Ablation behaviour and mechanical performance of ZrB_(2)-ZrC-SiC modified carbon/carbon composites prepared by vacuum infiltration combined with reactive melt infiltration

The development of advanced aircraft relies on high performance thermal-structural materials,and carbon/carbon com-posites(C/C)composited with ultrahigh-temperature ceramics are ideal candidates.However,the traditional routes of compositing are either inefficient and expensive or lead to a non-uniform distribution of ceramics in the matrix.Compared with the traditional C/C-ZrC-SiC composites prepared by the reactive melt infiltration of ZrSi_(2),C/C-ZrB_(2)-ZrC-SiC composites prepared by the vacuum infiltration of ZrB_(2) combined with reactive melt infiltration have the higher content and more uniform distribution of the introduced ceramic phases.The mass and linear ablation rates of the C/C-ZrB_(2)-ZrC-SiC composites were respectively 68.9%and 29.7%lower than those of C/C-ZrC-SiC composites prepared by reactive melt infiltration.The ablation performance was improved because the volatilization of B_(2)O_(3),removes some of the heat,and the more uniformly distributed ZrO_(2),that helps produce a ZrO2-SiO2 continu-ous protective layer,hinders oxygen infiltration and decreases ablation.

Composite rock-breaking of high-pressure CO_(2)jet&polycrystallinediamond-compact(PDC)cutter using a coupled SPH/FEM model

CO_(2) drilling is a promising underbalance drilling technology with great advantages,such as lower cutting force,intense cooling and excellent lubrication.However,in the underbalance drilling,the mechanism of the coupling CO_(2) jet and polycrystalline-diamond-compact(PDC)cutter are still unclear.Whereby,we established a coupled smoothed particle hydrodynamics/finite element method(SPH/FEM)model to simulate the composite rock-breaking of high-pressure CO_(2) jet&PDC cutter.Combined with the experimental research results,the mechanism of composite rock-breaking is studied from the perspectives of rock stress field,cutting force and jet field.The results show that the composite rock-breaking can effectively relieve the influence of vibration and shock on PDC cutter.Meanwhile,the high-pressure CO_(2) jet has a positive effect on carrying rock debris,which can effectively reduce the temperature rising and the thermal wear of the PDC cutter.In addition,the effects of CO_(2) jet parameters on composite rock-breaking were studied,such as jet impact velocity,nozzle diameter,jet injection angle and impact distance.The studies show that when the impact velocity of the CO_(2) jet is greater than 250 m/s,the CO_(2) jet could quickly break the rock.It is found that the optimal range of nozzle diameter is 1.5–2.5 mm,the best injection angle of CO_(2) jet is 60,the optimal impact distance is 10 times the nozzle diameter.The above studies could provide theoretical supports and technical guidance for composite rock-breaking,which is useful for the CO_(2) underbalance drilling and drill bit design.

Anti-oxidation properties of ZrB_2 modified silicon-based multilayer coating for carbon/carbon composites at high temperatures

To improve the anti-oxidation ability of silicon-based coating for carbon/carbon （C/C） composites at high temperatures, a ZrB2 modified silicon-based multilayer oxidation protective coating was prepared by pack cementation. The phase composition, microstructure and oxidation resistance at 1773, 1873 and 1953 K in air were investigated. The prepared coating exhibits dense structure and good oxidation protective ability. Due to the formation of stable ZrSiO4-SiO2 compound, the coating can effectively protect C/C composites from oxidation at 1773 K for more than 550 h. The anti-oxidation performance decreases with the increase of oxidation temperature. The mass loss of coated sample is 2.44% after oxidation at 1953 K for 50 h, which is attributed to the decomposition of ZrSiO4 and the volatilization of SiO2 protection layer.

C/SiC/MoSi_2-SiC-Si multilayer coating for oxidation protection of carbon/carbon composites

C/SiC/MoSi2-SiC-Si oxidation protective multilayer coating for carbon/carbon （C/C） composites was prepared by pack cementation and slurry method. The microstructure, element distribution and phase composition of the as-received coating were analyzed by scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and X-ray diffraction （XRD）. The results show that the multilayer coating was composed of MoSi2, SiC and Si. It could effectively protect C/C composites against oxidation for 200 h with the mass loss of 3.25% at 1873 K in static air. The mass loss of the coated C/C composites results from the volatilization of SiO2 and the formation of cracks and bubble holes in the coating.

