A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning elec...A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning electron microscopy, and elemental analysis show that the Si/SiO_(x)/C material is a secondary particle with a porous micronanostructure, and the presence of nanometer silicon does not affect the carbothermal reduction and carbon coating.Electrochemical test results indicate that the specific capacity and first coulombic efficiency of SiO_(x)/C composite with nanometer silicon can be increased to 1 946.05 mAh/g and 76.49%,respectively.The reversible specific capacity of Si/SiO_(x)/C material blended with graphite is 749.69 mAh/g after 100 cycles at a current density of 0.1 C,and the capacity retention rate is up to 89.03%.Therefore, the composite has excellent electrochemical cycle stability.展开更多
PTFE dispersion composites filled with nanometer ZnO were successfully prepared by controlling stirring speed and using ultrasonic mixture with no damage to PTFE dispersion. Properties of PTFE composites, such as wear...PTFE dispersion composites filled with nanometer ZnO were successfully prepared by controlling stirring speed and using ultrasonic mixture with no damage to PTFE dispersion. Properties of PTFE composites, such as wear rate, friction coefficient and thermal conductivity coefficient were tested respectively. Also, the grain size of nanometer filler in composites were observed by different methods, such as small angle X-ray scattering (SAXS), transmission electron microscopy (TEM) and dynamic light scattering particle size distribution analyzer (DLSPSDA). Results show that nanometer ZnO fillers can further improve properties of PTFE-based composite, and its properties varies with the content of the fillers.展开更多
Photocatalytic degradations of p-nitrochlorbenzene (p-NCB) with distilled water wereinvestigated with ZnO crystals (catalyst) of 70nm in diameter under UV irradiation.The suitable experimental conditions are determine...Photocatalytic degradations of p-nitrochlorbenzene (p-NCB) with distilled water wereinvestigated with ZnO crystals (catalyst) of 70nm in diameter under UV irradiation.The suitable experimental conditions are determined as: ZnO 0.25g, pH 7, p-NCBconcentration 30mg/L. These variables in terms of the degradation rate have beendiscussed, which was defined as the rate of the initial degradation to the final degrada-tion of p-NCB. When all of the experimental degradation rate values are plotted as afunction of irradiation time, all of the points appeared on a single line for wide range ofp-NCB degradations. On the basis of these results, it has been concluded that at lowerZnO catalyst amount, much of the light is transmitted through the slurry in the con-tainer beaker, while at higher catalyst amount, all the incident photons are observedby the slurry. Degradation rates of p-NCB were found to decrease with increasingsolution pH. It has been concluded that the maximum degradation rate values of p-NCB under principally the same experimental conditions mentioned above are 97.4%,98.8% and 95.5% at 100min respectively. The results suggest that the photocatalyticdegradation is initiated by an oxidation of the p-NCB through ZnO surface-adsorbedhydroxyl radicals. Absorption spectra are recorded using spectrophotometer before andafter UV-irradiation in the wavelength range 200-400nm at room temperature. Itis found that the variation of irradiation time over the range 20-100min resulted inchange in the form of the spectrum linear absorption and a higher maximum valuewill be obtained at longer irradiation time.展开更多
A series of photocatalysts of un-doped, single-doped and co-doped nanometer titanium diox- ide （TiO2） have been successfully prepared by template method using Fe（NO3）3.9H2O, La（NO3）3.6H2O, and tetrabutyl titanat...A series of photocatalysts of un-doped, single-doped and co-doped nanometer titanium diox- ide （TiO2） have been successfully prepared by template method using Fe（NO3）3.9H2O, La（NO3）3.6H2O, and tetrabutyl titanate as precursors and glucan as template. Scanning electron microscopy, X-ray diffraction, and N2 adsorption-desorption measurement were employed to characterize the morphology, crystal structure and surface structure of the samples. The photo-absorbance of the obtained catalysts was measured by UV-Vis absorption spectroscopy, and the photocatalytic activities of the prepared samples under UV and visible light were estimated by measuring the degradation rate of methyl orange in an aqueous solution. The characterizations indicated that the prepared photocatalysts consisted of anatase phase and possessed high surface area of ca. 163-176 m2/g. It was shown that the Fe and La co-doped nano-TiO2 could be activated by visible light and could thus be used as an effective catalyst in photo-oxidation reactions. The synergistic effect of Fe and La co-doping played an important role in improving the photocatalytic activity. In addition, the possibility of cyclic usage of co-doped nano-TiO2 was also confirmed, the photocatalytic activity of codoped nano-TiO2 remained above 89.6% of the fresh sample after being used four times.展开更多
Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structu...Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.展开更多
