Effects of Hydrogen on Behaviour of Low Cycle Fatigue of 2.25Cr-1Mo Steel

The effects of hydrogen atoms on behaviour of low cycle fatigue of 2.25Cr-1Mo steel have been investigated in present work. The results indicate that the cyclic softening rate and low cycle fatigue life are respectively increased and reduced remarkably by hydrogen atoms. In addition, hydrogen atoms make the original stress amplitude of low cycle fatigue increase, which is because of the drag effect of hydrogen atoms on the moving dislocations. Analyses using electron microscopy show that hydrogen atoms accelerate crack initiation of low cycle fatigue from inclusion and transfer the source of low cycle fatigue crack from the surface of specimen to the inclusion, which results in the marked decrease of low cycle fatigue life. The increase of cyclic softening rate for hydrogen charged specimen is due to hydrogen atoms accelerating the initiating and growing of microvoids from the secondary phase particles in the steel. The reducing of the drag effect of hydrogen atoms on moving dislocations is also helpful to the increase of the cyclic softening rate.

KINETICS OF TEMPER EMBRITTLEMENT IN 2.25Cr-1Mo STEEL USED FOR HOT-WALL HYDROFINING REACTORS

Based on the theory of grain boundary segregation, a kinetics model of temper em-brittlement caused by long-term service for hot-wall hydrofining reactors was studied.The kinetics model was applied to phosphorus (P) segregation in 2.25Cr-1Mo steelused for a hot-wall hydrofining reactor, and the kinetics of grain boundary segrea-tion of impurity P in the steel exposed to the process environment of the hydrofiningreactor was calculated on the basis of the model. The Auger electron spectroscopytest was performed in order to determine the grain boundary concentration of P. Theexperimental result is agreement with the theoretical calculated data. The results showthat the kinetics equation is reasonable for predicting the levels of grain boundarysegregation of impurity P in 2.25Cr-1Mo steel used for hot-wall hydrofining reactors.

Characterization and Modelling of High Temperature Flow Behaviour of V Modified 2.25Cr-1Mo Heat Resistant Steel Plate

In order to study the high temperature flow behaviour of the V modified 2.25Cr-1Mo steel plate to guide the industrial rolling practice, the hot compression tests were carried out at the temperatures from 900 ℃ to 1150 ℃ and the strain rates from 0.01s^-1 to 1 s^-1 on Thermecmastor-Z equipment. Based on the experimental data of the hot compression tests, a kind of Arrhenius-type constitutive equation was developed.The equation can accurately show the relationship between the flow stress and the deformation temperature, the strain and the strain rate. The measured true stress-true strain curves exhibit two kinds of flow stress curves. Moreover, the forming mechanisms of these two types curves were explained by softening, wok hardening theory as well as metallographic and hardness experimental results. The accuracy of the developed Arrheniustype constitutive equation was identified by three kinds of statistic parameters and also by comparison of the measured and predicted data. The reasonable value of the three types of statistic parameters and the good agreement between the experimental and predicted data can confirm the validity of the developed Arrheniustype constitutive equation for V modified 2.25 Cr-1 Mo heat resistant steel plate.

Effect of Mg addition on temper embrittlement in 2.25Cr–1Mo steel doped with 0.056% P–Mg segregation behavior at grain boundary

To verify the microalloying function and segregation behavior of trace Mg at grain boundary in steel,the 2.25Cr–1Mo steel doped with 0.056%P containing different Mg contents was refined with a vacuum-induction furnace.The effects of trace Mg addition on the temper embrittlement susceptibility of 2.25Cr–1Mo steel were studied by step-cooling test and the segregation behavior of Mg at grain boundary was explored by Auger electron spectroscopy.It is shown that P-induced temper embrittlement susceptibility can be reduced after subjecting to step-cooling treatment with trace Mg addition,mainly benefited from the segregation of Mg at grain boundary.This segregation can decrease the segregation amounts of P and S,especially for P,and increase the grain boundary cohesion,reducing the adverse effect on temper embrittlement caused by P and S.

Precipitation kinetics of carbides during cyclical and isothermal aging of 2.25Cr–1Mo steel and its effect on mechanical properties

The carbide precipitation was analyzed during aging of 2.25Cr–1Mo steel at 550℃.The as-received steel was aged in two different manners:the first treatment was an isothermal aging at 550℃ for time up to 1000 h,and the second one was carried out by a cyclical aging,which consisted of aging at 550℃ for 1 h,water quenching at room temperature and then newly heating at 550℃.This procedure was repeated up to 300 times.The M_(23)C_(6) and M6C carbide precipitation took place intragranularly and intergranularly for both aging treatments.The carbide coarsening was detected to occur with the increasing aging time.Nevertheless,the growth kinetics of precipitation occurred more rapidly in the case of cyclical aging.The specimen hardness decreased with the aging time in both cases;however,it occurred in shorter aging time for the cyclical aging.Nanoindentation testing indicated the increase in ductility with the aging time,and the cyclically aged specimens showed larger ductility than the isothermally aged specimens.