The electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment was investigated by potentiodynamic polarization technique, electrochemical impedance spectroscopy （EIS） an...The electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment was investigated by potentiodynamic polarization technique, electrochemical impedance spectroscopy （EIS） and scanning electron microscopy （SEM）. The results show that uniform corrosion occurs on 300M steel during the elec- trochemical measurements because no anodic passivation phenomenon is observed on polarization curves within the measurement range. The tests also show that 300M steel is highly susceptible to chloride containing solution, which is characterized by corrosion current density increasing with the addition of chlorides, and corrosion potential shifting towards positive direction and corrosion resistance decreasing, pos- itively suggesting that chloride ions speed up the corrosion rate of 300M steel. Mean- while corrosion products on the 300M steel surface formed during the salt spray test are too loose and porous to effectively slow down the corrosion rate. Additionally, a schematic structure of uniform corrosion mechanism can explain that 300M steel has better property of stress corrosion cracking （SCC） resistance than stainless steels.展开更多
The compressive deformation behaviors of 300M high strength steel were investigated over a wide range of temperatures （850- 1200 C） and strain rates （0. 001- 10 s^- 1 ） on a Gleeble-3800 thermo-mechanical simulato...The compressive deformation behaviors of 300M high strength steel were investigated over a wide range of temperatures （850- 1200 C） and strain rates （0. 001- 10 s^- 1 ） on a Gleeble-3800 thermo-mechanical simulator. The measured flow stress was modified by the corrections of the friction and the temperature compensations, which nicely reflect negative effects of the friction and temperature on the flow stress. The corrected stress-strain curves were the dynamic recrystallization type on the conditions of higher deformation temperature and lower strain rate. Flow stress increases with the increase of strain rate at the same deformation temperature and strain. By contrast, flow stress decreases with the increase of temperature at the same strain rate and strain. Dependence of the peak stress on temperature and strain rate for 300M steel is described by means of the conventional hyperbolic sine equation. By re gression analysis, the activation energy （Q） in the whole range of deformation temperature is determined to be 367. 562 kJ/mol. The effects of the temperature and the strain rate on mierostructural evolution are obvious. With the increase of the deformation temperature and the decrease of the strain rate, the original austenite grain sizes of 300M steel increase. At the same time, the corrected flow stress curves more accurately determine the evolution of the microstrueture.展开更多
Modified CCT diagram of carbide-flee bainite-martensite （CFB/M） ultra-high strength steel was established by applying controlled cooling of small samples. In addition, the influence of thermomechanical treatment tem...Modified CCT diagram of carbide-flee bainite-martensite （CFB/M） ultra-high strength steel was established by applying controlled cooling of small samples. In addition, the influence of thermomechanical treatment tem- perature on the structure and properties was discussed. The experimental results showed that when deformed at 860℃ and below, ferrite transformation occurred due to strain. With the decrease of ausforming temperature, the quantity of ferrite increased and strength and toughness were deteriorated. Therefore, certain information was provided for optimizing technical parameter of ausforming process., firstly, the thermomechanical treatment temperature should not be lower than 860 ℃ in order to avoid ferrite formation induced by deformation; secondly, rapid cooling rate is also significant after deformation in order to avoid ferrite precipitation during subsequent cooling stage.展开更多
300 M ultra-high strength steel has been widely used in critical structural components for aviation and aerospace vehicles,owing to its high strength,excellent transverse plasticity,fracture toughness and fatigue resi...300 M ultra-high strength steel has been widely used in critical structural components for aviation and aerospace vehicles,owing to its high strength,excellent transverse plasticity,fracture toughness and fatigue resistance.Herein,low and high power selective laser melting(SLM)of 300 M steel and their microstructural evolution and mechanical properties have been reported.The results show that the optimal energy density range with the highest relative density for SLMed 300 M steel is between 60 and160 J/mm^3.Furthermore,molten pools for deposition exhibit a conduction mode with semi-elliptical shape at a lower laser power of 300~600 W but a keyhole mode with"U"shape at a higher laser power of 800~1900 W.The heterogeneous microstructure of as-built samples is cha racterized by a skin-core structure which is that tempered troostite with the coarse non-equiaxed grains in the molten pool is wrapped by tempered sorbite with the fine equiaxed grains in the heat-affected zone.The skin-core structure of SLMed 300 M steel has the characteristics of hard inside and soft outside.The average microhardness of samples varies from 385 to 341 HV when laser power increases from 300 to 1900 W.Interestingly,ultimate tensile strength(1156-1193 MPa)and yield tensile strength(1085-1145 MPa)of dense samples fabricated at diffe rent laser powers vary marginally.But,the elongation(6.8-9.1%)of SLMed 300 M steel is greatly affected by the laser power.展开更多
基金supported by the Chinese National Science and Technology Infrastructure Platforms Construction Project (Grant No.2005DKA10400)Beijing Science and Technology Project (No.D09030303790901)
文摘The electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment was investigated by potentiodynamic polarization technique, electrochemical impedance spectroscopy （EIS） and scanning electron microscopy （SEM）. The results show that uniform corrosion occurs on 300M steel during the elec- trochemical measurements because no anodic passivation phenomenon is observed on polarization curves within the measurement range. The tests also show that 300M steel is highly susceptible to chloride containing solution, which is characterized by corrosion current density increasing with the addition of chlorides, and corrosion potential shifting towards positive direction and corrosion resistance decreasing, pos- itively suggesting that chloride ions speed up the corrosion rate of 300M steel. Mean- while corrosion products on the 300M steel surface formed during the salt spray test are too loose and porous to effectively slow down the corrosion rate. Additionally, a schematic structure of uniform corrosion mechanism can explain that 300M steel has better property of stress corrosion cracking （SCC） resistance than stainless steels.
