Studies were made of the effect of tempering at temperatures from 25 to 750℃ for 0.5 to 100 h on changes of hardness,precipitated phase and its alloying element content as well as activation energy of tempering for q...Studies were made of the effect of tempering at temperatures from 25 to 750℃ for 0.5 to 100 h on changes of hardness,precipitated phase and its alloying element content as well as activation energy of tempering for quenched steel 20Cr11MoVNbNB.Tempering of the steel at temperatures below 400℃ may be controlled by the diffusion of C atoms in α-Fe,and above 400℃,by diffusion of Cr,also Mo or V,in α-Fe.展开更多
Study was made on the swerving of the curves of strength and hardness vs L-M parameter P=T(20+lgt)for steel 20Crl 1MoVNbNB aged at 550.600 and 650℃ for 0—5000 h,T being aging temperature in K and taging time in h.Th...Study was made on the swerving of the curves of strength and hardness vs L-M parameter P=T(20+lgt)for steel 20Crl 1MoVNbNB aged at 550.600 and 650℃ for 0—5000 h,T being aging temperature in K and taging time in h.The swerving seems to be due to:(1)the coarsening of the mean size of principal precipitate M_(23)C_6,(2)the precipitation of Laves phase MoFe_2;(3)the decrease of Mo content in matrix and(4)the recovery and recrystallization of the matrix phase.展开更多
文摘Studies were made of the effect of tempering at temperatures from 25 to 750℃ for 0.5 to 100 h on changes of hardness,precipitated phase and its alloying element content as well as activation energy of tempering for quenched steel 20Cr11MoVNbNB.Tempering of the steel at temperatures below 400℃ may be controlled by the diffusion of C atoms in α-Fe,and above 400℃,by diffusion of Cr,also Mo or V,in α-Fe.
文摘Study was made on the swerving of the curves of strength and hardness vs L-M parameter P=T(20+lgt)for steel 20Crl 1MoVNbNB aged at 550.600 and 650℃ for 0—5000 h,T being aging temperature in K and taging time in h.The swerving seems to be due to:(1)the coarsening of the mean size of principal precipitate M_(23)C_6,(2)the precipitation of Laves phase MoFe_2;(3)the decrease of Mo content in matrix and(4)the recovery and recrystallization of the matrix phase.