Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy...Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.展开更多
This work investigated the gradient microstructure evolution and tensile property of LPBF fabricated 15-5 precipitation hardening stainless steel in post-process direct ageing(DA)and solution treating&ageing(STA)....This work investigated the gradient microstructure evolution and tensile property of LPBF fabricated 15-5 precipitation hardening stainless steel in post-process direct ageing(DA)and solution treating&ageing(STA).The varied microstructures for austenite and small-sized oxide inclusions at different sample heights in the as-built(AB)condition was generally preserved after DA treatment.However,austenite was almost disappeared,and oxide particle grew significantly after the STA treatment.As a result,the tensile property differences in sample top and bottom for AB and DA conditions did not occur in the STA samples.For the influence of post-process heat treatment,the STA condition had the highest yield strength due to the highest volume fraction of nano-sized Cu precipitates.However,the DA specimen had the highest ultimate tensile strength and elongation owing to the considerable amount of austenite phase and associated transformation induced plasticity effect.展开更多
The effect of different heat treatments on the reversed austenite in Cr15 super martensitic stainless steel was investigated. The experimental results indicate that the microstructure of the steel is composed of tempe...The effect of different heat treatments on the reversed austenite in Cr15 super martensitic stainless steel was investigated. The experimental results indicate that the microstructure of the steel is composed of tempered martensite and diffused reversed austenite after quenching at 1 050 ℃ and tempering from 550 to 750 ℃. The volume fraction and size of reversed austenite increase with increasing tempering temperature and both of them reach the maximum value at 700 ℃. The volume fraction and size of reversed austenite decrease when the temperature is above 700 ℃. The transmission electron microscope （TEM） results indicate that the orientation relationship between tempered martensite and reversed austenite belongs to Kurdjmov-Sach （K-S） relationship.展开更多
Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results show...Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results showed that the 15-5 PH stainless steel consists of NbC precipitates and lath matensite with a high dislocation density after solution treatment. With increasing aging temperature and aging time, the martensitic laths were resolved gradually. Meanwhile, the nanometric-sized Cu precipitates gradually coarsened and lost their coherency with＇the martensite matrix, which exhibited an elliptical shape finally. Fine Cu precipitates can lead to significant dispersion hardening effect, while the coarsened Cu precipitates have no contribution to strengthening. The reversed austenite was observed in the speci- mens aged at 550 ℃ and above; moreover, the amount of reversed austenite increased as aging temperature in- creased. The precipitation hardening behavior of 15-5 PH stainless steel may depend on the balance between the softening caused by the formation of reversed austenite and the hardening caused by the precipitation of copper.展开更多
文摘Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.
基金Foundation item:Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (51075189) supported by the National Natural Science Foundation of China
基金Sheng Cao thanks the support from the National Natural Science Foundation of China(No.52204391)the Special Fund Project for Science and Technology Innovation Strategy of Guangdong Province(Nos.STKJ202209021 and STKJ2023040)+1 种基金the Characteristic Innovation Project(Natural Science)for Regular University in Guangdong Province(No.2022KTSCX038)the Shantou University Research Foundation for Talents(No.NTF21013).
文摘This work investigated the gradient microstructure evolution and tensile property of LPBF fabricated 15-5 precipitation hardening stainless steel in post-process direct ageing(DA)and solution treating&ageing(STA).The varied microstructures for austenite and small-sized oxide inclusions at different sample heights in the as-built(AB)condition was generally preserved after DA treatment.However,austenite was almost disappeared,and oxide particle grew significantly after the STA treatment.As a result,the tensile property differences in sample top and bottom for AB and DA conditions did not occur in the STA samples.For the influence of post-process heat treatment,the STA condition had the highest yield strength due to the highest volume fraction of nano-sized Cu precipitates.However,the DA specimen had the highest ultimate tensile strength and elongation owing to the considerable amount of austenite phase and associated transformation induced plasticity effect.
文摘The effect of different heat treatments on the reversed austenite in Cr15 super martensitic stainless steel was investigated. The experimental results indicate that the microstructure of the steel is composed of tempered martensite and diffused reversed austenite after quenching at 1 050 ℃ and tempering from 550 to 750 ℃. The volume fraction and size of reversed austenite increase with increasing tempering temperature and both of them reach the maximum value at 700 ℃. The volume fraction and size of reversed austenite decrease when the temperature is above 700 ℃. The transmission electron microscope （TEM） results indicate that the orientation relationship between tempered martensite and reversed austenite belongs to Kurdjmov-Sach （K-S） relationship.
基金Item Sponsored by National High Technology Research and Development Program of China(2012AA03A507)Key Laboratory Foundation of Metal Material Microstructure Control of Jiangxi Province of China(JW201223001)Foundation of Jiangxi Educational Committee of China(GJJ14534)
文摘Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results showed that the 15-5 PH stainless steel consists of NbC precipitates and lath matensite with a high dislocation density after solution treatment. With increasing aging temperature and aging time, the martensitic laths were resolved gradually. Meanwhile, the nanometric-sized Cu precipitates gradually coarsened and lost their coherency with＇the martensite matrix, which exhibited an elliptical shape finally. Fine Cu precipitates can lead to significant dispersion hardening effect, while the coarsened Cu precipitates have no contribution to strengthening. The reversed austenite was observed in the speci- mens aged at 550 ℃ and above; moreover, the amount of reversed austenite increased as aging temperature in- creased. The precipitation hardening behavior of 15-5 PH stainless steel may depend on the balance between the softening caused by the formation of reversed austenite and the hardening caused by the precipitation of copper.