基金Sponsored by Technology Major Projects of "High-end CNC Machine Tools and Basic Manufacturing Equipment"(2012ZX04010081)Natural Science Research Foundation Program for Distinguished Young Scholars in Higher EducationInstitutions of Hebei Province of China(Y2012034)
文摘The compressive deformation behaviors of 300M high strength steel were investigated over a wide range of temperatures （850- 1200 C） and strain rates （0. 001- 10 s^- 1 ） on a Gleeble-3800 thermo-mechanical simulator. The measured flow stress was modified by the corrections of the friction and the temperature compensations, which nicely reflect negative effects of the friction and temperature on the flow stress. The corrected stress-strain curves were the dynamic recrystallization type on the conditions of higher deformation temperature and lower strain rate. Flow stress increases with the increase of strain rate at the same deformation temperature and strain. By contrast, flow stress decreases with the increase of temperature at the same strain rate and strain. Dependence of the peak stress on temperature and strain rate for 300M steel is described by means of the conventional hyperbolic sine equation. By re gression analysis, the activation energy （Q） in the whole range of deformation temperature is determined to be 367. 562 kJ/mol. The effects of the temperature and the strain rate on mierostructural evolution are obvious. With the increase of the deformation temperature and the decrease of the strain rate, the original austenite grain sizes of 300M steel increase. At the same time, the corrected flow stress curves more accurately determine the evolution of the microstrueture.
基金Item Sponsored by National Key Fundamental Research and Development Programme of China(2004CB619105)
文摘Modified CCT diagram of carbide-flee bainite-martensite （CFB/M） ultra-high strength steel was established by applying controlled cooling of small samples. In addition, the influence of thermomechanical treatment tem- perature on the structure and properties was discussed. The experimental results showed that when deformed at 860℃ and below, ferrite transformation occurred due to strain. With the decrease of ausforming temperature, the quantity of ferrite increased and strength and toughness were deteriorated. Therefore, certain information was provided for optimizing technical parameter of ausforming process., firstly, the thermomechanical treatment temperature should not be lower than 860 ℃ in order to avoid ferrite formation induced by deformation; secondly, rapid cooling rate is also significant after deformation in order to avoid ferrite precipitation during subsequent cooling stage.
基金supported by the Pre-research Fund Project of Ministry of Equipment and Development of China though no.61409230301)the Fundamental Research Funds for the Central Universities through Program no.2019kfy XMPY005 and no.2019kfy XKJC042。
文摘300 M ultra-high strength steel has been widely used in critical structural components for aviation and aerospace vehicles,owing to its high strength,excellent transverse plasticity,fracture toughness and fatigue resistance.Herein,low and high power selective laser melting(SLM)of 300 M steel and their microstructural evolution and mechanical properties have been reported.The results show that the optimal energy density range with the highest relative density for SLMed 300 M steel is between 60 and160 J/mm^3.Furthermore,molten pools for deposition exhibit a conduction mode with semi-elliptical shape at a lower laser power of 300~600 W but a keyhole mode with"U"shape at a higher laser power of 800~1900 W.The heterogeneous microstructure of as-built samples is cha racterized by a skin-core structure which is that tempered troostite with the coarse non-equiaxed grains in the molten pool is wrapped by tempered sorbite with the fine equiaxed grains in the heat-affected zone.The skin-core structure of SLMed 300 M steel has the characteristics of hard inside and soft outside.The average microhardness of samples varies from 385 to 341 HV when laser power increases from 300 to 1900 W.Interestingly,ultimate tensile strength(1156-1193 MPa)and yield tensile strength(1085-1145 MPa)of dense samples fabricated at diffe rent laser powers vary marginally.But,the elongation(6.8-9.1%)of SLMed 300 M steel is greatly affected by the laser power.