Black TiO2（B）/anatase bicrystalline TiO2-x nanofibers were synthesized from a porous titanate derivative by calcination in H2, and were characterized using field-emission scanning electron microscopy, Raman spectros...Black TiO2（B）/anatase bicrystalline TiO2-x nanofibers were synthesized from a porous titanate derivative by calcination in H2, and were characterized using field-emission scanning electron microscopy, Raman spectroscopy, N2 adsorption-desorption analysis, X-ray photoelectron spectroscopy, thermogravimetric analysis, ultraviolet-visible diffuse reflection spectroscopy and photoluminescence measurements. Characterization results showed that no Ti3＋ was present on the surface of black bicrystalline TiO2-x and oxygen vacancies were distributed in the bulk of both TiO2（B） and anatase phases. The O/Ti atom stoichiometric ratio of black bicrystalline TiO2-x was estimated to be 1.97 from the difference of mass loss between black bicrystalline TiO2-x and white bicrystalline TiO2 without oxygen vacancies. The photocatalytic activity of black bicrystalline TiO2-x was 4.2 times higher than that of white bicrystalline TiO2 and 10.5 times higher than that of anatase TiOz. The high photocatalytic activity of black bicrystalline TiO2-x was attributed to its effective separation of electrons and holes, which may be related to the effects of both bicrystalline structure and oxygen vacancies. Black bicrystalline TiO2-x also exhibited good photocatalytic activity after recycling ten times. The black bicrystalline TiO2-x nanofibers show potential for use in environmental and energy applications.展开更多
基金supported by the National Natural Science Foundation of China(21406118,91434109,91334202)the Highly Educated Talent Foundation of Nanjing Forestry University(GXL2014036)+2 种基金the Doctor Program of Jiangsu ProvinceDistinguished Experts Program of Science and Technology Vice-manager(Enterprise Innovation Job)the Priority Academic Program Development of Jiangsu Higher Education Institutions~~
文摘Black TiO2（B）/anatase bicrystalline TiO2-x nanofibers were synthesized from a porous titanate derivative by calcination in H2, and were characterized using field-emission scanning electron microscopy, Raman spectroscopy, N2 adsorption-desorption analysis, X-ray photoelectron spectroscopy, thermogravimetric analysis, ultraviolet-visible diffuse reflection spectroscopy and photoluminescence measurements. Characterization results showed that no Ti3＋ was present on the surface of black bicrystalline TiO2-x and oxygen vacancies were distributed in the bulk of both TiO2（B） and anatase phases. The O/Ti atom stoichiometric ratio of black bicrystalline TiO2-x was estimated to be 1.97 from the difference of mass loss between black bicrystalline TiO2-x and white bicrystalline TiO2 without oxygen vacancies. The photocatalytic activity of black bicrystalline TiO2-x was 4.2 times higher than that of white bicrystalline TiO2 and 10.5 times higher than that of anatase TiOz. The high photocatalytic activity of black bicrystalline TiO2-x was attributed to its effective separation of electrons and holes, which may be related to the effects of both bicrystalline structure and oxygen vacancies. Black bicrystalline TiO2-x also exhibited good photocatalytic activity after recycling ten times. The black bicrystalline TiO2-x nanofibers show potential for use in environmental and energy applications.
