The mechanical properties and phase morphologies of cis-1,4-butadiene rubber（BR） blended with polyethylene（PE） at different blend ratios were studied. The tensile test results show that the PE exhibits excellent r...The mechanical properties and phase morphologies of cis-1,4-butadiene rubber（BR） blended with polyethylene（PE） at different blend ratios were studied. The tensile test results show that the PE exhibits excellent reinforcing capabilities towards BR. Blending BR with PE results in a remarkable enhancement of tensile strength, modulus and the elongation at break simultaneously. An increment of tensile strength from 1.11 MPa to 16.26 MPa was achieved by incorporation of 40 wt% PE in the blends. The modulus and elongation at break of 40/60 PE/BR blends are also about 5 times higher than those of the pure BR treated under exactly the same conditions. The tear test indicates that the tear strength also increases with the increase of PE content. It reaches 58.38 MPa for the 40/60 PE/BR blend, which is approximately 10 times higher than that of the pure BR. Morphological study demonstrates that the PE forms elongated microdomains finely dispersed in the BR matrix when its content is over 30 wt%, which corresponds to the remarkably enhanced mechanical properties.According to the results, reinforcement mechanism of PE toward BR dependent on the microstructure has been discussed and two different mechanisms have been proposed.展开更多
Phase structure and crystallization behavior of polyethylene （PE） in its blends with cis-1,4-butadiene rubber （BR） at different blend ratios and sample preparation conditions were studied. The PE is finely dispers...Phase structure and crystallization behavior of polyethylene （PE） in its blends with cis-1,4-butadiene rubber （BR） at different blend ratios and sample preparation conditions were studied. The PE is finely dispersed in the BR matrix. For samples hot pressed at 145 ℃, circular PE microdomains with randomly oriented PE lamellar aggregates were produced. The domain size and number increase with increasing PE content. When the PE content is over 10 wt%, most of the PE domains impinged each other. The separated PE domains are connected by PE stripes with parallel arranged lamellar aggregates. For samples hot pressed at 140 ℃, elongated PE microdomains with oriented PE lamellar aggregates were obtained due to the shear flow. The crystallization of PE in the blends depends on the phase structure. Confined crystallization of PE occurs in small microdomains at relatively low temperature. With the increase of domain size, the crystallization ability of PE increases while the confined crystallization decreases.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51221002 and 21174014)
文摘The mechanical properties and phase morphologies of cis-1,4-butadiene rubber（BR） blended with polyethylene（PE） at different blend ratios were studied. The tensile test results show that the PE exhibits excellent reinforcing capabilities towards BR. Blending BR with PE results in a remarkable enhancement of tensile strength, modulus and the elongation at break simultaneously. An increment of tensile strength from 1.11 MPa to 16.26 MPa was achieved by incorporation of 40 wt% PE in the blends. The modulus and elongation at break of 40/60 PE/BR blends are also about 5 times higher than those of the pure BR treated under exactly the same conditions. The tear test indicates that the tear strength also increases with the increase of PE content. It reaches 58.38 MPa for the 40/60 PE/BR blend, which is approximately 10 times higher than that of the pure BR. Morphological study demonstrates that the PE forms elongated microdomains finely dispersed in the BR matrix when its content is over 30 wt%, which corresponds to the remarkably enhanced mechanical properties.According to the results, reinforcement mechanism of PE toward BR dependent on the microstructure has been discussed and two different mechanisms have been proposed.
基金financially supported by the National Natural Science Foundation of China(Nos.21274009 and 51221002)
文摘Phase structure and crystallization behavior of polyethylene （PE） in its blends with cis-1,4-butadiene rubber （BR） at different blend ratios and sample preparation conditions were studied. The PE is finely dispersed in the BR matrix. For samples hot pressed at 145 ℃, circular PE microdomains with randomly oriented PE lamellar aggregates were produced. The domain size and number increase with increasing PE content. When the PE content is over 10 wt%, most of the PE domains impinged each other. The separated PE domains are connected by PE stripes with parallel arranged lamellar aggregates. For samples hot pressed at 140 ℃, elongated PE microdomains with oriented PE lamellar aggregates were obtained due to the shear flow. The crystallization of PE in the blends depends on the phase structure. Confined crystallization of PE occurs in small microdomains at relatively low temperature. With the increase of domain size, the crystallization ability of PE increases while the confined crystallization decreases.