The high temperature deformation behaviors of α＋β type titanium alloy TC11 （Ti-6.5Al-3.5Mo-1.5Zr-0.3Si） with coarse lamellar starting microstructure were investigated based on the hot compression tests in the tem...The high temperature deformation behaviors of α＋β type titanium alloy TC11 （Ti-6.5Al-3.5Mo-1.5Zr-0.3Si） with coarse lamellar starting microstructure were investigated based on the hot compression tests in the temperature range of 950-1100 ℃ and the strain rate range of 0.001-10 s-1. The processing maps at different strains were then constructed based on the dynamic materials model, and the hot compression process parameters and deformation mechanism were optimized and analyzed, respectively. The results show that the processing maps exhibit two domains with a high efficiency of power dissipation and a flow instability domain with a less efficiency of power dissipation. The types of domains were characterized by convergence and divergence of the efficiency of power dissipation, respectively. The convergent domain in a＋fl phase field is at the temperature of 950-990 ℃ and the strain rate of 0.001-0.01 s^-1, which correspond to a better hot compression process window of α＋β phase field. The peak of efficiency of power dissipation in α＋β phase field is at 950 ℃ and 0.001 s 1, which correspond to the best hot compression process parameters of α＋β phase field. The convergent domain in β phase field is at the temperature of 1020-1080 ℃ and the strain rate of 0.001-0.1 s^-l, which correspond to a better hot compression process window of β phase field. The peak of efficiency of power dissipation in ℃ phase field occurs at 1050 ℃ over the strain rates from 0.001 s^-1 to 0.01 s^-1, which correspond to the best hot compression process parameters of ,8 phase field. The divergence domain occurs at the strain rates above 0.5 s^-1 and in all the tested temperature range, which correspond to flow instability that is manifested as flow localization and indicated by the flow softening phenomenon in stress-- strain curves. The deformation mechanisms of the optimized hot compression process windows in a＋β and β phase fields are identified to be spheroidizing and dynamic recrystallizing controlled by self-diffusion mechanism, respectively. The microstructure observation of the deformed specimens in different domains matches very well with the optimized results.展开更多
To study the hot deformation behavior of a new powder metallurgy nickel-based superalloy,hot compression tests were conducted in the temperature range of 1020−1110℃ with the strain rates of 0.001−1 s^−1.It is found t...To study the hot deformation behavior of a new powder metallurgy nickel-based superalloy,hot compression tests were conducted in the temperature range of 1020−1110℃ with the strain rates of 0.001−1 s^−1.It is found that the flow stress of the superalloy decreases with increasing temperature and decreasing strain rate.An accurate constitutive equation is established using a hyperbolic-sine type expression.Moreover,processing map of the alloy is constructed to optimize its hot forging parameters.Three domains of dynamic recrystallization stability and instability regions are identified from the processing map at a strain of 0.7,respectively.The adiabatic shear band,intergranular crack and a combination of intergranular crack and wedge crack are demonstrated to be responsible for the instabilities.Comprehensively analyzing the processing map and microstructure,the optimal isothermal forging conditions for the superalloy is determined to be t=1075−1105℃ andε&=10^−3−10−2.8 s^−1.展开更多
To improve the hot workability of hard-deformed superalloy U720Li,the effect of holding time before deformation(5 and 10 min)on hot deformation behavior was investigated by hot compression tests.Results show that the ...To improve the hot workability of hard-deformed superalloy U720Li,the effect of holding time before deformation(5 and 10 min)on hot deformation behavior was investigated by hot compression tests.Results show that the flow stress increases with increase in strain rate,while decreases with increase in deformation temperature and holding time.Based on the obtained Arrhenius-type constitutive models,the calculated peak stresses are in good agreement with experimental values,indicating that this model can accurately predict the hot deformation behavior of U720Li alloy,and the deformation activation energies for the holding time of 5 and 10 min were calculated to be 992.006 and 850.996 kJ·mol^(-1),respectively.Moreover,processing maps of U720Li alloy with these two holding durations were constructed.Through observation of deformation microstructures in each domain of the processing maps,the optimal hot working conditions for the holding time of 5 min are determined to be 1090‒1110℃/1‒10 s^(-1) and 1146‒1180℃/1‒10 s^(-1),and the optimal hot working conditions for the holding time of 10 min are 1080‒1090℃/1‒10 s-1 and 1153‒1160℃/1‒10 s^(-1),indicating that the safe processing window can be obviously enlarged by shortening the holding time reasonably.In the absence of cracking,the dynamic recrystallization(DRX)grain size increases gradually with increasing the deformation temperature and holding time,but it first decreases and then increases with the increase in strain rate.When the deformation temperature is below 1100℃,the DRX mechanism is mainly the particle-induced continuous DRX.As the temperature is raised to above 1130℃,the main DRX mechanism changes to discontinuous DRX.展开更多
IN706 superalloy is particularly sensitive to the parameters of hot working process.The flow stress of the IN706 superalloy was investigated during reduction deformation of 30%,45%,and 60%under the isothermal compress...IN706 superalloy is particularly sensitive to the parameters of hot working process.The flow stress of the IN706 superalloy was investigated during reduction deformation of 30%,45%,and 60%under the isothermal compression conditions of temperature at 1143–1393 K and strain rate at 0.01,0.1,0.5,and 1 s^(−1).The exponent-type Zener-Hollomon equation was used to describe the impact of strain and temperature on the thermal deformation.Meanwhile,the strain effect of various material constants,such asα,n,Q,and lnA,was considered in the constitutive equation considering the strain compensation,and the correlation coefficient R and the average absolute relative error were verified.On the basis of constitutive equation construction,the hot processing map of IN706 superalloy was drawn,and the instability region was obtained based on the Murty criterion.Results show that the reasonable thermal working process parameter window is strain rate of 0.1 s^(−1)and temperature of 1313–1353 K.展开更多
