A thin layer of TiO2 film was deposited on ITO surface via the liquid phase deposition （LPD） process. The photocurrent and electrochemical impedance spectroscopy （EIS） measurements indicated that the as-prepared L...A thin layer of TiO2 film was deposited on ITO surface via the liquid phase deposition （LPD） process. The photocurrent and electrochemical impedance spectroscopy （EIS） measurements indicated that the as-prepared LPD TiO2/ITO film had an excellent photoelectrochemical performance, which showed a sensitive and rapid response to the UV irradiation. The photogenerated electron-hole pairs could be effectively separated by applying an external bias to the TiO2 film electrode. The LPD TiO2/ITO film was employed to study the photoelectrocatalytic （PEC） degradation of 4-aminoantipyrine. Compared with other techniques, the PEC technique based on such a LPD film electrode had a synergetic effect for 4-aminoantipyrine degradation. When the applied bias potential was＋0.8 V and the supporting electrolyte concentration of Na2SO4 was 0.1 mol/L, the highest degradation efficiency within 120 min could reach 95%for 0.1 mmol/L 4-aminoantipyrine solution at pH 2.0.展开更多
A heterocyclic ligand synthesized by the coupling of diazotized 4-aminoantipyrine with acetylacetone reacted with lanthanide(Ⅲ) nitrate to form complexes of the type [Ln(HAAP)2(NOз)з] where, Ln=La(Ⅲ), Ce(Ⅲ), Pr(...A heterocyclic ligand synthesized by the coupling of diazotized 4-aminoantipyrine with acetylacetone reacted with lanthanide(Ⅲ) nitrate to form complexes of the type [Ln(HAAP)2(NOз)з] where, Ln=La(Ⅲ), Ce(Ⅲ), Pr(Ⅲ), Nd(Ⅲ), Sm(Ⅲ), or Gd(Ⅲ) and HAAP=3-{[2-(N-1-phenyl-2,3-dimethylpyrazol-3-in-5-on-4-yl)]hydrazone}pent-2,3,4-trione. The ligand and metal complexes were characterized on the basis of elemental analysis, molar conductance, magnetic susceptibility measurements, UV-Visible, infrared, far infrared and proton NMR spectral data. The spectral data revealed that the ligand existed in the hydrazo form and coordinated to the metal ion without deprotonation in a neutral tridentate manner, through carbonyl oxygen of pyrazolone ring, hydrazo nitrogen and carbonyl oxygen of the acetylace-tone moiety. The molar conductance values adequately supported their non-electrolytic nature. The ligand and the praseodymium(Ⅲ) complex were subjected to X-ray diffraction studies. Thermal decomposition behavior of the lanthanum(Ⅲ) complex was also examined.展开更多
The Schiff base pyridine-2-carboxaldehyde-4-aminoantipyrine （CI7H16N4O 1） and its perchlorate （C17H17N4O·ClO4 2） have been prepared and characterized by elemental analysis, IR spectra and single-crystal X-ray...The Schiff base pyridine-2-carboxaldehyde-4-aminoantipyrine （CI7H16N4O 1） and its perchlorate （C17H17N4O·ClO4 2） have been prepared and characterized by elemental analysis, IR spectra and single-crystal X-ray crystallography analysis. Both 1 and 2 crystallize in the monoclinic system, space group P21/c. For 1, a = 8.6820（12）, b = 24.934（3）, c = 7.0064（10） A,, β= 97.942（3）°, V = 1502.2（4） A^3, Z = 4, Dc = 1.293 g/cm^3, F（000） = 616,μ = 0.084 mm^-1, the final R = 0.0592 and wR = 0.1244. For 2, a = 5.9302（2）, b = 20.347（7）, c = 14.663（6） A, β= 90.200（9）°, V= 1769.201） A^3, Z = 4, Dc = 1.475 g/cm^3, F（000） = 816, μ = 0.254 mm^-1, the final R = 0.0533 and wR = 0.0819. As expected, both molecular structures of 1 and 2 adopt a trans configuration about the central C=N double bond. 2 is an ionic compound with the protonation at N（1） of pyridine-2-carboxaldehyde-4- aminoantipyrine.展开更多
Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_...Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_(4)/residual carbon from coal gasification fine slag(CFO/RC)composites were created using a novel hydrothermal method.Various mechanisms for microwave absorption,including conductive loss,natural resonance,interfacial dipole polarization,and magnetic flux loss,are involved in these composites.Consequently,compared with pure residual carbon materials,this composite offers superior capabilities in microwave absorption.At 7.76GHz,the CFO/RC-2 composite achieves an impressive minimum reflection loss(RL_(min))of-43.99 dB with a thickness of 2.44 mm.Moreover,CFO/RC-3 demonstrates an effective absorption bandwidth(EAB)of up to 4.16 GHz,accompanied by a thickness of 1.18mm.This study revealed the remarkable capability of the composite to diminish electromagnetic waves,providing a new generation method for microwave absorbing materials of superior quality.展开更多
The LiMnPO4/C composite material was synthesized via a sol-gel method based on the citric acid. The X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical performance tests were adopted to...The LiMnPO4/C composite material was synthesized via a sol-gel method based on the citric acid. The X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical performance tests were adopted to characterize the properties of LiMnPO4/C. The XRD studies show that the pure olivine phase LiMnPO4 can be obtained at a low temperature of 500 °C. The SEM analyses illustrate that the citric acid used as the chelating reagent and carbon source can restrain the particle size of LiMnPO4/C well. The LiMnPO4/C sample synthesized at 500 °C for 10 h performs the highest initial discharge capacity of 122.6 mA-h/g, retaining 112.4 mA-h/g over 30 cycles at 0.05C rate. The citric acid based sol-gel method is favor to obtain the high electrochemical performance of LiMnPO4/C.展开更多
Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization...Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization. The amount of carbon in the composite is less than 10% （mass fraction）, and the X-ray diffraction result confirms that the sample is of pure single phase indexed with the orthorhombic Pmn21 space group. The particle size of the Li2FeSiO4/C synthesized at 700 °C for 9 h is very fine and spherical-like with a size of 200 nm. The electrochemical performance of this material, including reversible capacity, cycle number, and charge-discharge characteristics, were tested. The cell of this sample can deliver a discharge capacity of 166 mA-h/g at C/20 rate in the first three cycles. After 30 cycles, the capacity decreases to 158 mA-h/g, and the capacity retention is up to 95%. The results show that this method can prepare nanosphere-like Li2FeSiO4/C composite with good electrochemical performance.展开更多
[Objective] This study aimed to establish a new method for determination of anemoside B4 content in pulsatilla water extract. [Method] Using acetonitrile-water （28：72） as the mobile phase, the high performance liqu...[Objective] This study aimed to establish a new method for determination of anemoside B4 content in pulsatilla water extract. [Method] Using acetonitrile-water （28：72） as the mobile phase, the high performance liquid chromatography, equipped with UV detector, was used to determine the anemoside B4 content in pulsatilla water extract. [Result] In the concentration range of 300-800 μg/ml, anemoside B4 content showed a good linear relationship with peak area. The average recovery of anemoside B4 was 98.12% （n=-6; RSD=-1.37%）. [Conclusion] The established method meets the requirements by methodology, and it can be used to determine the anemoside B4 content in pulsatilla water extract.展开更多
The preparation of Cu nanoparticles by the aqueous solution reduction method was investigated. The effects of different reaction parameters on the preparation of Cu nanoparticles were studied. The optimum conditions f...The preparation of Cu nanoparticles by the aqueous solution reduction method was investigated. The effects of different reaction parameters on the preparation of Cu nanoparticles were studied. The optimum conditions for preparing well-dispersed nanoparticles were found as follows: 0.4 mol/L NaBH4 was added into solution containing 0.2 mol/L Cu2+, 1.0% gelatin dispersant in mass fraction, and 1.2 mol/L NH3?H2O at pH 12 and 313 K. In addition, a series of experiments were performed to discover the reaction process. NH3?H2O was found to be able to modulate the reaction process. At pH=10, Cu2+ was transformed to Cu(NH3)42+ as precursor after the addition of NH3?H2O, and then Cu(NH3)42+ was reduced by NaBH4 solution. At pH=12, Cu2+ was transformed to Cu(OH)2 as precursor after the addition of NH3?H2O, and Cu(OH)2 was then reduced by NaBH4 solution.展开更多
