In this study,the pitting corrosion behavior of 13Cr4Ni martensitic stainless steel(BASE)and that modified with rare earth(REM)in 0.1 mol/L Na Cl solution were characterized.Techniques such as automatic secondary elec...In this study,the pitting corrosion behavior of 13Cr4Ni martensitic stainless steel(BASE)and that modified with rare earth(REM)in 0.1 mol/L Na Cl solution were characterized.Techniques such as automatic secondary electron microscope(ASPEX PSEM detector),scanning electron microscope(SEM),transmission electron microscope(TEM),scanning Kelvin probe force microscope(SKP),potentiodynamic and potentiostatic polarizations were employed.The results obtained indicate that BASE steel contains Al_(2)O_(3)/Mn S,Al_(2)O_(3) and Mn S inclusions,while REM steels contain(La,Ce,Cr,Fe)-O and(La,Ce,Cr,Fe)-O-S inclusions.Compared with BASE steel,REM steel is more susceptible to induce the metastable pitting nucleation and repassivation,whereas it restrains the transition from metastable pitting to stable pitting.Adding 0.021%rare earth element to BASE steel can reduce the number and area of inclusions,while that of 0.058%can increase the number and enlarged the size of inclusions,which is also the reason that pitting corrosion resistance of 58 REM steel is slightly lower than that of 21 REM steel.In the process of pitting corrosion induced by Al_(2)O_(3)/Mn S inclusions,Mn S is preferentially anodic dissolved,and also the matrix contacted with Al_(2)O_(3) is subsequently anodic dissolved.For REM steels,anodic dissolution preferentially occurs at the boundary between inclusions and matrix,while(La,Ce,Cr,Fe)-O inclusions chemically dissolve in local acidic environment or are separated from steel matrix.The chemically dissolved substance(La^(3+) and Ce^(3+))of(La,Ce,Cr,Fe)-O inclusions are concentrated in pitting pits,which inhibits its continuous growth.展开更多
基金supported by the National Natural Science Foundation of China(No.51801219)the Youth Innovation Promotion Association of the Chinese Academy of Sciences(No.2019193)+1 种基金the Scientific Research Project of China Three Gorges Corporation(No.JD-YJ-05006)the National Key Research and Development Program of China(No.2017YFB0702302)。
文摘In this study,the pitting corrosion behavior of 13Cr4Ni martensitic stainless steel(BASE)and that modified with rare earth(REM)in 0.1 mol/L Na Cl solution were characterized.Techniques such as automatic secondary electron microscope(ASPEX PSEM detector),scanning electron microscope(SEM),transmission electron microscope(TEM),scanning Kelvin probe force microscope(SKP),potentiodynamic and potentiostatic polarizations were employed.The results obtained indicate that BASE steel contains Al_(2)O_(3)/Mn S,Al_(2)O_(3) and Mn S inclusions,while REM steels contain(La,Ce,Cr,Fe)-O and(La,Ce,Cr,Fe)-O-S inclusions.Compared with BASE steel,REM steel is more susceptible to induce the metastable pitting nucleation and repassivation,whereas it restrains the transition from metastable pitting to stable pitting.Adding 0.021%rare earth element to BASE steel can reduce the number and area of inclusions,while that of 0.058%can increase the number and enlarged the size of inclusions,which is also the reason that pitting corrosion resistance of 58 REM steel is slightly lower than that of 21 REM steel.In the process of pitting corrosion induced by Al_(2)O_(3)/Mn S inclusions,Mn S is preferentially anodic dissolved,and also the matrix contacted with Al_(2)O_(3) is subsequently anodic dissolved.For REM steels,anodic dissolution preferentially occurs at the boundary between inclusions and matrix,while(La,Ce,Cr,Fe)-O inclusions chemically dissolve in local acidic environment or are separated from steel matrix.The chemically dissolved substance(La^(3+) and Ce^(3+))of(La,Ce,Cr,Fe)-O inclusions are concentrated in pitting pits,which inhibits its continuous growth.
