2026 aluminum alloy was compressed in a temperature range of 300-450 ℃ and strain rate range of 0.01-10 s^-1. The correlation between compression conditions and microstructural evolution after solution and aging heat...2026 aluminum alloy was compressed in a temperature range of 300-450 ℃ and strain rate range of 0.01-10 s^-1. The correlation between compression conditions and microstructural evolution after solution and aging heat treatment was investigated. It is found that the recrystallization and precipitation behavior after heat treatment are associated with the temperature compensated strain rate Z value during hot deformation. Under low Z parameter condition, a small quantity of free recrystallized grains are formed, and the well formed subgrains with clean high-angle boundaries and coarse precipitates seem to be remained during heat treatment. Under high Z parameter condition, a large number of fine equiaxed recrystallized grains are produced, and a high dislocation density with poorly developed cellularity and considerable fine dynamic precipitates are replaced by the well formed subgrains and relatively coarse precipitates after heat treatment. The average recrystallized grain size after heat treatment decreases with increasing Z value and a quantitative relation between the average grain size and the Z value is obtained.展开更多
The microstructural evolution of 2026 aluminum alloy during homogenization treatment was investigated by optical microscopy(OM),scanning electron microscopy(SEM),energy dispersive X-ray spectrometry(EDS),differential ...The microstructural evolution of 2026 aluminum alloy during homogenization treatment was investigated by optical microscopy(OM),scanning electron microscopy(SEM),energy dispersive X-ray spectrometry(EDS),differential scanning calorimetry(DSC)and X-ray diffraction(XRD).The results show that severe dendritic segregation exists in the as-cast 2026 alloy and the main secondary phases at grain boundary are S(Al2CuMg)andθ(Al2Cu)phases.Elements Cu,Mg and Mn distribute unevenly from grain boundary to the inside of as-cast alloy.With the increase of homogenization temperature or the prolongation of holding time,the residual phases gradually dissolve into the matrixα(Al)and all the elements become more homogenized.According to the results of microstructural evolution,differential scanning calorimetry and X-ray diffraction,the optimum homogenization parameter is at 490°C for 24 h,which is consistent with the result of homogenization kinetic analysis.展开更多
基金Projects (2008CB617608, 2009CB623704) supported by the National Basic Research Program of China
文摘2026 aluminum alloy was compressed in a temperature range of 300-450 ℃ and strain rate range of 0.01-10 s^-1. The correlation between compression conditions and microstructural evolution after solution and aging heat treatment was investigated. It is found that the recrystallization and precipitation behavior after heat treatment are associated with the temperature compensated strain rate Z value during hot deformation. Under low Z parameter condition, a small quantity of free recrystallized grains are formed, and the well formed subgrains with clean high-angle boundaries and coarse precipitates seem to be remained during heat treatment. Under high Z parameter condition, a large number of fine equiaxed recrystallized grains are produced, and a high dislocation density with poorly developed cellularity and considerable fine dynamic precipitates are replaced by the well formed subgrains and relatively coarse precipitates after heat treatment. The average recrystallized grain size after heat treatment decreases with increasing Z value and a quantitative relation between the average grain size and the Z value is obtained.
基金Project(2016B090931001)supported by Science and Technology Research and Development Program of Guangdong Province,China
文摘The microstructural evolution of 2026 aluminum alloy during homogenization treatment was investigated by optical microscopy(OM),scanning electron microscopy(SEM),energy dispersive X-ray spectrometry(EDS),differential scanning calorimetry(DSC)and X-ray diffraction(XRD).The results show that severe dendritic segregation exists in the as-cast 2026 alloy and the main secondary phases at grain boundary are S(Al2CuMg)andθ(Al2Cu)phases.Elements Cu,Mg and Mn distribute unevenly from grain boundary to the inside of as-cast alloy.With the increase of homogenization temperature or the prolongation of holding time,the residual phases gradually dissolve into the matrixα(Al)and all the elements become more homogenized.According to the results of microstructural evolution,differential scanning calorimetry and X-ray diffraction,the optimum homogenization parameter is at 490°C for 24 h,which is consistent with the result of homogenization kinetic analysis.