A new magnesium borate MgO·3B 2 O 3 ·3.5H 2 O has been synthesized by the method o f phase transformation of 2MgO·2B 2 O 3 ·MgCl 2 ·14H 2 O in boric acid solution and characte rized by XRD,FT-...A new magnesium borate MgO·3B 2 O 3 ·3.5H 2 O has been synthesized by the method o f phase transformation of 2MgO·2B 2 O 3 ·MgCl 2 ·14H 2 O in boric acid solution and characte rized by XRD,FT-IR and Raman spectra as well as by TG.The structural formula of this compound was Mg[B 6 O 9 (OH) 2 ]·2.5H 2 O.The main polyborate anions and their interaction in borate aqueous solution of preparation reactio n have been proposed according to the Raman spectrum of borate solution.The relation between the existing forms of polyborate anions and the crystalliz ing solid phase has been gained.展开更多
The adsorption and the growth of ZnO on α-Al2O3（0001） surface at various temperatures were theoretically calculated by using a plane wave pseudopotentials （USP） method based on density functional theory.The avera...The adsorption and the growth of ZnO on α-Al2O3（0001） surface at various temperatures were theoretically calculated by using a plane wave pseudopotentials （USP） method based on density functional theory.The average adsorption energy of ZnO at 400, 600 and 800 ℃ is 4.16±0.08, 4.25±0.11 and 4.05±0.23 eV respectively. Temperature has a remarkable effect on the structure of the surface and the interface of ZnO/α-Al2O3（0001）. It is found that the Zn-hexagonal symmetry deflexion does not appear during the adsorption growth of ZnO at 400 ℃, and that the ZnO[10^-10] is parallel with the [10^-10] of the α-Al2O3（0001）, which is favorable for forming ZnO film with the Zn-terminated surface. It is observed from simulation that there are two kinds of surface structures in the adsorption of ZnO at 600 ℃： one is the ZnO surface that has the Zn-terminated structure, and whose [10^-10] parallels the [10^-10] of the substrate surface, and the other is the ZnO[10^-10] //sapphire [11-20] with the O-terminated surface. The energy barrier of the phase transition between these two different surface structures is about 1.6 eV, and the latter is more stable. Therefore,the suitable temperature for the thin film growth of ZnO on sapphire is about 600 ℃, and it facilitates the formation of wurtzite structure containing Zn-O-Zn-O-Zn-O double-layers as a growth unit-cell. At 600 ℃, the average bond length of Zn-O is 0.190±0.01 nm, and the ELF value indicates that the bond of （substrate）-O-Zn-O has a distinct covalent character, whereas the （Zn）O-Al （substrate） shows a clear character of ionic bond. However, at a temperature of 800 ℃, the dissociation of Al and O atoms on the surface of the α-Al2O3（0001） leads to a disordered surface and interface structure. Thus, the Zn-hexagonal symmetry structure of the ZnO film is not observed under this condition.展开更多
A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, ...A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.展开更多
Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The ...Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The phase diagram of the system consisted of two invariant points E and F, five univariant curves, and four crystallization fields that belonged to K 2CO 3·3/2H 2O,Li 2 B 4O 7·3H 2O, K 2 B 4O 7 ·4H 2O and Li 2CO 3. The composition of the solution corresponding to E was w(CO 2- 3)=2.27 %, w(B 4O 2- 7) =6.05 %, w(K + ) =4.30%,w(Li + )=0.30 % and the equilibrium solids were Li 2 B 4O 7· 3H 2O+K 2 B 4O 7·4H 2O+Li 2CO 3;The composition of the solution for F was w(CO 2- 3) =22.45%,w(B 4O 2- 7)=1.88%,w(K + )=29.96%,w(Li + )=0.03% and the equilibrium solids were K 2CO 3·3/2H 2O+ K 2 B 4O 7·4H 2O+Li 2CO 3. K 2CO 3 possesses strong salting-out effect on K 2 B 4O 7,Li 2CO 3 and Li 2 B 4O 7.展开更多
Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure ...Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure was solved by direct method and refined by full-matrix least-square method. The crystal is monoclinic and belongs to space group Cc with a=2.645 3(5) nm, b= 1.670 4(3) nm, c=1\^821 6(4) nm, β=128.16(3) °, V=6.329(2) nm 3, Z=2 , D c=20.200 Mg/m 3, M r= 1 314.744, μ=10.274 mm -1, F(000) =38 226, GOF=0.99, R=0.094 1, ωR=0.257 3.展开更多
Eu(DBM) 3·H 2O nanocrystallites were obtained by the chemical precipitation method.By the elemental analyzer,infrared spectrum,TGA-DSC and TEM,that the construction of nanocrystallines,the thermal properties and ...Eu(DBM) 3·H 2O nanocrystallites were obtained by the chemical precipitation method.By the elemental analyzer,infrared spectrum,TGA-DSC and TEM,that the construction of nanocrystallines,the thermal properties and size were confirmed,in addition,fluorescence excitation and emission spectrum,ultraviolet absorption spectrums were investigation.Then the nanocrystallines were incorporated into the copolymer system of styrene and methyl acrylic acid,the fluorescence functional polymer nanometer material with high lanthanide content (50、wt%) were obtained.The experiment indicated that Eu(DBM) 3·H 2O nanocrystallines particle sizes were in 30～300、nm,it exhibited europium ion charlatanistic luminescence.The optical resins could provide a relatively stable environment for Eu(DBM) 3·H 2O nanocrystallines.展开更多
文摘A new magnesium borate MgO·3B 2 O 3 ·3.5H 2 O has been synthesized by the method o f phase transformation of 2MgO·2B 2 O 3 ·MgCl 2 ·14H 2 O in boric acid solution and characte rized by XRD,FT-IR and Raman spectra as well as by TG.The structural formula of this compound was Mg[B 6 O 9 (OH) 2 ]·2.5H 2 O.The main polyborate anions and their interaction in borate aqueous solution of preparation reactio n have been proposed according to the Raman spectrum of borate solution.The relation between the existing forms of polyborate anions and the crystalliz ing solid phase has been gained.
