In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,Si...In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.展开更多
文摘In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.