To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vi...To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vis DRS techniques.The results showed that single or double doping did not change the crystalline structure and morphology,but the particle size decreased with Ni doping.The band gap energy absorption edge of Ni-B-BiVO4shifted to a longer wavelength compared with undoped,B or Ni single doped BiVO4.More V4+and surface hydroxyl oxygen were observed in BiVO4after Ni-B co-doping.When the optimal mass fraction of Ni is0.30%,the degradation rate of MO in50min is95%for0.3Ni-B-BiVO4sample which also can effectively degrade methyl blue(MB),acid orange(AOII)II and rhodamine B(RhB).The enhanced photocatalytic activity is attributed to the synergistic effects of B and Ni doping.展开更多
Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase ...Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B（RhB） solution and gaseous formaldehyde（FAD）. With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.展开更多
Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased w...Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.展开更多
基金Projects(12JJ3013,11JJ5010,10JJ5002)supported by the Natural Science Foundation of Hunan Province,ChinaProject(2013CL04)supported by the Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation,Changsha University of Science and Technology,ChinaProject(2011RS4069)supported by the Planned Science and Technology Program of Hunan Province,China
文摘A thin layer of TiO2 film was deposited on ITO surface via the liquid phase deposition （LPD） process. The photocurrent and electrochemical impedance spectroscopy （EIS） measurements indicated that the as-prepared LPD TiO2/ITO film had an excellent photoelectrochemical performance, which showed a sensitive and rapid response to the UV irradiation. The photogenerated electron-hole pairs could be effectively separated by applying an external bias to the TiO2 film electrode. The LPD TiO2/ITO film was employed to study the photoelectrocatalytic （PEC） degradation of 4-aminoantipyrine. Compared with other techniques, the PEC technique based on such a LPD film electrode had a synergetic effect for 4-aminoantipyrine degradation. When the applied bias potential was＋0.8 V and the supporting electrolyte concentration of Na2SO4 was 0.1 mol/L, the highest degradation efficiency within 120 min could reach 95%for 0.1 mmol/L 4-aminoantipyrine solution at pH 2.0.
文摘A heterocyclic ligand synthesized by the coupling of diazotized 4-aminoantipyrine with acetylacetone reacted with lanthanide(Ⅲ) nitrate to form complexes of the type [Ln(HAAP)2(NOз)з] where, Ln=La(Ⅲ), Ce(Ⅲ), Pr(Ⅲ), Nd(Ⅲ), Sm(Ⅲ), or Gd(Ⅲ) and HAAP=3-{[2-(N-1-phenyl-2,3-dimethylpyrazol-3-in-5-on-4-yl)]hydrazone}pent-2,3,4-trione. The ligand and metal complexes were characterized on the basis of elemental analysis, molar conductance, magnetic susceptibility measurements, UV-Visible, infrared, far infrared and proton NMR spectral data. The spectral data revealed that the ligand existed in the hydrazo form and coordinated to the metal ion without deprotonation in a neutral tridentate manner, through carbonyl oxygen of pyrazolone ring, hydrazo nitrogen and carbonyl oxygen of the acetylace-tone moiety. The molar conductance values adequately supported their non-electrolytic nature. The ligand and the praseodymium(Ⅲ) complex were subjected to X-ray diffraction studies. Thermal decomposition behavior of the lanthanum(Ⅲ) complex was also examined.
