热处理制度对S11306-Q345R复合钢板组织和性能的影响

研究了热处理制度对S11306-Q345R复合钢板组织和性能的影响。试验结果表明：S11306-Q345R复合钢板在910℃热处理后覆层S11306晶界有大量碳化物析出，塑性降低；在620—690℃范围内进行热处理时，S11306-Q345R不锈钢复合钢板可得到较好的综合性能。

Development of S11306+SA516Gr70 roll-bonded clad steel plate for pressure vessels

To meet the demand of the pressure vessel industry, Baosteel has developed an S11306 ＋ SA516Gr70 roll-bonded clad steel plate. Comprehensive inspections of the composition, microstructure, and properties are performed to systematically evaluate the steel plate in normalized state and normalized ＋ stress relieved state. The results show the cladding interface of the Sl1306 ＋ SA516Gr70 roll-bonded clad steel plate has high shear strength, and the base metal has good mechanical properties. The performance is fully consistent with the technical requirements of the roll-bonded clad steel plate for pressure vessels.

S11306/Q245R不锈钢复合钢板焊接工艺

为满足安庆石化新建200万t/a重油加氢装置中分馏塔的焊接任务,采用SMAW的焊接方法,对该材料S11306/Q245R进行了焊接工艺研究,在分析焊接性和反复试验的基础上,拟定了合理的焊接材料、焊接方法、焊接工艺参数以及焊接过程中的操作技巧和操作要点。结果表明,拟定的焊接工艺方案是可行的,焊缝性能可以得到保证,同时也可作为制定类似材料焊接工艺的参考。

S11306/Q245R不锈钢复合钢板焊接工艺

采用SMAW的焊接方法,对S11306/Q245R进行了焊接工艺研究,在分析焊接性和反复试验的基础上,拟定了合理的焊接材料、焊接方法、焊接工艺参数以及焊接过程中的操作技巧和操作要点。结果表明,拟定的焊接工艺方案是可行的,焊缝性能可以得到保证,同时也可作为制定类似材料焊接工艺的参考。

常压塔不锈钢复合板的焊接

依据焊接工艺评定报告及现场施工实际,对Q345R+S11306复合板焊接工作进行了分析,确定了最佳的施工工艺。