Oxidation behavior of C/C composites with SiC/ZrSiO_4-SiO_2 coating

A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.

TiB_(2)/B_(4)C复相陶瓷自蔓延热爆炸烧结与性能表征

为了探究高硬度复相陶瓷高效且低成本的制备方法,利用自蔓延高温合成结合爆炸烧结技术,开展制备二硼化钛/碳化硼(TiB_(2)/B_(4)C)复相陶瓷的研究,成功制备厚度约为1 cm、直径约为5 cm的TiB_(2)/B_(4)C复相陶瓷块体。烧结样品物相和微观结构分析表征结果表明:烧结样品中TiB_(2)相和B_(4)C相分布均匀,截面观察到致密的微米级颗粒。该方法制备的样品致密度和硬度较高,随冲击压力不同,致密度范围在90%~93%之间,相应平均维氏硬度为16.64~17.35 GPa;根据不同条件下回收样品的微结构、致密度等分析,冲击压力和起爆时刻生坯温度对TiB_(2)/B_(4)C复相陶瓷烧结质量有重要影响;冲击压力为40 GPa,生坯温度为1800 K时,烧结致密度为93%;为进一步提高烧结质量,应提高冲击压力或冲击波作用时间。研究表明自蔓延热爆炸烧结技术是一种高效且低成本的高硬度复相陶瓷的制备方法。

Nb_(2)O_(5)/Nb_(2)C催化剂的制备及其光催化NO转化的性能

采用焙烧法原位构建Nb_(2)O_(5)/Nb_(2)C异质样品,通过XRD、Raman、SEM、BET、UV-Vis DRS、MottSchottky及EIS等技术对样品的结构及性质进行分析,以NO为目标污染物评价其光催化活性。结果表明:Nb_(2)O_(5)/Nb_(2)C异质样品能够提供较多的反应活性位点、提高光的利用率及光生电子和空穴的分离效率,进而提高其光催化活性;在模拟太阳光照射下,其对NO的转化率达到了50.5%,分别为Nb_(2)O_(5)和Nb_(2)C样品的2.4倍和14.4倍,且在NO转化过程中,NO_(2)选择性转化率仅为0.75%。

一锅法制备MgO/蓝藻基碳介孔复合材料及CO_(2)吸附性能研究

采用一锅法,以KOH活化后的蓝藻粉为碳源,以六水硝酸镁为镁源,通过简单研磨固相反应,成功制备了MgO/C复合材料,并探究了镁源和碳源的投料比对介孔MgO/C复合材料结构的影响,同时采用X-射线衍射法、N_(2)等温吸脱附曲线法、扫描电镜法、红外光谱法、拉曼光谱法等现代技术对复合材料的组织结构进行表征。结果表明,MgO/C复合材料具有介孔结构,随着MgO负载量的增加,复合材料的比表面积和孔容下降;CO_(2)等温吸附性能研究表明,氧化镁与碳复合后对CO_(2)吸附能力有明显的改善,样品的孔结构对CO_(2)吸附能力有一定程度影响。

Preparation and properties of C/C-ZrB2-SiC composites by high-solid-loading slurry impregnation and polymer infiltration and pyrolysis（PIP）

Ultrahigh-temperature ceramics were added to C/C composites to meet their application requirement in a high-temperature oxidizing environment. C/C-ZrB2-SiC composites were fabricated by high-solid-loading slurry impregnation with polymer infiltration and pyrolysis. The dispersion and rheological behavior of ZrB2 slurry and the microstructural, mechanical, and ablation properties of the C/C-ZrB2-SiC composites were investigated. Results indicated that a well-dispersed and low-viscosity ZrB2 slurry was obtained using 0.40 wt.% polyethyleneimine as a dispersant at pH 5. Ceramics were uniformly distributed in the short-cut fiber layer and needle-punched area. The flexural strength of the C/C-ZrB2-SiC composites was 309.30 MPa. The composites exhibited satisfactory ablation resistance under the oxyacetylene flame of 2500℃, and the mass and linear ablation rates were 0.40 mg/s and 0.91 μm/s, respectively. A continuous and compact Zr O2 layer, which could effectively reduce the diffusion rate of oxygen and protect the composites from being ablated, was formed.

