A novel 1-3-2 piezoelectric composite has been developed,which consists of piezoelectric ceramic plate and 1-3 piezoelectric composite.The composite was fabricated by dicing PZT ceramic along mutual perpendicular two ...A novel 1-3-2 piezoelectric composite has been developed,which consists of piezoelectric ceramic plate and 1-3 piezoelectric composite.The composite was fabricated by dicing PZT ceramic along mutual perpendicular two directions and then filling epoxy into grooves.The piezoelectric and electromechanical properties of the novel composite were determined. The results show a coefficient d_ (33) of 405pC/N,a vibration displacement of 113.5pm,an acoustic impendence of 13.3 Mraly, a bandwidth of 12kHz and a thickness electromechanical coupling coefficient of 0.56.展开更多
The cathode material La1-xSrxCuO3-δ(x=0.15, 0.2, 0.3, 0.4) was synthesized by a sol-gel method. X-ray diffraction reveals that a single phase of perovskite is formed. The investigation of the electrical properties su...The cathode material La1-xSrxCuO3-δ(x=0.15, 0.2, 0.3, 0.4) was synthesized by a sol-gel method. X-ray diffraction reveals that a single phase of perovskite is formed. The investigation of the electrical properties suggests that La0.7Sr0.3CuO3-δ has the highest electrical conductivity. La0.7Sr0.3CuO3-δ powder was mixed with different amount SDC (Sm0.15Ce0.85O1.925) powder (5wt.%-30wt.%) as composite cathodes. Electrochemical properties of the composite cathodes were researched further. Investigation suggests that the addition of appropriate amount SDC to La0.7Sr0.3CuO3-δ can improve the electrochemical properties and obtain better cathodic performance. Using La0.7Sr0.3CuO3-δ-SDC composite materials as a cathode based on SDC electrolyte, higher current density and power density at intermediate temperatures can be obtained.展开更多
A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon...A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon - carbon double bonds systems and reusability. Furthermore, XPS and IR spectra shouted that active component in the composite catalysts is atomic Pd(0). An addition of a small amount of Fe2O3 has a promotive action upon hydrogenation activity of the catalysts, which indicated that there are some strong interactions (electron transfer) between Pd(0) and Fe(Ⅲ) species. Based on these results, a possible catalytic hydrogenation mechanism was also suggested.展开更多
The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with r...The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.展开更多
Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- ...Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.展开更多
La0.8Sr0.2Co1-yFeyO3-δ (y=0.2, 0.4, 0.6, 0.8) powders were synthesized by ethylenediamine tetraacetic acid (EDTA) complexing sol-gel process. The powders were characterized via X-ray diffraction (XRD) and scanning el...La0.8Sr0.2Co1-yFeyO3-δ (y=0.2, 0.4, 0.6, 0.8) powders were synthesized by ethylenediamine tetraacetic acid (EDTA) complexing sol-gel process. The powders were characterized via X-ray diffraction (XRD) and scanning electron microscope and energy dispersive X-ray spectroscopy (SEM-EDS). The results showed that single-phased perovskite-type oxide powders with small particle size were obtained by the process, and the compositions of the productions agreed with the designed molar ratio. The electronic conductivity and ionic conductivity of La0.8Sr0.2Co1-yFeyO3-δ were investigated by DC four-terminal method and AC impedance spectroscopy, respectively. The electronic conductivity of La0.8Sr0.2Co1-yFeyO3-δ is approximately 2~4 orders of magnitude higher than the ionic conductivity. It was confirmed that the conductivities of the materials were strongly influenced by the composition anions, temperature and sample preparing process.展开更多