In the electric field and layer-to-layer interaction energy, the law of split-level of high-level Stark effect of spherical nanometer system is explored as well as the frequency of spectrum, intensity and size effect ...In the electric field and layer-to-layer interaction energy, the law of split-level of high-level Stark effect of spherical nanometer system is explored as well as the frequency of spectrum, intensity and size effect of coefficient of spontaneous radiation. Taking three layers CdS/HgS spherical nanometer system as an example, the influence of the electric field and layer-to- layer interaction energy is explored on Stark effect and spectrum. The results show that in the Stark effect system, the energy level is split based on 1, 3, ..., （2n-1）, when it is in the electric field only, similar to the hydrogen atoms; and in the electric field and layer-to-layer interaction, it is split based on 1, 4, ~ -., n2; with the quantum transition, the frequency of the spectrum decreases with the increasing size of the system; apart from a few spectral lines, the intensity of most spectral lines will decreased as the size increases; while the coefficient of spontaneous radiation will increase with the increasing size; the electric field will cause the changes of spectrum frequency; its spectrum frequency shift is proportional to the square of the electric field intensity; apart from a few spectral lines, the frequency shift of spectral lines that is caused by the electric field and layer-to-layer interaction will decrease as the size increases; the interaction will make the level of electronic energy level lower slightly （the order of magnitude is between 10-7-10-9 eV）, the slightly increased spectrum intensity and the slightly increased value of coefficient of spontaneous radiation, but it will not influence the frequency of spectrum, intensity, and the trend that coefficient of spontaneous radiation changes with the size; when the size is smaller, the layer-to-layer interaction effect will be significant.展开更多
The relation of mass, stiffness and rate of damping is obtained by using the mechanical analysis of the obstructive vibration system of two dimensions for the design of the obstructive vibration system of more freedom...The relation of mass, stiffness and rate of damping is obtained by using the mechanical analysis of the obstructive vibration system of two dimensions for the design of the obstructive vibration system of more freedom and the micro vibration test bed. The result of stimulational experiment indicates that the isolation of vibration of this system is satisfactory. The design method of vibration can be used as the reference to ultra precision machine tool, super micro orientation machanism and so on.展开更多
The nanometer cobalt blue pigments were prepared by microemulsion method. Using dynamic light scattering(DLS) test method, the influences of water content on the size of liquid drop of microemulsion and the liquid dro...The nanometer cobalt blue pigments were prepared by microemulsion method. Using dynamic light scattering(DLS) test method, the influences of water content on the size of liquid drop of microemulsion and the liquid drop of microemulsion on the final diameter of nanometer particle were studied in the course of preparation. Accordingly, the method to control the diameter of nanometer particle by changing water content was established. The nanometer cobalt blue particles were confirmed by XRD and TEM. Color parameters of pigments were determined. The quantum size effect of the pigments was discussed.展开更多
Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structu...Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.展开更多
文摘A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning electron microscopy, and elemental analysis show that the Si/SiO_(x)/C material is a secondary particle with a porous micronanostructure, and the presence of nanometer silicon does not affect the carbothermal reduction and carbon coating.Electrochemical test results indicate that the specific capacity and first coulombic efficiency of SiO_(x)/C composite with nanometer silicon can be increased to 1 946.05 mAh/g and 76.49%,respectively.The reversible specific capacity of Si/SiO_(x)/C material blended with graphite is 749.69 mAh/g after 100 cycles at a current density of 0.1 C,and the capacity retention rate is up to 89.03%.Therefore, the composite has excellent electrochemical cycle stability.
文摘PTFE dispersion composites filled with nanometer ZnO were successfully prepared by controlling stirring speed and using ultrasonic mixture with no damage to PTFE dispersion. Properties of PTFE composites, such as wear rate, friction coefficient and thermal conductivity coefficient were tested respectively. Also, the grain size of nanometer filler in composites were observed by different methods, such as small angle X-ray scattering (SAXS), transmission electron microscopy (TEM) and dynamic light scattering particle size distribution analyzer (DLSPSDA). Results show that nanometer ZnO fillers can further improve properties of PTFE-based composite, and its properties varies with the content of the fillers.
