The hot deformation behavior of ultra purified 17% Cr ferritic stainless steel stabilized with Nb and Ti was investigated using axisymmetric hot compression tests on a thermomechanical simulator.The deformation was ca...The hot deformation behavior of ultra purified 17% Cr ferritic stainless steel stabilized with Nb and Ti was investigated using axisymmetric hot compression tests on a thermomechanical simulator.The deformation was carried out at the temperatures ranging from 700 to 1 100℃ and strain rates from 1to 10s-1.The microstructure was investigated using electron backscattering diffraction.The effects of temperature and strain rate on deformation behavior were represented by Zener-Hollomon parameter in an exponent type equation.The effect of strain was incorporated in the constitutive equation by establishing polynomial relationship between the material constants and strain.A sixth order polynomial was suitable to represent the effect of strain.The modified constitutive equation considering the effect of strain was developed and could predict the flow stress throughout the deformation conditions except at800℃in 1s-1 and at 700℃in 5and 10s-1.Losing the reliability of the modified constitutive equation was possibly ascribed to the increase in average Taylor factor at 800℃in 1s-1 and the increase in temperature at 700℃in 5and10s-1 during hot deformation.The optimum window for improving product quality of the ferritic stainless steels was identified as hot rolling at a low finisher entry temperature of 700℃,which can be achieved in practical production.展开更多
The oxidation resistance behavior of SmCo(2:17)-type high-temperature magnets modified with Ni-Cr two-layer coating was studied. The study depicts the mass gain kinetics and magnetic properties of uncoated and NiCr-mo...The oxidation resistance behavior of SmCo(2:17)-type high-temperature magnets modified with Ni-Cr two-layer coating was studied. The study depicts the mass gain kinetics and magnetic properties of uncoated and NiCr-modified magnets oxidized at high temperature(500 ℃) in air for 200 h. The oxidation test results illustrate that the mass gain of uncoated magnet is6.95 mg·cm^(-2) which is more than that(0.08 mg·cm^(-2)) of coated magnet after 200 h. For the magnetic properties concerned, there is a great loss for uncoated magnet, while for coated magnet, magnetic properties do not change much. The study of uncoated magnet through X-ray diffraction(XRD) and electron probe microanalysis(EPMA) shows that the invasion of oxygen at high temperature leads to the loss of magnetic properties by changing the microstructure of magnet.展开更多
基金Sponsored by National Science and Technology Pillar Program during the Twelfth Five-year Plan Period of China(2012BAE04B02)National Natural Science Foundation of China(51271050)
文摘The hot deformation behavior of ultra purified 17% Cr ferritic stainless steel stabilized with Nb and Ti was investigated using axisymmetric hot compression tests on a thermomechanical simulator.The deformation was carried out at the temperatures ranging from 700 to 1 100℃ and strain rates from 1to 10s-1.The microstructure was investigated using electron backscattering diffraction.The effects of temperature and strain rate on deformation behavior were represented by Zener-Hollomon parameter in an exponent type equation.The effect of strain was incorporated in the constitutive equation by establishing polynomial relationship between the material constants and strain.A sixth order polynomial was suitable to represent the effect of strain.The modified constitutive equation considering the effect of strain was developed and could predict the flow stress throughout the deformation conditions except at800℃in 1s-1 and at 700℃in 5and 10s-1.Losing the reliability of the modified constitutive equation was possibly ascribed to the increase in average Taylor factor at 800℃in 1s-1 and the increase in temperature at 700℃in 5and10s-1 during hot deformation.The optimum window for improving product quality of the ferritic stainless steels was identified as hot rolling at a low finisher entry temperature of 700℃,which can be achieved in practical production.
基金financially supported by the National Science Foundation of China(No.51471016)the Natural Science Foundation of Beijing(No.2151002)
文摘The oxidation resistance behavior of SmCo(2:17)-type high-temperature magnets modified with Ni-Cr two-layer coating was studied. The study depicts the mass gain kinetics and magnetic properties of uncoated and NiCr-modified magnets oxidized at high temperature(500 ℃) in air for 200 h. The oxidation test results illustrate that the mass gain of uncoated magnet is6.95 mg·cm^(-2) which is more than that(0.08 mg·cm^(-2)) of coated magnet after 200 h. For the magnetic properties concerned, there is a great loss for uncoated magnet, while for coated magnet, magnetic properties do not change much. The study of uncoated magnet through X-ray diffraction(XRD) and electron probe microanalysis(EPMA) shows that the invasion of oxygen at high temperature leads to the loss of magnetic properties by changing the microstructure of magnet.