The reaction of Zn（ClO4）2·6H2O with 3,3＇-bis（2-benzimidazolyl）-2,2＇-dipyridine （L） gave a mononuclear zinc（Ⅱ） complex： [ZnL2]（CIO4）2·2DMF·4H2O, which was structurally characterized by EA, ...The reaction of Zn（ClO4）2·6H2O with 3,3＇-bis（2-benzimidazolyl）-2,2＇-dipyridine （L） gave a mononuclear zinc（Ⅱ） complex： [ZnL2]（CIO4）2·2DMF·4H2O, which was structurally characterized by EA, IR, UV, ^1H NMR, fluorescence spectrum and single-crystal X-ray diffraction. The crystal （C54H54Cl2N14O14Zn, Mr = 1259.38） belongs to the monoclinic system, space group C2/c with a = 20.874（2）, b = 14.9953（16）, c = 20.462（3）A,β= 101.553（2）°, V= 6274.8（13） A, Z= 4, Dc= 1.333 g/cm^3, F （000） = 2608,/a（MoKcr） = 0.548 mm 1, R = 0.0682 and wR = 0.1931 for 4984 observed reflections with I 〉 2σ（I）. The Zn（Ⅱ） is four-coordinated in a slightly distorted tetrahedral geometry through four N atoms from four benzimidazole units of two ligands. In the crystal lattice, the [ZnL2]2^＋ cations are linked to each other by extensive intermolecular hydrogen bonds between nitrogen atoms of benzimidazole rings, water and DMF molecules.展开更多
通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量...通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量大于0.81%时,随Al含量增加,钢板的晶粒尺寸减小,同时铁损增加。Al含量对硅钢板磁感的影响没有明显的规律。2.2%Si无取向硅钢的合适Al含量为0.48%～0.81%。展开更多
基金Supported by the National Natural Science Foundation of China (No. 20471054) the Henan Innovation Project for University Prominent Research Talents (No. 2005 KYCX021)
文摘The reaction of Zn（ClO4）2·6H2O with 3,3＇-bis（2-benzimidazolyl）-2,2＇-dipyridine （L） gave a mononuclear zinc（Ⅱ） complex： [ZnL2]（CIO4）2·2DMF·4H2O, which was structurally characterized by EA, IR, UV, ^1H NMR, fluorescence spectrum and single-crystal X-ray diffraction. The crystal （C54H54Cl2N14O14Zn, Mr = 1259.38） belongs to the monoclinic system, space group C2/c with a = 20.874（2）, b = 14.9953（16）, c = 20.462（3）A,β= 101.553（2）°, V= 6274.8（13） A, Z= 4, Dc= 1.333 g/cm^3, F （000） = 2608,/a（MoKcr） = 0.548 mm 1, R = 0.0682 and wR = 0.1931 for 4984 observed reflections with I 〉 2σ（I）. The Zn（Ⅱ） is four-coordinated in a slightly distorted tetrahedral geometry through four N atoms from four benzimidazole units of two ligands. In the crystal lattice, the [ZnL2]2^＋ cations are linked to each other by extensive intermolecular hydrogen bonds between nitrogen atoms of benzimidazole rings, water and DMF molecules.
文摘通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量大于0.81%时,随Al含量增加,钢板的晶粒尺寸减小,同时铁损增加。Al含量对硅钢板磁感的影响没有明显的规律。2.2%Si无取向硅钢的合适Al含量为0.48%～0.81%。