Poly （butylene succinatc-co-terephthalate） （PBST） copolycsters were prepared by polycondensation. The crystallization behavior of the as-prepared copolyesters was investigated by depolarized light intensity （DLI...Poly （butylene succinatc-co-terephthalate） （PBST） copolycsters were prepared by polycondensation. The crystallization behavior of the as-prepared copolyesters was investigated by depolarized light intensity （DLI） at high undercoolings. According to Avrami equation, the exponent n, independent of the crystallization temperature, is at a range of 2. 5 to 3. 4, which probably corresponds to the heterogeneous mucleation and a 3-dimensional spherulitic growth. The maximum crystallization rate, very useful to polymer processing, was found at about 90℃ based on the half-crystallization time t1/2 analysis.展开更多
Poly （ butylene succinate ） （ PBS ）, poly （ butylene terephthalate） （PBT） and poly （butylene succirmte-coterephthalate） （PBST）s were synthesized from dimethyl succinate and/or dimethyl terephthalate reacti...Poly （ butylene succinate ） （ PBS ）, poly （ butylene terephthalate） （PBT） and poly （butylene succirmte-coterephthalate） （PBST）s were synthesized from dimethyl succinate and/or dimethyl terephthalate reacting with 1,4- butanediol through a process of transesterification/ polycondmsation in the presence of a high effective catalyst and characterized by means of GPC and DSC. The investigation was mainly focused on the influence of content of terephthalate units on the molecular weight and thermal properties of resulting polymers. It is revealed that the melting temperature and crystallinity of synthesized polymers decrease first with the increase of terephthalate units, then shift to rise gradually by DSC measurements. The results of Flory equation suggest sequence structure of PBSTs is random.展开更多
The poly （butylene sucinate-co-terphthalate）（PBST） copolyesters with differnet monocs of the PBST has been investigated by differential scanning calorimeter（DSC）.According to Avrami equation,the exponent n for ...The poly （butylene sucinate-co-terphthalate）（PBST） copolyesters with differnet monocs of the PBST has been investigated by differential scanning calorimeter（DSC）.According to Avrami equation,the exponent n for all the copolyesters is independent of the crystallization temperature and content of BT units,and is close to 3,which probably corresponds to the heterogeneous nucleation and a 3-dimensional spherulitic growth.Polarized light micrographs confimed the result.展开更多
文摘Poly （butylene succinatc-co-terephthalate） （PBST） copolycsters were prepared by polycondensation. The crystallization behavior of the as-prepared copolyesters was investigated by depolarized light intensity （DLI） at high undercoolings. According to Avrami equation, the exponent n, independent of the crystallization temperature, is at a range of 2. 5 to 3. 4, which probably corresponds to the heterogeneous mucleation and a 3-dimensional spherulitic growth. The maximum crystallization rate, very useful to polymer processing, was found at about 90℃ based on the half-crystallization time t1/2 analysis.
基金Supported by Shanghai Municipal Science and Technology Development Fund (No.045211052)
文摘Poly （ butylene succinate ） （ PBS ）, poly （ butylene terephthalate） （PBT） and poly （butylene succirmte-coterephthalate） （PBST）s were synthesized from dimethyl succinate and/or dimethyl terephthalate reacting with 1,4- butanediol through a process of transesterification/ polycondmsation in the presence of a high effective catalyst and characterized by means of GPC and DSC. The investigation was mainly focused on the influence of content of terephthalate units on the molecular weight and thermal properties of resulting polymers. It is revealed that the melting temperature and crystallinity of synthesized polymers decrease first with the increase of terephthalate units, then shift to rise gradually by DSC measurements. The results of Flory equation suggest sequence structure of PBSTs is random.
文摘The poly （butylene sucinate-co-terphthalate）（PBST） copolyesters with differnet monocs of the PBST has been investigated by differential scanning calorimeter（DSC）.According to Avrami equation,the exponent n for all the copolyesters is independent of the crystallization temperature and content of BT units,and is close to 3,which probably corresponds to the heterogeneous nucleation and a 3-dimensional spherulitic growth.Polarized light micrographs confimed the result.