基金supported by the NSF of Guangxi Province (No. 0575046, 0575049)the Program for New Century Ten-Hundred-Thousand Excellent Talents of Guangxi (No. 2003223)+1 种基金the National Natural Science Foundation of China (No. 20361002, 30460153) as well as TRAPOYTNCET-04-0836 of Chinese Ministry of Education
文摘The Schiff base pyridine-2-carboxaldehyde-4-aminoantipyrine （CI7H16N4O 1） and its perchlorate （C17H17N4O·ClO4 2） have been prepared and characterized by elemental analysis, IR spectra and single-crystal X-ray crystallography analysis. Both 1 and 2 crystallize in the monoclinic system, space group P21/c. For 1, a = 8.6820（12）, b = 24.934（3）, c = 7.0064（10） A,, β= 97.942（3）°, V = 1502.2（4） A^3, Z = 4, Dc = 1.293 g/cm^3, F（000） = 616,μ = 0.084 mm^-1, the final R = 0.0592 and wR = 0.1244. For 2, a = 5.9302（2）, b = 20.347（7）, c = 14.663（6） A, β= 90.200（9）°, V= 1769.201） A^3, Z = 4, Dc = 1.475 g/cm^3, F（000） = 816, μ = 0.254 mm^-1, the final R = 0.0533 and wR = 0.0819. As expected, both molecular structures of 1 and 2 adopt a trans configuration about the central C=N double bond. 2 is an ionic compound with the protonation at N（1） of pyridine-2-carboxaldehyde-4- aminoantipyrine.
基金financially supported by the Key Project of Natural Science Research in Colleges and Universities of Anhui Province,China(No.2022AH050816)the Open Research Grant of Joint National-Local Engineering Research Centre for Safe and Precise Coal Mining(Nos.EC2023013 and EC2022018)+1 种基金the National Natural Science Foundation of China(No.52200139)the Introduction of Talent in Anhui University of Science and Technology,China(Nos.2021yjrc18 and 2023yjrc79)。
文摘Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_(4)/residual carbon from coal gasification fine slag(CFO/RC)composites were created using a novel hydrothermal method.Various mechanisms for microwave absorption,including conductive loss,natural resonance,interfacial dipole polarization,and magnetic flux loss,are involved in these composites.Consequently,compared with pure residual carbon materials,this composite offers superior capabilities in microwave absorption.At 7.76GHz,the CFO/RC-2 composite achieves an impressive minimum reflection loss(RL_(min))of-43.99 dB with a thickness of 2.44 mm.Moreover,CFO/RC-3 demonstrates an effective absorption bandwidth(EAB)of up to 4.16 GHz,accompanied by a thickness of 1.18mm.This study revealed the remarkable capability of the composite to diminish electromagnetic waves,providing a new generation method for microwave absorbing materials of superior quality.
基金Project (0991025) supported by Natural Science Foundation of Guangxi, ChinaProject (51164007) supported by the National Natural Science Foundation of ChinaProject (201101ZD008) supported by Educational Commission of Guangxi, China
文摘The LiMnPO4/C composite material was synthesized via a sol-gel method based on the citric acid. The X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical performance tests were adopted to characterize the properties of LiMnPO4/C. The XRD studies show that the pure olivine phase LiMnPO4 can be obtained at a low temperature of 500 °C. The SEM analyses illustrate that the citric acid used as the chelating reagent and carbon source can restrain the particle size of LiMnPO4/C well. The LiMnPO4/C sample synthesized at 500 °C for 10 h performs the highest initial discharge capacity of 122.6 mA-h/g, retaining 112.4 mA-h/g over 30 cycles at 0.05C rate. The citric acid based sol-gel method is favor to obtain the high electrochemical performance of LiMnPO4/C.
