分别通过溶液聚合、乳液聚合和两步聚合法制备了3种水性羟基丙烯酸树脂(PAS、PAE、PAT),采用傅里叶变换红外光谱(FT-IR)、动态光散射(DLS)和示差扫描量热法(DSC)对所合成树脂进行了表征。在无催化剂存在的条件下,分别将3种水性树脂与异...分别通过溶液聚合、乳液聚合和两步聚合法制备了3种水性羟基丙烯酸树脂(PAS、PAE、PAT),采用傅里叶变换红外光谱(FT-IR)、动态光散射(DLS)和示差扫描量热法(DSC)对所合成树脂进行了表征。在无催化剂存在的条件下,分别将3种水性树脂与异氰酸酯固化剂Bayhydur XP 2655以及助剂混合得到双组分水性聚氨酯清漆,通过红外光谱对固化后清漆结构进行了表征,并对3种水性清漆的性能进行了研究。实验结果表明基于PAT的水性清漆综合性能较优。展开更多
Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling proces...Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling process on phase composition and morphology of the whiskers were investigated by TG-DSC（thermo gravimetric-differential scanning calorimeter）, XRD（X-ray diffraction）, and SEM（scanning electron microscope）. Pure K2Ti4O9 potassium titanate whiskers with large length-diameter ratio（r）（over 250） can be obtained at RT/K = 2.9 and TC = 950 ℃.展开更多
文摘分别通过溶液聚合、乳液聚合和两步聚合法制备了3种水性羟基丙烯酸树脂(PAS、PAE、PAT),采用傅里叶变换红外光谱(FT-IR)、动态光散射(DLS)和示差扫描量热法(DSC)对所合成树脂进行了表征。在无催化剂存在的条件下,分别将3种水性树脂与异氰酸酯固化剂Bayhydur XP 2655以及助剂混合得到双组分水性聚氨酯清漆,通过红外光谱对固化后清漆结构进行了表征,并对3种水性清漆的性能进行了研究。实验结果表明基于PAT的水性清漆综合性能较优。
基金Funded by the Natural Science Foundation Key Project of Hubei Province(No.2011CDA060)
文摘Pure K2Ti4O9 whiskers were prepared by KDC（Kneading-Drying-Calcination） method with TiO2 and K2CO3 as raw materials. The influences of TiO2/K2CO3 molar ratio（RT/K）, calcination temperature（TC） and cooling process on phase composition and morphology of the whiskers were investigated by TG-DSC（thermo gravimetric-differential scanning calorimeter）, XRD（X-ray diffraction）, and SEM（scanning electron microscope）. Pure K2Ti4O9 potassium titanate whiskers with large length-diameter ratio（r）（over 250） can be obtained at RT/K = 2.9 and TC = 950 ℃.