研究T6处理、深冷处理和T6+深冷处理对ZCuAl 10 Fe 3Mn 2合金微观组织、力学性能以及在室温至450℃下的热疲劳行为。通过XRD,OM,SEM,EDS对合金组织和裂纹形貌进行观察分析。结果表明:T6+深冷复合处理工艺能够显著改善ZCuAl 10 Fe 3Mn 2...研究T6处理、深冷处理和T6+深冷处理对ZCuAl 10 Fe 3Mn 2合金微观组织、力学性能以及在室温至450℃下的热疲劳行为。通过XRD,OM,SEM,EDS对合金组织和裂纹形貌进行观察分析。结果表明:T6+深冷复合处理工艺能够显著改善ZCuAl 10 Fe 3Mn 2合金的力学性能和微观组织。与T6处理相比,其抗拉强度、硬度以及伸长率分别提高了7.28%,16.96%和23.53%;其α相进一步细化且分布更加均匀,位错密度增加,使得合金整体的组织均匀性、致密性更好。综合性能的提高也有效地提高了合金的热疲劳性能,其抗热应力和氧化腐蚀的能力增强。在相同冷热循环次数下,疲劳裂纹长度最短,裂纹生长速率最慢。展开更多
Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resista...Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.展开更多
文摘研究T6处理、深冷处理和T6+深冷处理对ZCuAl 10 Fe 3Mn 2合金微观组织、力学性能以及在室温至450℃下的热疲劳行为。通过XRD,OM,SEM,EDS对合金组织和裂纹形貌进行观察分析。结果表明:T6+深冷复合处理工艺能够显著改善ZCuAl 10 Fe 3Mn 2合金的力学性能和微观组织。与T6处理相比,其抗拉强度、硬度以及伸长率分别提高了7.28%,16.96%和23.53%;其α相进一步细化且分布更加均匀,位错密度增加,使得合金整体的组织均匀性、致密性更好。综合性能的提高也有效地提高了合金的热疲劳性能,其抗热应力和氧化腐蚀的能力增强。在相同冷热循环次数下,疲劳裂纹长度最短,裂纹生长速率最慢。
文摘Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.