The influence of rare earth metals and heat treatment on the microstructure and performance of M42 steel has been investigated by means of an optical microscope OM scanning electron microscope SEM energy dispersive sp...The influence of rare earth metals and heat treatment on the microstructure and performance of M42 steel has been investigated by means of an optical microscope OM scanning electron microscope SEM energy dispersive spectroscopy EDS transmission electron microscope TEM electron back-scatter diffraction EBSD and X-ray diffraction XRD . The results show that M2 C is the prevailing type of eutectic carbides in M42 steel. After modification with rare earth metals M2 C eutectic carbides change from the ordered lamellar structure into a circular structure.Despite different morphologies the two carbides present the same characteristics of microstructure and growth orientation.Compared with lamellar carbides M2 C carbides with the circular structure are much easier to decompose and spheroidize after heating which remarkably refines the carbide dimensions.The refined carbides improve the supersaturation of alloying elements in martensite and increase the hardness of M42 steel by 1.5 HRC.展开更多
In order to study the effect of the withdrawing rate on carbide morphology,MC-type carbide in single crystal superalloy AM3 was systematically investigated with sample growth rates from 3.5 μm/s to 500 μm/s.The carb...In order to study the effect of the withdrawing rate on carbide morphology,MC-type carbide in single crystal superalloy AM3 was systematically investigated with sample growth rates from 3.5 μm/s to 500 μm/s.The carbide morphologies were investigated by scanning electron microscopy(SEM),and the electron probe microanalysis(EPMA) was used to characterize the carbide composition.The results indicate that the solidification rate is the important factor governing MC carbide growth morphology,size and distribution,composition and growth mechanism.With the increase of withdrawing rate,nodular,rod-like,Chinese script types of carbide morphology are observed.For the low withdrawing rate,with the increase of withdrawing rate,the carbide size becomes larger.For the case of dendritic interface,the carbide size becomes smaller with refinement of dendrites as withdrawing rate increases.The volume fraction of carbides increases with the withdrawing rate increasing.展开更多
基金The National Natural Science Foundation of China(No.51301038,51201031,51371050)the Industry-AcademiaResearch Cooperative Innovation Fund of Jiangsu Province(No.BY2014127-03)+1 种基金the Natural Science Foundation of Jiangsu Province(No.BK20141306)the Scientific and Technological Innovation Fund of Danyang(No.SY201305)
文摘The influence of rare earth metals and heat treatment on the microstructure and performance of M42 steel has been investigated by means of an optical microscope OM scanning electron microscope SEM energy dispersive spectroscopy EDS transmission electron microscope TEM electron back-scatter diffraction EBSD and X-ray diffraction XRD . The results show that M2 C is the prevailing type of eutectic carbides in M42 steel. After modification with rare earth metals M2 C eutectic carbides change from the ordered lamellar structure into a circular structure.Despite different morphologies the two carbides present the same characteristics of microstructure and growth orientation.Compared with lamellar carbides M2 C carbides with the circular structure are much easier to decompose and spheroidize after heating which remarkably refines the carbide dimensions.The refined carbides improve the supersaturation of alloying elements in martensite and increase the hardness of M42 steel by 1.5 HRC.
基金Projects(50771081, 50931004) supported by the National Natural Science Foundation of ChinaProject(2010CB631202) supported by the National Basic Research Program of China
文摘In order to study the effect of the withdrawing rate on carbide morphology,MC-type carbide in single crystal superalloy AM3 was systematically investigated with sample growth rates from 3.5 μm/s to 500 μm/s.The carbide morphologies were investigated by scanning electron microscopy(SEM),and the electron probe microanalysis(EPMA) was used to characterize the carbide composition.The results indicate that the solidification rate is the important factor governing MC carbide growth morphology,size and distribution,composition and growth mechanism.With the increase of withdrawing rate,nodular,rod-like,Chinese script types of carbide morphology are observed.For the low withdrawing rate,with the increase of withdrawing rate,the carbide size becomes larger.For the case of dendritic interface,the carbide size becomes smaller with refinement of dendrites as withdrawing rate increases.The volume fraction of carbides increases with the withdrawing rate increasing.