X-射线高温衍射台在高聚物相转变中的应用

本文介绍了X-射线高温衍射台的结构，及其应用于高聚物相转变的研究及参数拉制的特点。

Meso-structure and fracture mechanism of mudstone at high temperature

The meso-structure mineral composition and fracture mechanism of uniaxial compressed mudstone samples at high temperature were analyzed by XRD and scanning electron microscopy. The effect of tem- perature on mudstone composition and fracture mechanism were studied from a meso-structural per- spective, and the relationship between meso-structure and macro-mechanical characteristics at high temperature was revealed. The findings demonstrated that the fluctuation in diffraction intensity of kao- linite in the mudstone caused the fluctuation in its mechanical properties. The overall structure under- went a phase change around 600℃, which led to the sudden change in the mechanical properties of mudstone samples. When the temperature reached 600 ℃, the crystalline state worsened and kaolinite disappeared; however, some illite was produced, indicating that the chemical reaction of the structure and sudden drop of bearing capacity of the mudstone. Mudst0ne fracturing at high temperature involves mainly intergranular and transgranular fractures, which are typical in micro-brittle tensile failure. Con- sidering the macro-fracture characteristics of mudstone, the results suggested that macro-fracture under external force corresoonds to the meso-fracture.

Preparation of microsized single-crystalline Co_3O_4 by high-temperature hydrolysis

Microsized single-crystalline Co3O4 has been synthesized by high-temperature hydrolysis of CoCD2H20 at 600℃. The samples were characterized by powder X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The results reveal that the as-prepared powders are microsized single-crystalline CO3O4 with cubic spinel structure. An increase in the high-temperature hydrolysis time results in the evolution of particle shapes from cube to quasi-sphere, and then to octahedron. The effect of NaCl additive on the surface morphologies of Co3O4 particles was experimentally investigated. The results indicate that the NaCl additive acts as an inert disperse phase in the high-temperature hydrolysis, and prevents the aggregation of Co3O4 particles effectively.

Ba4M（CO3）2（BO3）2（M=Ba, Sr）: two borate-carbonates synthesized by open high temperature solution method

Two borate-carbonates Ba4M(CO3)2(BO3)2(M =Ba, Sr) have been successfully synthesized in the open air representing the first examples of borate-carbnate complex.Their structures were determined by single crystal X-ray diffraction and they both crystallize in same space group, Pnma.Their structures feature a Ba/Sr-based three dimensional framework composed of the BaO8 polyhedra(the SrO8 polyhedra), isolated BO3 and CO3 triangles. Detailed structure analysis shows that the intergrowth of [Ba3(BO3)2]/[Ba2Sr(BO3)2] and [BaCO3] layers favors the formation of these two borate-carbonates. In addition, their syntheses, spectroscopic properties and thermal behaviors were investigated.

Implantation induced defects and electrical properties of Sb-implanted ZnO

Defects in Sb implanted Zn O single crystals have been studied by using photoluminescence(PL) spectroscopy,X-ray diffraction(XRD) and Raman scattering.Electrical properties of the samples were analyzed by Hall effect measurement.The results indicate that the annealed Sb-implanted sample is n-type with a free electron concentration of the same amplitude as the calculated implantation concentration.The well-known oxygen vacancy related deep level green PL band is suppressed in the as-implanted sample and recovers to the level close to the as-grown Zn O single crystal after annealing.These phenomena suggest that a large portion of as-implanted Sb atoms occupy oxygen lattice site in an unstable state and move to the interstitial site,forming the complex donor defect upon high temperature annealing,resulting in n-type conduction even if the implantation dose is quite high.