In order to expand the application of steel 20 in precision device,fast multiple rotation rolling( FMRR) is applied to fabricate a nanostructured layer on the surface of steel 20. The FMRR samples are then Cr-Rare ear...In order to expand the application of steel 20 in precision device,fast multiple rotation rolling( FMRR) is applied to fabricate a nanostructured layer on the surface of steel 20. The FMRR samples are then Cr-Rare earth-boronized under low-temperature. The microstructure of the top surface layer is characterized by transmission electron microscopy( TEM). Microhardness of the top surface is measured by a Vickers microhardness tester. The boride layer is characterized by using scanning electron microscopy( SEM).Experimental results show that a nanostructured layer with their grain size range from 200 to 400 nm is obtained in the top surface layer. The microhardness of FMRR sample changes gradiently along the depth from about274 HV in the top surface layer to about 159 HV in the matrix,which is nearly 1.7 times harder than that of the original sample. The penetrating rate is enhanced significantly when the FMRR samples are Cr-Rare earthboronized at 600 ℃ for 6 h. Thickness of the boride layer increases to around 20 μm,which is nearly twice thicker than that of the original sample.展开更多
Many new types of rolling mills have been studied and developed corresponding to the needs of improvement in productivity and quality.This presentation reflects back at some of the innovative technologies,which were d...Many new types of rolling mills have been studied and developed corresponding to the needs of improvement in productivity and quality.This presentation reflects back at some of the innovative technologies,which were developed by Mitsubishi-Hitachi Metals Machinery,Inc.(hereinafter referred to as M-H),including the evolution of the pair cross mill,mill stabilizing device,on-line roll profiler,shape meter for hot-rolling,endless hot-rolling, recent application of UCM,and M-H split housing type 20-high mill.展开更多
文摘In order to expand the application of steel 20 in precision device,fast multiple rotation rolling( FMRR) is applied to fabricate a nanostructured layer on the surface of steel 20. The FMRR samples are then Cr-Rare earth-boronized under low-temperature. The microstructure of the top surface layer is characterized by transmission electron microscopy( TEM). Microhardness of the top surface is measured by a Vickers microhardness tester. The boride layer is characterized by using scanning electron microscopy( SEM).Experimental results show that a nanostructured layer with their grain size range from 200 to 400 nm is obtained in the top surface layer. The microhardness of FMRR sample changes gradiently along the depth from about274 HV in the top surface layer to about 159 HV in the matrix,which is nearly 1.7 times harder than that of the original sample. The penetrating rate is enhanced significantly when the FMRR samples are Cr-Rare earthboronized at 600 ℃ for 6 h. Thickness of the boride layer increases to around 20 μm,which is nearly twice thicker than that of the original sample.
文摘Many new types of rolling mills have been studied and developed corresponding to the needs of improvement in productivity and quality.This presentation reflects back at some of the innovative technologies,which were developed by Mitsubishi-Hitachi Metals Machinery,Inc.(hereinafter referred to as M-H),including the evolution of the pair cross mill,mill stabilizing device,on-line roll profiler,shape meter for hot-rolling,endless hot-rolling, recent application of UCM,and M-H split housing type 20-high mill.