foundation of Central South University, China
文摘Ni coating and Ni-Co alloy coatings were produced by adjusting the composition of the plating solution using a direct current electrodepositing process. The oxidation behaviors of nickel and nickel-cobalt alloys in air at 960 ℃ were studied by thermogravimetric （TG） analyzer and then the formed oxide scales were examined by scanning electron microscopy/energy dispersive spectroscopy （SEM/EDS）, X-ray diffractometry （XRD）, and Raman spectroscopy. The scale morphologies, composition, grain size and mechanism of oxidation were discussed in detail. The results show that oxidation rates ofNi, Ni-7%Co （mass fraction） and Ni-15%Co generally follow parabolic relationship, whereas that of Ni-30% Co alloy follows cubic relationship. The higher the Co content of the alloys is, the faster the oxidation rate is. Metal concentration profiles reveal cobalt depletion in the alloy surface beneath oxide scales, and a progressive＇enrichment in cobalt towards the outer surface of the scale.
基金Project(GC13A113)supported by the Technology Research and Development Program of Heilongjiang Provincial Science and Technology DepartmentProject(12511469)supported by Heilongjiang Provincial Science and Technology Department
文摘Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.
基金Projects(50671116,50901081) supported by the National Natural Science Foundation of China
文摘An 8 mm-high NiCoCrAlYTa coating was epitaxially built-up on a directionally solidified (DS) Ni-based superalloy blade tip by electro-spark deposition.Epitaxial morphologies of the coating and its microstructural characteristics were investigated by means of SEM,XRD and TEM etc.It is observed that the fine column-like dendrites originated from the γ'-particles or γ'-clusters of the DS substrate and are un-continuously coarsened.The β-phase particles precipitate and grow eutectically with the γ-phase.The orientation of fine column dendrites depends on electro-spark deposition processing parameters and the microstructure can be characterized with superfine γ and β phases.