基金Project (51005112) supported by the National Natural Science Foundation of ChinaProject (2010ZF56019) supported by the Aviation Science Foundation of China+1 种基金Project (GJJ11156) supported by the Education Commission of Jiangxi Province, ChinaProject(GF200901008) supported by the Open Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology, China
文摘The high temperature deformation behaviors of α＋β type titanium alloy TC11 （Ti-6.5Al-3.5Mo-1.5Zr-0.3Si） with coarse lamellar starting microstructure were investigated based on the hot compression tests in the temperature range of 950-1100 ℃ and the strain rate range of 0.001-10 s-1. The processing maps at different strains were then constructed based on the dynamic materials model, and the hot compression process parameters and deformation mechanism were optimized and analyzed, respectively. The results show that the processing maps exhibit two domains with a high efficiency of power dissipation and a flow instability domain with a less efficiency of power dissipation. The types of domains were characterized by convergence and divergence of the efficiency of power dissipation, respectively. The convergent domain in a＋fl phase field is at the temperature of 950-990 ℃ and the strain rate of 0.001-0.01 s^-1, which correspond to a better hot compression process window of α＋β phase field. The peak of efficiency of power dissipation in α＋β phase field is at 950 ℃ and 0.001 s 1, which correspond to the best hot compression process parameters of α＋β phase field. The convergent domain in β phase field is at the temperature of 1020-1080 ℃ and the strain rate of 0.001-0.1 s^-l, which correspond to a better hot compression process window of β phase field. The peak of efficiency of power dissipation in ℃ phase field occurs at 1050 ℃ over the strain rates from 0.001 s^-1 to 0.01 s^-1, which correspond to the best hot compression process parameters of ,8 phase field. The divergence domain occurs at the strain rates above 0.5 s^-1 and in all the tested temperature range, which correspond to flow instability that is manifested as flow localization and indicated by the flow softening phenomenon in stress-- strain curves. The deformation mechanisms of the optimized hot compression process windows in a＋β and β phase fields are identified to be spheroidizing and dynamic recrystallizing controlled by self-diffusion mechanism, respectively. The microstructure observation of the deformed specimens in different domains matches very well with the optimized results.
基金Project(2016YFB0700300)supported by the National Key Research and Development Program of ChinaProject(51774335)supported by the National Natural Science Foundation of China。
文摘To study the hot deformation behavior of a new powder metallurgy nickel-based superalloy,hot compression tests were conducted in the temperature range of 1020−1110℃ with the strain rates of 0.001−1 s^−1.It is found that the flow stress of the superalloy decreases with increasing temperature and decreasing strain rate.An accurate constitutive equation is established using a hyperbolic-sine type expression.Moreover,processing map of the alloy is constructed to optimize its hot forging parameters.Three domains of dynamic recrystallization stability and instability regions are identified from the processing map at a strain of 0.7,respectively.The adiabatic shear band,intergranular crack and a combination of intergranular crack and wedge crack are demonstrated to be responsible for the instabilities.Comprehensively analyzing the processing map and microstructure,the optimal isothermal forging conditions for the superalloy is determined to be t=1075−1105℃ andε&=10^−3−10−2.8 s^−1.
基金National Natural Science Foundation of China(52174317,51904146)。
文摘To improve the hot workability of hard-deformed superalloy U720Li,the effect of holding time before deformation(5 and 10 min)on hot deformation behavior was investigated by hot compression tests.Results show that the flow stress increases with increase in strain rate,while decreases with increase in deformation temperature and holding time.Based on the obtained Arrhenius-type constitutive models,the calculated peak stresses are in good agreement with experimental values,indicating that this model can accurately predict the hot deformation behavior of U720Li alloy,and the deformation activation energies for the holding time of 5 and 10 min were calculated to be 992.006 and 850.996 kJ·mol^(-1),respectively.Moreover,processing maps of U720Li alloy with these two holding durations were constructed.Through observation of deformation microstructures in each domain of the processing maps,the optimal hot working conditions for the holding time of 5 min are determined to be 1090‒1110℃/1‒10 s^(-1) and 1146‒1180℃/1‒10 s^(-1),and the optimal hot working conditions for the holding time of 10 min are 1080‒1090℃/1‒10 s-1 and 1153‒1160℃/1‒10 s^(-1),indicating that the safe processing window can be obviously enlarged by shortening the holding time reasonably.In the absence of cracking,the dynamic recrystallization(DRX)grain size increases gradually with increasing the deformation temperature and holding time,but it first decreases and then increases with the increase in strain rate.When the deformation temperature is below 1100℃,the DRX mechanism is mainly the particle-induced continuous DRX.As the temperature is raised to above 1130℃,the main DRX mechanism changes to discontinuous DRX.
文摘IN706 superalloy is particularly sensitive to the parameters of hot working process.The flow stress of the IN706 superalloy was investigated during reduction deformation of 30%,45%,and 60%under the isothermal compression conditions of temperature at 1143–1393 K and strain rate at 0.01,0.1,0.5,and 1 s^(−1).The exponent-type Zener-Hollomon equation was used to describe the impact of strain and temperature on the thermal deformation.Meanwhile,the strain effect of various material constants,such asα,n,Q,and lnA,was considered in the constitutive equation considering the strain compensation,and the correlation coefficient R and the average absolute relative error were verified.On the basis of constitutive equation construction,the hot processing map of IN706 superalloy was drawn,and the instability region was obtained based on the Murty criterion.Results show that the reasonable thermal working process parameter window is strain rate of 0.1 s^(−1)and temperature of 1313–1353 K.