基金Project supported by Ministry of Education Key Laboratory of Synthetic and Natural Functional Molecular Chemistry, China Project (2010JK765) supported by the Education Department of Shaanxi Province, China
文摘Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization. The amount of carbon in the composite is less than 10% （mass fraction）, and the X-ray diffraction result confirms that the sample is of pure single phase indexed with the orthorhombic Pmn21 space group. The particle size of the Li2FeSiO4/C synthesized at 700 °C for 9 h is very fine and spherical-like with a size of 200 nm. The electrochemical performance of this material, including reversible capacity, cycle number, and charge-discharge characteristics, were tested. The cell of this sample can deliver a discharge capacity of 166 mA-h/g at C/20 rate in the first three cycles. After 30 cycles, the capacity decreases to 158 mA-h/g, and the capacity retention is up to 95%. The results show that this method can prepare nanosphere-like Li2FeSiO4/C composite with good electrochemical performance.
基金Supported by General Program of Beijing Municipal Education Commission(KM201410020007)~~
文摘[Objective] This study aimed to establish a new method for determination of anemoside B4 content in pulsatilla water extract. [Method] Using acetonitrile-water （28：72） as the mobile phase, the high performance liquid chromatography, equipped with UV detector, was used to determine the anemoside B4 content in pulsatilla water extract. [Result] In the concentration range of 300-800 μg/ml, anemoside B4 content showed a good linear relationship with peak area. The average recovery of anemoside B4 was 98.12% （n=-6; RSD=-1.37%）. [Conclusion] The established method meets the requirements by methodology, and it can be used to determine the anemoside B4 content in pulsatilla water extract.
文摘The preparation of Cu nanoparticles by the aqueous solution reduction method was investigated. The effects of different reaction parameters on the preparation of Cu nanoparticles were studied. The optimum conditions for preparing well-dispersed nanoparticles were found as follows: 0.4 mol/L NaBH4 was added into solution containing 0.2 mol/L Cu2+, 1.0% gelatin dispersant in mass fraction, and 1.2 mol/L NH3?H2O at pH 12 and 313 K. In addition, a series of experiments were performed to discover the reaction process. NH3?H2O was found to be able to modulate the reaction process. At pH=10, Cu2+ was transformed to Cu(NH3)42+ as precursor after the addition of NH3?H2O, and then Cu(NH3)42+ was reduced by NaBH4 solution. At pH=12, Cu2+ was transformed to Cu(OH)2 as precursor after the addition of NH3?H2O, and Cu(OH)2 was then reduced by NaBH4 solution.
基金Projects (21207093,51004072) supported by the National Natural Science Foundation of China for YouthProject (LJQ2014023) supported by the Liaoning Excellent Talents in University,China+1 种基金Project (L20150178) supported by the General Scientific Research Projects Foundation of Liaoning Educational Committee,ChinaProject (N140303002) supported by the Fundamental Research Funds for the Central Universities,China
文摘To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vis DRS techniques.The results showed that single or double doping did not change the crystalline structure and morphology,but the particle size decreased with Ni doping.The band gap energy absorption edge of Ni-B-BiVO4shifted to a longer wavelength compared with undoped,B or Ni single doped BiVO4.More V4+and surface hydroxyl oxygen were observed in BiVO4after Ni-B co-doping.When the optimal mass fraction of Ni is0.30%,the degradation rate of MO in50min is95%for0.3Ni-B-BiVO4sample which also can effectively degrade methyl blue(MB),acid orange(AOII)II and rhodamine B(RhB).The enhanced photocatalytic activity is attributed to the synergistic effects of B and Ni doping.
基金Supported by the National Natural Science Foundation of China(Nos.20433010and20571047)Specialized Research Fundfor the Doctoral Program of Higher Education(No.20060003082).
文摘Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B（RhB） solution and gaseous formaldehyde（FAD）. With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.
文摘Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.