Layered F-doped cathode materials 0.3 Li_2 MnO_3-0.7 LiMn_(1/3)Ni_(1/3)CO_(1/3))O_(2-x)F_x(x = 0, 0.01, 0.02, 0.03, 0.04,0.05) microspheres made up of nanosized primary grains were prepared through co-precipitation me...Layered F-doped cathode materials 0.3 Li_2 MnO_3-0.7 LiMn_(1/3)Ni_(1/3)CO_(1/3))O_(2-x)F_x(x = 0, 0.01, 0.02, 0.03, 0.04,0.05) microspheres made up of nanosized primary grains were prepared through co-precipitation method. The sample of x = 0.02 demonstrates a large discharge capacity of226 mAh g^(-1) over 100 cycles at 0.1 C and excellent rate performance with discharge capacity of 96 mAh g-1 at 5.0 C and room temperature. Particularly, this material shows much enhanced electrochemical performances even at high temperature of 55 ℃. It delivers a quite high discharge capacity of 233.7 mAh·g^(-1) at 1.0 C with capacity retention as high as 97.9% after 100 cycles. The results demonstrate that the fluorine incorporation stabilizes the cathode structure and maintains stable interfacial resistances.展开更多
Piezoelectric properties and related figures of merit are studied in novel 1-3-type composites based on ferroelectric domain-engineered lead-free single crystal with the relatively large longitudinal piezoelectric coe...Piezoelectric properties and related figures of merit are studied in novel 1-3-type composites based on ferroelectric domain-engineered lead-free single crystal with the relatively large longitudinal piezoelectric coefficient d_(33).Relationships between the piezoelectric properties and the set of figures of merit are analyzed for the 1-3 and 1-3-0 composites that contain the same single-crystal and polymer components.For a composite characterized by 1-3-0 connectivity,an influence of a porous piezo-passive matrix on the figures of merit and their volume-fraction behavior is considered additionally.A large anisotropy of figures of merit is observed in the 1-3-0 composite with specific porous matrices.A diagram is put forward to show volume-fraction regions of the large anisotropy of figures of merit of the studied 1-3-0 composite.Due to large figures of merit and their considerable anisotropy,the studied lead-free composites can be applied in piezoelectric energy-harvesting systems,sensors,transducers,and so on.展开更多
The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The in...The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900~1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.展开更多
基金supported by the Beijing Natural Science Foundation of China(No.KZ200410772016)Academic Innovative Team Program of University in Beijing.
文摘A novel 1-3-2 piezoelectric composite has been developed,which consists of piezoelectric ceramic plate and 1-3 piezoelectric composite.The composite was fabricated by dicing PZT ceramic along mutual perpendicular two directions and then filling epoxy into grooves.The piezoelectric and electromechanical properties of the novel composite were determined. The results show a coefficient d_ (33) of 405pC/N,a vibration displacement of 113.5pm,an acoustic impendence of 13.3 Mraly, a bandwidth of 12kHz and a thickness electromechanical coupling coefficient of 0.56.
文摘The cathode material La1-xSrxCuO3-δ(x=0.15, 0.2, 0.3, 0.4) was synthesized by a sol-gel method. X-ray diffraction reveals that a single phase of perovskite is formed. The investigation of the electrical properties suggests that La0.7Sr0.3CuO3-δ has the highest electrical conductivity. La0.7Sr0.3CuO3-δ powder was mixed with different amount SDC (Sm0.15Ce0.85O1.925) powder (5wt.%-30wt.%) as composite cathodes. Electrochemical properties of the composite cathodes were researched further. Investigation suggests that the addition of appropriate amount SDC to La0.7Sr0.3CuO3-δ can improve the electrochemical properties and obtain better cathodic performance. Using La0.7Sr0.3CuO3-δ-SDC composite materials as a cathode based on SDC electrolyte, higher current density and power density at intermediate temperatures can be obtained.
文摘A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon - carbon double bonds systems and reusability. Furthermore, XPS and IR spectra shouted that active component in the composite catalysts is atomic Pd(0). An addition of a small amount of Fe2O3 has a promotive action upon hydrogenation activity of the catalysts, which indicated that there are some strong interactions (electron transfer) between Pd(0) and Fe(Ⅲ) species. Based on these results, a possible catalytic hydrogenation mechanism was also suggested.
