The deterioration of concrete by sulfuric acid attack in sewage environments has become a serious problem for many existing sewage structures. In this study, the properties of concrete using the blast furnace slag hav...The deterioration of concrete by sulfuric acid attack in sewage environments has become a serious problem for many existing sewage structures. In this study, the properties of concrete using the blast furnace slag have been examined. It was shown that by using the blast furnace slag fine aggregate and blast furnace slag fine powder, it is possible to enhance the resistance of mortar and concrete to sulfuric acid. The resistance to sulfuric acid of mortar and concrete can be improved by using a blast-furnace slag fine aggregate in the total amount of fine aggregate. When mortar or concrete reacts to sulfuric acid, dihydrated gypsum film is formed around the particulate of the fine aggregate. This dihydrated gypsum film could retard the penetration of sulfuric acid, thus, improving the resistance to sulfuric acid. Furthermore, it has been proved that the relationship between the erosion depth by sulfuric acid attack and the product of immersion period and concentration of sulfuric acid can be expressed linearly. However, this relationship is dependent on the type of materials of concrete.展开更多
In the present study, compressive strength, pore structure, thermal behavior and microstrncture characteristics of concrete containing ground granulated blast furnace slag and TiO2 nanoparticles as binder were investi...In the present study, compressive strength, pore structure, thermal behavior and microstrncture characteristics of concrete containing ground granulated blast furnace slag and TiO2 nanoparticles as binder were investigated. Portland cement was replaced by different amounts of ground granulated blast furnace slag and the properties of concrete specimens were investigated. Al- though it negatively impacts the properties of concrete at early ages, ground granulated blast furnace slag up to 45 wt% was found to improve the physical and mechanical properties of concrete at later ages. TiO2 nanoparticles with the average particle size of 15 nm were partially added to concrete with the optimum content of ground granulated blast furnace slag and physical and mechanical properties of the specimens were measured. TiO2 nanoparticle as a partial replacement of cement up to 3 wt% could accelerate C-S-H gel formation as a result of increased crystalline Ca（OH）2 amount at the early age of hydration and hence increase compressive strength of concrete. The increased TiO2 nanoparticles＇ content of more than 3 wt% may cause reduced compressive strength because of the decreased crystalline Ca（OH）2 content required for C-S-H gel formation and unsuitable dispersed nanoparticles in the concrete matrix. TiO2 nanoparticles could improve the pore structure of concrete and shift the distributed pores to harmless and less-harm pores.展开更多
文摘The deterioration of concrete by sulfuric acid attack in sewage environments has become a serious problem for many existing sewage structures. In this study, the properties of concrete using the blast furnace slag have been examined. It was shown that by using the blast furnace slag fine aggregate and blast furnace slag fine powder, it is possible to enhance the resistance of mortar and concrete to sulfuric acid. The resistance to sulfuric acid of mortar and concrete can be improved by using a blast-furnace slag fine aggregate in the total amount of fine aggregate. When mortar or concrete reacts to sulfuric acid, dihydrated gypsum film is formed around the particulate of the fine aggregate. This dihydrated gypsum film could retard the penetration of sulfuric acid, thus, improving the resistance to sulfuric acid. Furthermore, it has been proved that the relationship between the erosion depth by sulfuric acid attack and the product of immersion period and concentration of sulfuric acid can be expressed linearly. However, this relationship is dependent on the type of materials of concrete.
文摘In the present study, compressive strength, pore structure, thermal behavior and microstrncture characteristics of concrete containing ground granulated blast furnace slag and TiO2 nanoparticles as binder were investigated. Portland cement was replaced by different amounts of ground granulated blast furnace slag and the properties of concrete specimens were investigated. Al- though it negatively impacts the properties of concrete at early ages, ground granulated blast furnace slag up to 45 wt% was found to improve the physical and mechanical properties of concrete at later ages. TiO2 nanoparticles with the average particle size of 15 nm were partially added to concrete with the optimum content of ground granulated blast furnace slag and physical and mechanical properties of the specimens were measured. TiO2 nanoparticle as a partial replacement of cement up to 3 wt% could accelerate C-S-H gel formation as a result of increased crystalline Ca（OH）2 amount at the early age of hydration and hence increase compressive strength of concrete. The increased TiO2 nanoparticles＇ content of more than 3 wt% may cause reduced compressive strength because of the decreased crystalline Ca（OH）2 content required for C-S-H gel formation and unsuitable dispersed nanoparticles in the concrete matrix. TiO2 nanoparticles could improve the pore structure of concrete and shift the distributed pores to harmless and less-harm pores.
