Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results show...Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results showed that the 15-5 PH stainless steel consists of NbC precipitates and lath matensite with a high dislocation density after solution treatment. With increasing aging temperature and aging time, the martensitic laths were resolved gradually. Meanwhile, the nanometric-sized Cu precipitates gradually coarsened and lost their coherency with＇the martensite matrix, which exhibited an elliptical shape finally. Fine Cu precipitates can lead to significant dispersion hardening effect, while the coarsened Cu precipitates have no contribution to strengthening. The reversed austenite was observed in the speci- mens aged at 550 ℃ and above; moreover, the amount of reversed austenite increased as aging temperature in- creased. The precipitation hardening behavior of 15-5 PH stainless steel may depend on the balance between the softening caused by the formation of reversed austenite and the hardening caused by the precipitation of copper.展开更多
Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding pro...Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding process were numerically simulated and experimentally measured. The results show that the rotated parabola body heat source is fit for the simulation of the electron beam welding. The temperature distribution is asymmetric along the weld center and the temperature in the titanium alloy plate is higher than that in the 304 STS plate. The thermal stress also appears to be in asymmetric distribution. The residual tensile stress mainly exists in the weld at the 304 STS side. The copper filler metal decreases the peak temperature and temperature grade in the joint as well as the residual stress. The longitudinal and lateral residual tensile strengths reduce by 66 MPa and 31 MPa, respectively. From the temperature and residual stress, it is concluded that copper is a good filler metal candidate for the electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel.展开更多
Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy...Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.展开更多
基金Item Sponsored by National High Technology Research and Development Program of China(2012AA03A507)Key Laboratory Foundation of Metal Material Microstructure Control of Jiangxi Province of China(JW201223001)Foundation of Jiangxi Educational Committee of China(GJJ14534)
文摘Microstructure transformation and aging hardening behavior of 15-5 PH stainless steel were studied by optical microscopy （OM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The results showed that the 15-5 PH stainless steel consists of NbC precipitates and lath matensite with a high dislocation density after solution treatment. With increasing aging temperature and aging time, the martensitic laths were resolved gradually. Meanwhile, the nanometric-sized Cu precipitates gradually coarsened and lost their coherency with＇the martensite matrix, which exhibited an elliptical shape finally. Fine Cu precipitates can lead to significant dispersion hardening effect, while the coarsened Cu precipitates have no contribution to strengthening. The reversed austenite was observed in the speci- mens aged at 550 ℃ and above; moreover, the amount of reversed austenite increased as aging temperature in- creased. The precipitation hardening behavior of 15-5 PH stainless steel may depend on the balance between the softening caused by the formation of reversed austenite and the hardening caused by the precipitation of copper.
基金Foundation item:Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (51075189) supported by the National Natural Science Foundation of China
文摘Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding process were numerically simulated and experimentally measured. The results show that the rotated parabola body heat source is fit for the simulation of the electron beam welding. The temperature distribution is asymmetric along the weld center and the temperature in the titanium alloy plate is higher than that in the 304 STS plate. The thermal stress also appears to be in asymmetric distribution. The residual tensile stress mainly exists in the weld at the 304 STS side. The copper filler metal decreases the peak temperature and temperature grade in the joint as well as the residual stress. The longitudinal and lateral residual tensile strengths reduce by 66 MPa and 31 MPa, respectively. From the temperature and residual stress, it is concluded that copper is a good filler metal candidate for the electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel.
文摘Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.