By using newly developed CuNi5~25Ti16~28 B rapldly solidifled brazing filler the joining of Si3 N4/1.25Cr-0.5Mo steel has been carried out with interlayer method. If employing the interlayer structure of steel (0.2 mm...By using newly developed CuNi5~25Ti16~28 B rapldly solidifled brazing filler the joining of Si3 N4/1.25Cr-0.5Mo steel has been carried out with interlayer method. If employing the interlayer structure of steel (0.2 mm)/W (2.0 mm)/Ni(0.2 mm), the joint strength can be increased greatly compared with employing that of Ni/W/Ni, and the three point bend strength of the Joint shows the value of 261 MPa. The metallurgical behaviour at the interface between Si3N4 and the interlayer has been studied. It is found that Fe participated in the interfacial reactions between Si3N4 and the brazing filler at the Si3N4/steel (0.2 mm) interface and the compound Fe5Si3 was produced. However, since the reactions of Fe with the active Ti are weaker than those of Ni with Ti, the normal inter facial reactions were still assured at the interface of Si3N4/steel (0.2 mm) instead of Si3N4/Ni (0.2 mm), resulting in the improvement of the joint strength. The mechanism of the formation of Fe5Si3 is also discussed. Finally, some ideas to further ameliorate and simplify the interlayer structure are put forward.展开更多
针对1.25Cr-0.5Mo材料的交直流两用电焊条进行设计开发,介绍了依据各类标准及客户实际使用情况下的B HLER FOX E8016-B2电焊条的药皮配方、化学成分和力学性能指标的设计思路。对焊条进行试验验证后,详细介绍了熔敷金属的化学成分和交...针对1.25Cr-0.5Mo材料的交直流两用电焊条进行设计开发,介绍了依据各类标准及客户实际使用情况下的B HLER FOX E8016-B2电焊条的药皮配方、化学成分和力学性能指标的设计思路。对焊条进行试验验证后,详细介绍了熔敷金属的化学成分和交直流焊接时不同焊后热处理条件下的熔敷金属的各项力学性能数据及其金相组织结构,同时也给出了焊接接头的性能试验数据以及焊条扩散氢等试验数据。该焊条适用焊接电流范围广,在不同焊接电流下均有良好的焊接工艺性,且均能保持优良的力学性能。展开更多
文摘By using newly developed CuNi5~25Ti16~28 B rapldly solidifled brazing filler the joining of Si3 N4/1.25Cr-0.5Mo steel has been carried out with interlayer method. If employing the interlayer structure of steel (0.2 mm)/W (2.0 mm)/Ni(0.2 mm), the joint strength can be increased greatly compared with employing that of Ni/W/Ni, and the three point bend strength of the Joint shows the value of 261 MPa. The metallurgical behaviour at the interface between Si3N4 and the interlayer has been studied. It is found that Fe participated in the interfacial reactions between Si3N4 and the brazing filler at the Si3N4/steel (0.2 mm) interface and the compound Fe5Si3 was produced. However, since the reactions of Fe with the active Ti are weaker than those of Ni with Ti, the normal inter facial reactions were still assured at the interface of Si3N4/steel (0.2 mm) instead of Si3N4/Ni (0.2 mm), resulting in the improvement of the joint strength. The mechanism of the formation of Fe5Si3 is also discussed. Finally, some ideas to further ameliorate and simplify the interlayer structure are put forward.
文摘针对1.25Cr-0.5Mo材料的交直流两用电焊条进行设计开发,介绍了依据各类标准及客户实际使用情况下的B HLER FOX E8016-B2电焊条的药皮配方、化学成分和力学性能指标的设计思路。对焊条进行试验验证后,详细介绍了熔敷金属的化学成分和交直流焊接时不同焊后热处理条件下的熔敷金属的各项力学性能数据及其金相组织结构,同时也给出了焊接接头的性能试验数据以及焊条扩散氢等试验数据。该焊条适用焊接电流范围广,在不同焊接电流下均有良好的焊接工艺性,且均能保持优良的力学性能。