Cobalt-phthalocyanine/iron nanocomposite particles have been obtained using method of composite in situ, with the mixture of carbonyl iron and solution of cobalt ( Ⅱ ) - phthalocyanine (Co-Pc) ultrasonic dispersing i...Cobalt-phthalocyanine/iron nanocomposite particles have been obtained using method of composite in situ, with the mixture of carbonyl iron and solution of cobalt ( Ⅱ ) - phthalocyanine (Co-Pc) ultrasonic dispersing in N,N-dimethyl-formamide (DMF). Structure characterization of their inner and surface have relation with method of carbonyl iron joined in the mixture, contents of carbonyl iron and Co-Pc in the mixture of Co-Pc ultrasonic dispersing in DMF. With a method of composite in situ controlling reasonable experiment condition, it can be obtained that cobalt-phthalocyanine/iron nanocomposite particles has completely been covered with Co-Pc, they had structure of Chinese gooseberry in inner and mere made up of almost regular spherical shape and the average diameter is 1. 4 μm.展开更多
Magnetorheological suspension based on 20 (v/V) % CoPc-iron composite particles dispersed in sili-cone oil have been obtained, which exhibited dynamic shear stress up to 2000Pa upon application of external magnetic fi...Magnetorheological suspension based on 20 (v/V) % CoPc-iron composite particles dispersed in sili-cone oil have been obtained, which exhibited dynamic shear stress up to 2000Pa upon application of external magnetic field at 1300 Oe. The response is faster than 0. 15 -with superior reversibility of changes in viscosity induced by external magnetic field at above 12. 5℃. Further, it was found that the MR fluid is in possession of long-term stability a-gainst sedimentation.展开更多
基金Funded by Chinese National Natural Science Foundation (No. 29904005), Key Foundation (No. 50038010) and Open Foundation from State Key Lab.of Advanced Technology for Materials Synthesis and Processing.
文摘Cobalt-phthalocyanine/iron nanocomposite particles have been obtained using method of composite in situ, with the mixture of carbonyl iron and solution of cobalt ( Ⅱ ) - phthalocyanine (Co-Pc) ultrasonic dispersing in N,N-dimethyl-formamide (DMF). Structure characterization of their inner and surface have relation with method of carbonyl iron joined in the mixture, contents of carbonyl iron and Co-Pc in the mixture of Co-Pc ultrasonic dispersing in DMF. With a method of composite in situ controlling reasonable experiment condition, it can be obtained that cobalt-phthalocyanine/iron nanocomposite particles has completely been covered with Co-Pc, they had structure of Chinese gooseberry in inner and mere made up of almost regular spherical shape and the average diameter is 1. 4 μm.
基金Chinese National Natural Science Foundation (No. 29674021) Hubei Natural Science Foundation(NO. 97J086).
文摘Magnetorheological suspension based on 20 (v/V) % CoPc-iron composite particles dispersed in sili-cone oil have been obtained, which exhibited dynamic shear stress up to 2000Pa upon application of external magnetic field at 1300 Oe. The response is faster than 0. 15 -with superior reversibility of changes in viscosity induced by external magnetic field at above 12. 5℃. Further, it was found that the MR fluid is in possession of long-term stability a-gainst sedimentation.