Non‑Magnetic Bimetallic MOF‑Derived Porous Carbon‑Wrapped TiO2/ ZrTiO4 Composites for Efficient Electromagnetic Wave Absorption

Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To break the mindset of magneticderivative design,and make up the shortage of monometallic non-magnetic derivatives,we first try non-magnetic bimetallic MOFs derivatives to achieve efficient EMW absorption.The porous carbon-wrapped TiO2/ZrTiO4 composites derived from PCN-415(TiZr-MOFs)are qualified with a minimum reflection loss of−67.8 dB(2.16 mm,13.0 GHz),and a maximum effective absorption bandwidth of 5.9 GHz(2.70 mm).Through in-depth discussions,the synergy of enhanced interfacial polarization and other attenuation mechanisms in the composites is revealed.Therefore,this work confirms the huge potentials of nonmagnetic bimetallic MOFs derivatives in EMW absorption applications.

Na2FePO4F/C composite synthesized via a simple solid state route for lithium-ion batteries

Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.

Electrochemical performance of LiFePO_4/(C+Fe_2P) composite cathode material synthesized by sol-gel method

A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical tests. The Fe2P content, morphology and electrochemical performance of LiFePOa/（C＋Fe2P） composite depend on the calcination temperature. The optimized LiFePO4/（C＋FeeP） composite is prepared at 650 ~C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2% （mass fraction）. The discharge capacity of the optimized LiFePO4/（C＋FeRP） at 0.1C is 156 and 161 mA.h/g at 25 and 55 ℃, respectively, and the corresponding capacity retentions are 96% after 30 cycles; while the capacity at 1C is 142 and 149 mA.h/g at 25 and 55 ℃, respectively, and the capacity still remains 135 and 142 mA-h/g after 30 cycles at 25 and 55℃, respectively.

Effect of baking processes on properties of TiB_2/C composite cathode material

Pitch and TiB2/C green composite cathode material were respectively analyzed with simultaneous DSC-TGA, and effects of three baking processes of TiB2/C composite cathode material, i.e. K25, K5 and M5, on properties of TiB2/C composite cathode material were investigated. The results show that thermogravimetrie behavior of pitch and TiB2/C green composite cathode is similar, and appears the largest mass loss rate in the temperature range from 200 to 600 ℃. The bulk density variation of sample K5 before and after baking is the largest （11.9%）, that of sample K25 is the second, and that of sample M5 is the smallest （6.7%）. The crushing strength of sample M5 is the biggest （51.2 MPa）, that of sample K2.5 is the next, and that of sample K5 is the smallest （32.8 MPa）. But, the orders of the electrical resistivity and electrolysis expansion of samples are just opposite with the order of crushing strength. The heating rate has a great impact on the microstructure of sample. The faster the heating rate is, the bigger the pore size and porosity of sample are. Compared with the heating rate between 200 and 600℃ of samples K25 and K5, that of sample M5 is slower and suitable for baking process of TiB2/C composite cathode material.

Model of critical strain for dynamic recrystallization in 10%TiC/Cu-Al_2O_3 composite

Using the Gleeble-1500 D simulator, the hot deformation behavior and dynamic recrystallization critical conditions of the 10%Ti C/Cu-Al2O3(volume fraction) composite were investigated by compression tests at the temperatures from 450 °C to 850 °C with the strain rates from 0.001 s-1 to 1 s-1. The results show that the softening mechanism of the dynamic recrystallization is a feature of high-temperature flow true stress-strain curves of the composite, and the peak stress increases with the decreasing deformation temperature or the increasing strain rate. The thermal deformation activation energy was calculated as 170.732 k J/mol and the constitutive equation was established. The inflection point in the lnθ-ε curve appears and the minimum value of-(lnθ)/ε-ε curve is presented when the critical state is attained for this composite. The critical strain increases with the increasing strain rate or the decreasing deformation temperature. There is linear relationship between critical strain and peak strain, i.e., εc=0.572εp. The predicting model of critical strain is described by the function of εc=1.062×10-2Z0.0826.

The influence of ablation products on the ablation resistance of C/C-SiC composites and the growth mechanism of SiO_2 nanowires

Ablation under oxyacetylene torch with heat flux of 4186.8（10%kW/m2 for 20 s was performed to evaluate the ablation resistance of C/C-SiC composites fabricated by chemical vapor infiltration（CVI） combined with liquid silicon infiltration（LSI） process.The results indicated that C/C-SiC composites present a better ablation resistance than C/C composites without doped SiC.The doped SiC and the ablation products SiO2 derived from it play key roles in ablation process.Bulk quantities of SiO2 nanowires with diameter of 80 nm-150 nm and length of tens microns were observed on the surface of specimens after ablation.The growth mechanism of the SiO_2 nanowires was interpreted with a developed vapor-liquid-solid（VLS） driven by the temperature gradient.

