The effect of Ce, Co, and B on the formation of 1：13 phase in La（Fe, Si）13 alloys was investigated by XRD, SEM and EDS. The results show that Co can improve the formation of 1：13 phase in as-cast LaFe11.6-xCoxSi1....The effect of Ce, Co, and B on the formation of 1：13 phase in La（Fe, Si）13 alloys was investigated by XRD, SEM and EDS. The results show that Co can improve the formation of 1：13 phase in as-cast LaFe11.6-xCoxSi1.4 alloys, but in as-cast and annealed LaFe11.6Si1.4-xCox alloys, it will hamper the formation of 1：13 phase and help the formation of a-Fe（Co, Si） solid solution. Ce2Fel7 phases will form when x reaches a certain value in as-cast and annealed La1-xCexFe11.5Si1.5 alloys. B can improve the formation of 1：13 phase accompanied with Fe2B phase in as-cast LaFe11.6-xBxSi1.4 alloys. B improves the formation of a-Fe solid solution in LaFe11.6Si1.4-xBx alloys, and there is almost only a-Fe in as-cast and annealed LaFe11.6Si0.9B0.5 alloy. In all, the introduction of Co, B, and Ce cannot eliminate the a-Fe phases in corresponding alloys prepared by the high-temperature and short-time annealing process.展开更多
基金Project(51176050)supported by the National Natural Science Foundation of ChinaProject(12ZB073)supported by the Research Projects in Sichuan Province Education Office,China
文摘The effect of Ce, Co, and B on the formation of 1：13 phase in La（Fe, Si）13 alloys was investigated by XRD, SEM and EDS. The results show that Co can improve the formation of 1：13 phase in as-cast LaFe11.6-xCoxSi1.4 alloys, but in as-cast and annealed LaFe11.6Si1.4-xCox alloys, it will hamper the formation of 1：13 phase and help the formation of a-Fe（Co, Si） solid solution. Ce2Fel7 phases will form when x reaches a certain value in as-cast and annealed La1-xCexFe11.5Si1.5 alloys. B can improve the formation of 1：13 phase accompanied with Fe2B phase in as-cast LaFe11.6-xBxSi1.4 alloys. B improves the formation of a-Fe solid solution in LaFe11.6Si1.4-xBx alloys, and there is almost only a-Fe in as-cast and annealed LaFe11.6Si0.9B0.5 alloy. In all, the introduction of Co, B, and Ce cannot eliminate the a-Fe phases in corresponding alloys prepared by the high-temperature and short-time annealing process.