The ring-opening polymerization of 1,4-dioxan-2-one （PDO） was carried out by lanthanum tris（2,6-di-tert-butyl-4- methylphenolate） （La（OAr）3） as novel single component initiaLor. The influences of polymerizatio...The ring-opening polymerization of 1,4-dioxan-2-one （PDO） was carried out by lanthanum tris（2,6-di-tert-butyl-4- methylphenolate） （La（OAr）3） as novel single component initiaLor. The influences of polymerization reaction temperature and the molar ratio of monomer to initiator on the monomer conversion and molecular weight of poly（1,4-dioxan-2-one） （PPDO） were explored. PPDO with high viscosity average molecular weight of 1.95×10^5 can be prepared at 40℃ when [PDO]/ [La（OAr）3] molar ratio was 800. Mechanism investigation shows that the polymerization proceeds through a ＂coordination- insertion＂ mechanism with selective rupture of acyl-oxygen be,nd of PDO.展开更多
The polymerization of n-hexyl isocyanate(HNCO) was carried out in the presence of a novel single initiator, rare earth tris(2,6-di-tert-butyl-4-methylphenolate)[Ln(OAr)_3]. The influences of reaction conditions such a...The polymerization of n-hexyl isocyanate(HNCO) was carried out in the presence of a novel single initiator, rare earth tris(2,6-di-tert-butyl-4-methylphenolate)[Ln(OAr)_3]. The influences of reaction conditions such as the monomer concentration, the polymerization temperature and time, and the types of solvents on the polymerization of HNCO were studied. Polymerizations of phenyl, i-propyl, p-tolyl, n-butyl and n-octyl isocyanates with La(OAr)_3 were also examined.展开更多
基金This work was financially supported by the financial support of National Natural Science Foundation of China (No. 20434020)
文摘The ring-opening polymerization of 1,4-dioxan-2-one （PDO） was carried out by lanthanum tris（2,6-di-tert-butyl-4- methylphenolate） （La（OAr）3） as novel single component initiaLor. The influences of polymerization reaction temperature and the molar ratio of monomer to initiator on the monomer conversion and molecular weight of poly（1,4-dioxan-2-one） （PPDO） were explored. PPDO with high viscosity average molecular weight of 1.95×10^5 can be prepared at 40℃ when [PDO]/ [La（OAr）3] molar ratio was 800. Mechanism investigation shows that the polymerization proceeds through a ＂coordination- insertion＂ mechanism with selective rupture of acyl-oxygen be,nd of PDO.
文摘The polymerization of n-hexyl isocyanate(HNCO) was carried out in the presence of a novel single initiator, rare earth tris(2,6-di-tert-butyl-4-methylphenolate)[Ln(OAr)_3]. The influences of reaction conditions such as the monomer concentration, the polymerization temperature and time, and the types of solvents on the polymerization of HNCO were studied. Polymerizations of phenyl, i-propyl, p-tolyl, n-butyl and n-octyl isocyanates with La(OAr)_3 were also examined.