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF TiB_2-B_4C CERAMIC COMPOSITES

The microstructure and mechanical properties of TiB_2 /B_4C composites have been investi- gated.It was found that both the strength and hardness for TiB_2 greatly increase with the ad- dition of 20 to 30 wt-% B_4C,and the fracture toughness K_(IC) value remaines on the original high level.The flexure strength,Vicker's hardness and fracture toughness are 782 MPa,26.2 GPa and 7.2 MPam^(1/2),respectively,for the TiB_2-30 wt-% B_4C composite,compared to 450 MPa,21 GPa and 7.0 MPam^(1/2) for monolithic TiB_2.The toughening and strengthening mechanisms,have also been discussed.

Thermodynamic Analysis of Combusion Synthesis and Reaction Hot Pressing of Al_2O_3/B_4C Composite

The equilibrium phases and adiabatic temperature for combustion synthesis and reaction hot pressing of Al 2O 3/B 4C employing ① Al, B 2O 3 and C ② C, B, Al 2O 3 as starting reactants were analyzed by the CALPHAD technique. It is shown that the equilibrium phases at the adiabatic temperature in the combusion system (1) are not the intended composite Al 2O 3/B 4C but other phases. Good agreement with the experimental data was achieved for the calculated adiabatic temperature. The results were discussed with respect to the elimination of the by product in the combustion synthesis. It also revealed that the reactant mixture (2) is a weak exothermic or endothermic reaction system, which can be employed in the reaction hot pressing.

Microstructures and mechanical properties of MgAl_2O_4 particle-reinforced AC4C aluminum composites

MgAl2O4 particle-reinforced AC4C based alloy composites were fabricated by the stirring-casting method. The effects of the average sizes and the size distributions of MgAl2O4 particles on the dispersibility were investigated, and the microstructures, strength, and fatigue properties of MgAl2O4 particle-reinforced AC4C based alloy composites were evaluated. Tensile strength in the MgAl2O4 particle-reinforced AC4C based alloy composite was increased by using the classified particles. The fatigue limit at 107 cycles in the MgA1204 particle-reinforced AC4C-Cu composite increased by 27% compared to the unreinforced alloy at 250 ~C. Dislocations were observed in the matrix around the MgAl204 particle which resulted from the mismatch of thermal expansion coefficients between MgAl2O4 and Al, and resisted failure and caused fatigue cracks to propagate around the MgAl2O4 particles, resulting in extensive crack deflection and crack bowing which contributed to the improvement of fatigue strength.

Thermochemical Evaluation of Combustion Synthesis of Al_2O_3/B_4C Composite

The equilibrium phase and adiabatic temperature for combustion synthesis of Al_2O_3/B_4C employing Al, B_2O_3 and C as starting materials is analyzed by both conventional and CALPHAD method. The adiabatic temperature calculed by CALPHAD method is significantly lower than that obtained by conventional method. The CALPHAD calculation also reveals that the equilibrium phases presented at the adiabatic temperature are different to the desired composites. The adiabatic temperature in this system can be lowered by introducing Al_2O_3 as diluents. The maximum amount of Al_2O_3 that can be added to the system while maintain a self-sustaining combusion mode is 1.3 mol.

Wear resistance of surface metal matrix composite produced by gas tungsten arc melt injection of Cr3C2 -NiCr particles into low carbon steel

Cr3 C2-NiCr particles were injected into the melted surface of Q235 low carbon steel to make a surface metal matrix composite （MMC） layer by gas tungsten are melt injection （GTAMI） process. Hardness of the surface MMC layer was tested. Wear resistance of the surface MMC was investigated with a ball-on-disk dry sliding setup. Microstrnetures of the surface MMC layer and morphology of the worn surfaces were investigated with scanning electron microscopy （SEM）. The results showed that the hardness of the MMC was as high as 1 960. 7 HV. Wear loss of the upper part of the MMC layer is onlyO. 8% of that of the substrate under the dry sliding condition given. Wear loss of the bottom part is 2. 5 % of that of the substrate.