文摘The adsorption and the growth of ZnO on α-Al2O3（0001） surface at various temperatures were theoretically calculated by using a plane wave pseudopotentials （USP） method based on density functional theory.The average adsorption energy of ZnO at 400, 600 and 800 ℃ is 4.16±0.08, 4.25±0.11 and 4.05±0.23 eV respectively. Temperature has a remarkable effect on the structure of the surface and the interface of ZnO/α-Al2O3（0001）. It is found that the Zn-hexagonal symmetry deflexion does not appear during the adsorption growth of ZnO at 400 ℃, and that the ZnO[10^-10] is parallel with the [10^-10] of the α-Al2O3（0001）, which is favorable for forming ZnO film with the Zn-terminated surface. It is observed from simulation that there are two kinds of surface structures in the adsorption of ZnO at 600 ℃： one is the ZnO surface that has the Zn-terminated structure, and whose [10^-10] parallels the [10^-10] of the substrate surface, and the other is the ZnO[10^-10] //sapphire [11-20] with the O-terminated surface. The energy barrier of the phase transition between these two different surface structures is about 1.6 eV, and the latter is more stable. Therefore,the suitable temperature for the thin film growth of ZnO on sapphire is about 600 ℃, and it facilitates the formation of wurtzite structure containing Zn-O-Zn-O-Zn-O double-layers as a growth unit-cell. At 600 ℃, the average bond length of Zn-O is 0.190±0.01 nm, and the ELF value indicates that the bond of （substrate）-O-Zn-O has a distinct covalent character, whereas the （Zn）O-Al （substrate） shows a clear character of ionic bond. However, at a temperature of 800 ℃, the dissociation of Al and O atoms on the surface of the α-Al2O3（0001） leads to a disordered surface and interface structure. Thus, the Zn-hexagonal symmetry structure of the ZnO film is not observed under this condition.
文摘A new inorganic-organic hybrid framework microporous material Cd 3(BDC) 0.5(BTC) 2·(DMF)(H 2O)·3DMF·H 3O·H 2O, in which two kinds of carboxylate ligands coordinate with cadmium ions synchronously, was obtained under a mild synthesis condition. The titled compound is crystallized in a monoclinic system, space group P2(1)/c with a=1.584 7(7) nm, b=1.426 7(6) nm, c=1.936 3(6) nm, β=113.186(7)°, V=4.024 6(3) nm 3, Z=4, D X=1.947 mg/m 3, M r=1 179.92, μ=1.662 mm -1, F(000)=2 344, R=0.074 8, wR=0.215 1. Three cadmium centers link with each other through BDC or BTC ligand to form a 3-D open framework.
文摘Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The phase diagram of the system consisted of two invariant points E and F, five univariant curves, and four crystallization fields that belonged to K 2CO 3·3/2H 2O,Li 2 B 4O 7·3H 2O, K 2 B 4O 7 ·4H 2O and Li 2CO 3. The composition of the solution corresponding to E was w(CO 2- 3)=2.27 %, w(B 4O 2- 7) =6.05 %, w(K + ) =4.30%,w(Li + )=0.30 % and the equilibrium solids were Li 2 B 4O 7· 3H 2O+K 2 B 4O 7·4H 2O+Li 2CO 3;The composition of the solution for F was w(CO 2- 3) =22.45%,w(B 4O 2- 7)=1.88%,w(K + )=29.96%,w(Li + )=0.03% and the equilibrium solids were K 2CO 3·3/2H 2O+ K 2 B 4O 7·4H 2O+Li 2CO 3. K 2CO 3 possesses strong salting-out effect on K 2 B 4O 7,Li 2CO 3 and Li 2 B 4O 7.
文摘Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure was solved by direct method and refined by full-matrix least-square method. The crystal is monoclinic and belongs to space group Cc with a=2.645 3(5) nm, b= 1.670 4(3) nm, c=1\^821 6(4) nm, β=128.16(3) °, V=6.329(2) nm 3, Z=2 , D c=20.200 Mg/m 3, M r= 1 314.744, μ=10.274 mm -1, F(000) =38 226, GOF=0.99, R=0.094 1, ωR=0.257 3.
文摘Eu(DBM) 3·H 2O nanocrystallites were obtained by the chemical precipitation method.By the elemental analyzer,infrared spectrum,TGA-DSC and TEM,that the construction of nanocrystallines,the thermal properties and size were confirmed,in addition,fluorescence excitation and emission spectrum,ultraviolet absorption spectrums were investigation.Then the nanocrystallines were incorporated into the copolymer system of styrene and methyl acrylic acid,the fluorescence functional polymer nanometer material with high lanthanide content (50、wt%) were obtained.The experiment indicated that Eu(DBM) 3·H 2O nanocrystallines particle sizes were in 30～300、nm,it exhibited europium ion charlatanistic luminescence.The optical resins could provide a relatively stable environment for Eu(DBM) 3·H 2O nanocrystallines.