文摘Photocatalytic degradations of p-nitrochlorbenzene (p-NCB) with distilled water wereinvestigated with ZnO crystals (catalyst) of 70nm in diameter under UV irradiation.The suitable experimental conditions are determined as: ZnO 0.25g, pH 7, p-NCBconcentration 30mg/L. These variables in terms of the degradation rate have beendiscussed, which was defined as the rate of the initial degradation to the final degrada-tion of p-NCB. When all of the experimental degradation rate values are plotted as afunction of irradiation time, all of the points appeared on a single line for wide range ofp-NCB degradations. On the basis of these results, it has been concluded that at lowerZnO catalyst amount, much of the light is transmitted through the slurry in the con-tainer beaker, while at higher catalyst amount, all the incident photons are observedby the slurry. Degradation rates of p-NCB were found to decrease with increasingsolution pH. It has been concluded that the maximum degradation rate values of p-NCB under principally the same experimental conditions mentioned above are 97.4%,98.8% and 95.5% at 100min respectively. The results suggest that the photocatalyticdegradation is initiated by an oxidation of the p-NCB through ZnO surface-adsorbedhydroxyl radicals. Absorption spectra are recorded using spectrophotometer before andafter UV-irradiation in the wavelength range 200-400nm at room temperature. Itis found that the variation of irradiation time over the range 20-100min resulted inchange in the form of the spectrum linear absorption and a higher maximum valuewill be obtained at longer irradiation time.
文摘A series of photocatalysts of un-doped, single-doped and co-doped nanometer titanium diox- ide （TiO2） have been successfully prepared by template method using Fe（NO3）3.9H2O, La（NO3）3.6H2O, and tetrabutyl titanate as precursors and glucan as template. Scanning electron microscopy, X-ray diffraction, and N2 adsorption-desorption measurement were employed to characterize the morphology, crystal structure and surface structure of the samples. The photo-absorbance of the obtained catalysts was measured by UV-Vis absorption spectroscopy, and the photocatalytic activities of the prepared samples under UV and visible light were estimated by measuring the degradation rate of methyl orange in an aqueous solution. The characterizations indicated that the prepared photocatalysts consisted of anatase phase and possessed high surface area of ca. 163-176 m2/g. It was shown that the Fe and La co-doped nano-TiO2 could be activated by visible light and could thus be used as an effective catalyst in photo-oxidation reactions. The synergistic effect of Fe and La co-doping played an important role in improving the photocatalytic activity. In addition, the possibility of cyclic usage of co-doped nano-TiO2 was also confirmed, the photocatalytic activity of codoped nano-TiO2 remained above 89.6% of the fresh sample after being used four times.
文摘Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.
文摘In the electric field and layer-to-layer interaction energy, the law of split-level of high-level Stark effect of spherical nanometer system is explored as well as the frequency of spectrum, intensity and size effect of coefficient of spontaneous radiation. Taking three layers CdS/HgS spherical nanometer system as an example, the influence of the electric field and layer-to- layer interaction energy is explored on Stark effect and spectrum. The results show that in the Stark effect system, the energy level is split based on 1, 3, ..., （2n-1）, when it is in the electric field only, similar to the hydrogen atoms; and in the electric field and layer-to-layer interaction, it is split based on 1, 4, ~ -., n2; with the quantum transition, the frequency of the spectrum decreases with the increasing size of the system; apart from a few spectral lines, the intensity of most spectral lines will decreased as the size increases; while the coefficient of spontaneous radiation will increase with the increasing size; the electric field will cause the changes of spectrum frequency; its spectrum frequency shift is proportional to the square of the electric field intensity; apart from a few spectral lines, the frequency shift of spectral lines that is caused by the electric field and layer-to-layer interaction will decrease as the size increases; the interaction will make the level of electronic energy level lower slightly （the order of magnitude is between 10-7-10-9 eV）, the slightly increased spectrum intensity and the slightly increased value of coefficient of spontaneous radiation, but it will not influence the frequency of spectrum, intensity, and the trend that coefficient of spontaneous radiation changes with the size; when the size is smaller, the layer-to-layer interaction effect will be significant.
文摘The relation of mass, stiffness and rate of damping is obtained by using the mechanical analysis of the obstructive vibration system of two dimensions for the design of the obstructive vibration system of more freedom and the micro vibration test bed. The result of stimulational experiment indicates that the isolation of vibration of this system is satisfactory. The design method of vibration can be used as the reference to ultra precision machine tool, super micro orientation machanism and so on.
文摘The nanometer cobalt blue pigments were prepared by microemulsion method. Using dynamic light scattering(DLS) test method, the influences of water content on the size of liquid drop of microemulsion and the liquid drop of microemulsion on the final diameter of nanometer particle were studied in the course of preparation. Accordingly, the method to control the diameter of nanometer particle by changing water content was established. The nanometer cobalt blue particles were confirmed by XRD and TEM. Color parameters of pigments were determined. The quantum size effect of the pigments was discussed.
文摘Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.