基金the National Natural Science Foundation of China (No. 51602126)the National Key Research and Development Plan of China (No. 2016YFB0303505)+1 种基金China and University of Jinan Postdoctoral Science Foundation (No. 2017M622118 and XBH1716)the 111 Project of International Corporation on Advanced Cement-based Materials (D17001).
文摘The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.
文摘Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.
基金the National Natural Science Foundation of China (50204007)the Talent Foundation of Yunnan Province (2005PY01-33)Programfor New Century Excellent Talents in University (NCET-07-0387)
文摘La0.8Sr0.2Co1-yFeyO3-δ (y=0.2, 0.4, 0.6, 0.8) powders were synthesized by ethylenediamine tetraacetic acid (EDTA) complexing sol-gel process. The powders were characterized via X-ray diffraction (XRD) and scanning electron microscope and energy dispersive X-ray spectroscopy (SEM-EDS). The results showed that single-phased perovskite-type oxide powders with small particle size were obtained by the process, and the compositions of the productions agreed with the designed molar ratio. The electronic conductivity and ionic conductivity of La0.8Sr0.2Co1-yFeyO3-δ were investigated by DC four-terminal method and AC impedance spectroscopy, respectively. The electronic conductivity of La0.8Sr0.2Co1-yFeyO3-δ is approximately 2~4 orders of magnitude higher than the ionic conductivity. It was confirmed that the conductivities of the materials were strongly influenced by the composition anions, temperature and sample preparing process.
基金financially supported by the National Natural Science Foundation of China (No. 51372136)the NSFC-Guangdong United Fund (No. U1401246)
文摘Layered F-doped cathode materials 0.3 Li_2 MnO_3-0.7 LiMn_(1/3)Ni_(1/3)CO_(1/3))O_(2-x)F_x(x = 0, 0.01, 0.02, 0.03, 0.04,0.05) microspheres made up of nanosized primary grains were prepared through co-precipitation method. The sample of x = 0.02 demonstrates a large discharge capacity of226 mAh g^(-1) over 100 cycles at 0.1 C and excellent rate performance with discharge capacity of 96 mAh g-1 at 5.0 C and room temperature. Particularly, this material shows much enhanced electrochemical performances even at high temperature of 55 ℃. It delivers a quite high discharge capacity of 233.7 mAh·g^(-1) at 1.0 C with capacity retention as high as 97.9% after 100 cycles. The results demonstrate that the fluorine incorporation stabilizes the cathode structure and maintains stable interfacial resistances.
基金The authors are grateful to Prof.Dr.I.A.Parinov and Prof.Dr.A.E.Panich(Southern Federal University,Russia),and Prof.Dr.C.R.Bowen(University of Bath,UK)for their interest in the field of modern piezo-active materials and applications.Research was financially supported by Southern Federal University,grant No.VnGr-07/2020-04-IM(Ministry of Science and Higher Education of the Russian Federation).
文摘Piezoelectric properties and related figures of merit are studied in novel 1-3-type composites based on ferroelectric domain-engineered lead-free single crystal with the relatively large longitudinal piezoelectric coefficient d_(33).Relationships between the piezoelectric properties and the set of figures of merit are analyzed for the 1-3 and 1-3-0 composites that contain the same single-crystal and polymer components.For a composite characterized by 1-3-0 connectivity,an influence of a porous piezo-passive matrix on the figures of merit and their volume-fraction behavior is considered additionally.A large anisotropy of figures of merit is observed in the 1-3-0 composite with specific porous matrices.A diagram is put forward to show volume-fraction regions of the large anisotropy of figures of merit of the studied 1-3-0 composite.Due to large figures of merit and their considerable anisotropy,the studied lead-free composites can be applied in piezoelectric energy-harvesting systems,sensors,transducers,and so on.
文摘The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900~1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.